Predict the end product by drawing the cooling curve in TTT-diagram for - Alloy begins at 760 ˚C and Rapidly cool to 350 ˚C and hold for 104 seconds. TTT-diagram should be drawn considering the steel alloy.

Q: Metal A (Tm=860 oC) and metal B (Tm=620 oC) were fully dissolved in each other in the liquid state.…

A: Draw the phase diagram of the system.

Q: A 80%Ag-20%Cu alloy is slowly heated from room temperature (25°C). Determine (1) At what…

A:

Q: Figure Q4 (b) displays the time-temperature cooling paths for a 1080 steel on an isothermal…

A: In the given diagram, it can be seen that for paths (i) and (ii), the final position lies below the…

Q: Torricellian vaccum is

A: answer is 2nd option, Barometer.for solution refer below image.

Q: Show that for homogeneous nucleation during solid state transformation the critical radius r* is…

A: Nucleation is defined as the localised development of an unique thermodynamic phase in a gas,…

Q: Copper-rich copper-beryllium alloys are precipitation hardenable. After con the portion of the phase…

A: The phase diagram for compositions VS temperature is given as follows.

Q: For a Fe-2.5 %C alloy , what is the temperature at which the first liquid forms on heating and also…

A: Given: Fe-2.5 %C alloy

Q: A nitriding heat treatment of a BCC steel normally requires 2 h at 600 °C. What temperature would be…

A:

Q: Differentiate between equillibrium and non equillibrium cooling curve

A: The cooling curve is the graph showing phase change of material with respect to temperature of the…

Q: A steel is heated until 40% austenite, with a carbon content of 0.5%, forms. Estimate the…

A:

Q: 7. The following figure shows the continue cycling transformation diagram for a 0.35wt.%C…

A: Steel is an iron-carbon alloy with high carbon content. Steel grades within this range are known as…

Q: Assume you have 1kg of an alloy consisting of 85 wt% Sn and 15 wt% Pb at a temperature of 184 °C.…

A: Draw the above given phase diagram.

Q: A 1.05% C steel is slowly cooled from 900 °C to temperature just slightly above 723 °C. Calculate…

A: From the iron-carbide diagram understand that γ is used for austenite and Fe3C for cementite. Draw…

Q: Using the continuous-cooling transformation diagram for a eutectoid Fe-C alloy shown below, perform…

A: Given:

Q: Briefly describe how precipitation hardening happens in Al alloys (how the microstructure evolves as…

A: Hello. Since your question has multiple sub-parts, we will solve first three sub-parts for you. If…

Q: A molten Ag-Cu (20%) alloy is allowed to cool slowly from liquid phase till room temperature. Refer…

A:

Q: For alloy A-B of composition Co (C dot) is 33 at some temperature is found to consist of mass…

A:

Q: Q2/ * QI/For a 60 wt% Pb -30 wt% Sn alloy as shown in figure below, Determine: (a) The phase(s) is…

A:

Q: For the preceding problem, use the inverse lever rule to determine the proportions of liquid and…

A: Dear Students

Q: (b) The Low carbon steel (1% C) is required to be hardened by heat treatment. Related phase diagram…

A:

Q: Below is shown the isothermal transformation diagram for a 0.45 wt% C iron-carbon alloy. List the…

A: Alloy metals can exist in a variety of states. An alloy's phases are physically homogenous states.…

Q: For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of…

A: according to the figure (a) phase present liquid , α+βα phase , α+Lβ phase, β + L

Q: phase diagram (a) below, briefly des the mechanisms of precipitation hardening/strengthening o…

A: Precipitation hardening is a heat treatment procedure that may be used to strengthen aluminium…

Q: ) Is it advisable to have austenite in the HAZ (Heat Affected Zone)? Explain?

A: Explanation- Whenever a material (steels) welds with a specific welding process, there will heat…

Q: IDENTIFY THE PHASE OF THE FOLLOWING USING THE PHASE DIAGRAM. Write your solutions. 1. 66kPa and 15C…

A:

Q: C/ Bismuth (Bi) was melted at 2710C and tin (Sn) was melted at 2320C. Bismuth and ten are formed a…

A: The bismuth - tin phase diagram is given below -

Q: Predict the end product by drawing the cooling curve in TTT-diagram for - Alloy begins at 760 ˚C…

A:

Q: Steady flow of 10kg and temperature of 200°C. If the heat dissipation from the alloy is 715.5kJ.…

A:

Q: a) Explain the normalizing process in the heat treatment of metals. b) What are the final properties…

A:

Q: Quenching is a process used to preserve at room temperature a phase which exists in equilibrium at…

A: We are authorized to answer one question at a time since you have not mentioned which question you…

Q: RD Which line on the above phase diagram corresponds to the Solid-Liquid transition? Answer P.

A:

Q: Q4) Explain the alloy formation process and the different between Binary and Triple or (Ternary)…

A: Alloy : Definition of Alloy A alloy is mainly combination or mixture of metals or metal with another…

Q: For hypoeutoctoid plain carbon steel(select %C content yourself), determine the phasesthat are…

A: Steels with a carbon weight percentage of 0.8 are called eutectoids. Steels with a carbon weight…

Q: Suppose an alloy consists of a 75 wt% Sn-25 wt% Pb. i. List the phases present in the alloy at 185…

A:

Q: i) For a 68 wt% Zn-32 wt% Cu alloy, make schematic sketches of the microstructure that would be…

A: given Diagram consists of 4-temperature composition

Q: (b) Figure Q4 (b) displays the time-temperature cooling paths for a 1080 steel on an isothermal…

A: it can be seen that the final positions of paths (i) and (ii) are below the 220 oC temperature.

Q: A nitriding heat treatment of a BCC steel normally requires 2 h at 600 °C. What temperature would be…

A: Write the given values and constants for the given process:

Q: Using the TTT diagram, explain how you can get the following: (explain by mentioning detailed heat…

A:

Q: or for a sI forged om high-carbon steel AISI 1080 that has een quenched and tempered at 800 C.

A:

Q: Q5/ For a 75 wt% Pb -25 wt% Sn alloy as shown in figure below, Determine: 1.The phase(s) is (are)…

A: Note: Since you have posted a question with multiple sub-parts, we will solve the first three…

Q: A/ The lead and tin are partially dissolved in each other in solid state although they completely…

A: Given: The lead melting point, TPb = 329°C The tin melting point, TSn = 232°C The mass of α at…

Q: A/ The lead and tin are partially dissolved in each other in solid state although they completely…

A: The lead melting point, TPb = 329°C The tin melting point, TSn = 232°C The mass of α at eutectic…

Q: Draw a well labelled TTT-diagram of steel alloy mentioning the cooling curves for Annealing,…

A: TTT diagram stands for Time-Temperature-Transformation diagram. For eutectoid steel the diagram is…