(a)
The true strain for the 1112 steel specimen during necking.
The true strain for the annealed 1112 steel specimen during necking.
The elongation of the 1112 steel specimen during necking.
The elongation of the annealed 1112 steel specimen during necking.
(a)
Answer to Problem 2.96P
The true strain for the 1112 steel specimen during necking is
The true strain for the annealed 1112 steel specimen during necking is
The elongation of the 1112 steel specimen during necking is
The elongation of the annealed 1112 steel specimen during necking is
Explanation of Solution
Given:
The diameter of specimen is
The length of the specimen is
Formula used:
The expression for the true strain for 1112 steel specimen during necking is given as,
Here,
The expression for the true strain for 1112 annealed steel specimen during necking is given as,
Here,
The expression for the true strain for the 1112 steel specimen is given as,
Here,
The expression for the true strain for the 1112 annealed steel specimen is given as,
Here,
The expression for the elongation of the 1112 steel specimen at that instant is given as,
The expression for the elongation of the 1112 annealed steel specimen at that instant is given as,
Calculation:
The properties of 1112 steel specimen is given as,
The constant is
The exponent is
The properties of 1112 annealed steel specimen is given as,
The constant is
The exponent is
The true strain when necking occurs can be calculated as,
The true strain for 1112 annealed steel specimen during necking can be calculated as,
The length of the cold rolled 1112 steel after necking can be calculated as,
The elongation of the 1112 steel specimen at that instant can be calculated as,
The length of the 1112 annealed steel after necking can be calculated as,
The elongation of the 1112 annealed steel specimen at that instant can be calculated as,
Conclusion:
Therefore, the true strain for the 1112 steel specimen during necking is
Therefore, the true strain for the annealed 1112 steel specimen during necking is
Therefore, the elongation of the 1112 steel specimen during necking is
Therefore, the elongation of the annealed 1112 steel specimen during necking is
(b)
The ultimate strength for 1112 steel specimen.
The ultimate strength for 1112 annealed steel specimen.
(b)
Answer to Problem 2.96P
The ultimate strength for 1112 steel specimen is
The ultimate strength for 1112 annealed steel specimen is
Explanation of Solution
Formula used:
The expression for the ultimate strength for 1112 steel specimen is given as,
The expression for the ultimate tensile strength for 1112 steel specimen is given as,
The expression for the ultimate strength for 1112 annealed steel specimen is given as,
The expression for the ultimate tensile strength for 1112 annealed steel specimen is given as,
Calculation:
The ultimate strength for 1112 steel specimen can be calculated as,
The ultimate tensile strength for 1112 steel specimen can be calculated as,
The ultimate strength for 1112 annealed steel specimen can be calculated as,
The ultimate tensile strength for 1112 annealed steel specimen can be calculated as,
Conclusion:
Therefore, the ultimate strength for 1112 steel specimen is
Therefore, the ultimate strength for 1112 annealed steel specimen is
Want to see more full solutions like this?
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
- For some metal alloy, a true stress 345 MPa (50040 psi) produces a plastic true strain of 0.02. How much will a specimen of this material elongate when a true stress of 418 MPa (60630 psi) is applied if the original length is 500 mm (19.69in) ? Assume a value of 0.22 for the strain- hardening exponent, narrow_forwardA tensile specimen is elongated to twice its original length. Determine the engineering strain and true strain for this test? If the values are different explanations why they are different?arrow_forwardDuring stress-strain test, the unit deformation at a stress of 35 MPa was observed to be 167 x 10^-6 m/m and at a stress of 140 MPa it was 667 x 10^-6. If the proportional limit was 200 MPa, what is the modulus of Elasticity (GPa)? What is the strain corresponding to a stress of 80 MPa?arrow_forward
- A steel rod is subjected to a force of 5 kN. The initial length of the rod is 690 mm and after elongation its length is equal to 700 mm. Estimate engineering and true strain.arrow_forward1.From the tensile stress-strain behavior for the brass specimen shown in below, determine the following: (a) The modulus of elasticity, (b) The yield strength at a strain offset of 0.002, (c) The maximum load that can be sustained by a cylinderical specimen having an original diameter of 12.8 mm, (d) The change in length of a specimen originally 250 mm long that is subjected to a tensile stress of 345 MPa.arrow_forwardA cylindrical specimen of brass that has a diameter of 15 mm, a tensile modulus of 120 GPa, and a Poisson’s ratio of 0.30 is pulled in tension with force of 50,000 N. If the deformation is totally elastic, what is the approximate strain experienced by the specimen?arrow_forward
- A ductile specimen that has an initial length of 10 cm is tested under uniaxial loading. If the test is under tension and the nominal strain is 21.9%, please