Which material has the greatest UTS? Stress vs. Strain (Tensile)600500400Brass Trial 1-Brass Trial 2300Aluminum-Copper200Steel Trial 1Steel Trial 21000.050.10.150.20.250.30.350.4Tensile Strain (mm/mm)Tensile Stress (MPa)

The ultimate tensile stress is the maximum stress in the material corresponding to the strain.

Answered: Which material has the greatest UTS?

Engineering

Mechanical Engineering

Which material has the greatest UTS?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Name five elements that should generally be removed from steel to improve toughness.

A: In steel there are various types of the alloying element which can improve and reduce some specific…

Q: Define the term critical load?

A: Critical load – critical load on a column is the maximum value of load which can be carried out by…

Q: Define the term Surface Load?

A: Loads are the externally applied Forces, Couples on the member. The weight of the member is also a…

Q: An ASE automotive grade bolt with three slash marks on its head, indicates a hardness of what grade…

Q: If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of…

A: First go to Figure below and draw a horizontal line from 1.5 in. diamater and intersect it with…

Q: What happens if the principal stresses at a critical point in the material?

A: First, define the critical point. Critical points are those points in the given plane where the…

Q: What thickness limit classifies metal as being sheet?

Q: What is the discontinuity of loading?

A: The load along the length of the structure, say a beam if is consistent then we can say that the…

Q: How can the ductility of material be specified?

A: Ductility is the material’s property to undergo large plastic deformation (permanent type) after the…

Q: What is creep strength?

A: Creep is the phenomena of deformation of a body which is time-dependent. It occurs when a load is…

Q: What is the use of discontinuity functions?

A: Discontinuity function: On the basis of the continuity in an interval, the function is of two types…

Q: How does point defect affects the property of a material?

A: To find : How does point defect affects the property of a material

Q: What are free vibrations?

A: Vibration is a mechanical phenomenon whereby oscillations occur about an equilibrium point, that is…

Q: What is the Constant Load and Cross-Sectional Area?

A: Load: The load is a force that caused the stresses, deformation, and acceleration in the bodies.…

Q: What is the best way to test load/stress testing?

A: following is the answer to the above question-

Q: Q\ What is the best material that has a very good Young modulus and low density?

A: The process of designing any physical thing includes the choice of materials. The major objective…

Q: What is meant by the terms “Endurance Limit” and “Fatigue Limit”?

A: Endurance Limit” and “Fatigue Limit” are very important terms in the strength of a material. The…

Q: On what is the Design of a member for strength-based?

A: The strength-based design approach is a type of design where our main focus is on strength of…

Q: Which of the following material has minimum Indentation diameter? Select one: Mildsteel Aluminium…

A: Indentation dimeter is inversely proportional to the hardness of the material.

Q: Which of the four major material groups has the lowest thermal conductivity?

A: The four major material groups are :Metals, Non metallic organics, organics and polymers. Among…

Q: Name the 2 types of axial loading?

A: Two types of axial loading are tensile and compressive stress. Both kinds of stresses arise within…

Q: What happens If the material is subjected to triaxial stress?

A: Triaxial stresses are those in which three mutually perpendicular normal stresses acts as shown in…

Q: 5275 is a commonly used grade of steel For this grade, the ultimate tensile strength fy=? Select…

A: Answer For First:- According to standard for mild steel code S275 Composition: Carbon 0.25%…

Q: How is the Force Method of Analysis applied?

A: The force method of analysis is a method that is used to determine the unknown forces form the…

Q: What are the Discontinuity Functions?

A: In Mathematics and Engineering, discontinuity functions are all those functions which are not…

Q: What happens if the material is isotropic?

A: Materials have certain properties like homogeneity, showing isotropic behavior, etc. Isotropy is…

Q: 4) Which of the following is correct in case of Residual stresses? Increase fatigue strength Can…

A: Residual stress: These are the stress that remains in the object (specially in welded object) even…

Q: What is the equivalent stiffness?

Q: Define the term load-displacement relations?

A: Load displacement relations give the relationship between the displacement caused by any load on any…

Q: CCGC Helical Beam TEM00 Spiral Phase Plate A) TEM? B) a? C) r? D) d?

Q: What is the Endurance or Fatigue limit?

A: Given Endurance limit To find Definition

Q: . Compressive stress can be defined or described 2s an internal force in a material resisting a a…

A: Compressive stress can be described as an internal force in a material resisting a pushing load.…

Q: What is meant by the terms “Endurance Limit” and “Fatigue Limit”?

A: Endurance Limit: It is defined as the maximum value of completely reversed bending stress that a…

Q: Describe the method that may be used to displacement and slope at a point on the elastic curve?

Q: A cleaving failure results from which type of stress test? а.

A: A cantilever beam , is a beam having one free end and one fixed end. The most heavily loaded section…

Q: The unit of torsional rigidity and the flexural rigidity is the same. Select one: True Fals

A: Torsional rigidity: It is defined as the product of modulus of rigidity and polar moment of inertia.…

Q: Stress and strain: What are they and why are they used instead of load and deformation?

Q: Why are most of the loadings coplanar?

A: In the case of coplanar loadings system The net force of the system is zero and The net moment is…

Q: What 3 types of loading may lead to failure?

A: There are various ways by which a material may lead to failure. For instance, in case of mechanical…

Q: What are the compatibility requirements for the body?

A: Compatibility term is encountered in continuum mechanics where it generally stands for the study of…

Q: ) Which ferrous material is used for making brake shoe? How it is produced? State any two…

A: generally cast iron (CI) used in break shoes. From CI family Vermicular cast iron (VG Cast iron) is…

Q: What happens when the material is stressed beyond the yield point?

A: Any material is subjected to various processes and follows a stress-strain curve. In this curve,…

Q: why specific rigidity is needed?

A: Specific rigidity is defined by the ratio of young's modulas to the density. The more accurate term…

Q: What steps should be taken for the force method of analysis?

A: The force method of analysis is utilized to evaluate the forces generated by loads in indeterminate…

Q: ultimate strength in MPa

A: Maximum load ( from given table )Pmax = 47500N Diameter=12.8 mm radious - diameter/2 -12.8/2=…

Q: What is the neutral plane of a material that is being bent?

A: When the force applied on the beam perpendicular to the centroidal axis results bending in the beam.…

Q: 7. What is meant by eccentric loading and eccentricity?

A: What is meant by eccentric loading and eccentricity

Q: what is the equation and units for finding yield stress?

Q: What is a Brale penetrator and what hardness scale uses it?

A: The hardness of the material is defined as the properties of being material due to which it resists…

Q: What is the reason for using a minor load in the case of Rockwell hardness test method? ...

A: Reason for using minor load

Concept explainers

Joining Processes

It is the process of permanent or temporary joining of two metal pieces with the help of heat or pressure. Two metal parts are assembled by applying an energy source for the formation of a single unit. The obtained joined metals cannot be fragmented easily with the application of any force.

Question

100%

Which material has the greatest UTS?

Stress vs. Strain (Tensile)
600
500
400
Brass Trial 1
-Brass Trial 2
300
Aluminum
-Copper
200
Steel Trial 1
Steel Trial 2
100
0.05
0.1
0.15
0.2
0.25
0.3
0.35
0.4
Tensile Strain (mm/mm)
Tensile Stress (MPa)

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Draw the tensile curves of the following materials, taking into account the appropriate elongation at break, modulus of elasticity and tensile stress, on the side stress-strain graph. a)Low carbon steel (Ecelik=200Gpa),(Syield=300MPa),(Stensile=400MPa) b)High carbon steel (Esteel=200GPa),(Stensile=700MPa) c)Aluminum (Ealuminum=70GPa), (Syield=200MPa),(Stensile=300MPa) d)Cast iron (Ecast iron=120GPa),(Stensile=200MPa)
Please annotate the attached to highlight the different phases of the stress/strain graph for 0.15% carbon steel. From the attached graph, calculate the following: 1-modulus of elasticity 2-tensile strength 3-the ductility in % of elongation 4- yield strength at a strain offset of 0.002
explain stress strain diagram.
A material has the following properties, ultimate Sul = σul = 350mpa, the strain hardening exponent n=0.20. Determine the value for the strength coefficient K.
Figure 6.23 shows the tensile engineering stress– strain curve in the elastic region for a gray cast iron. Determine (a) the tangent modulus at 25 MPa (3625 psi) and (b) the secant modulus taken to 35 MPa (5000 psi).
Bronze alloy, the following true stresses produce the corresponding plastic true strains, before to necking: On the basis of this information, compute the true stress necessary to produce a true strain of 0.25 and then find the engineering stress and strain at this point. True stresses (MPa) True strain 354 0121 70 018
Draw a Stress/Strain graph of a mild tensile steel and identify the limit of proportionality and the yield point
Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?
Ductile - Stress and Strain Graph.
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.
hi im reviewing my class notes and im confused as to how it obtained the answer of 87.47 Mpa. P.S. this topic is stress transformation
The elastic constant related to direct stress is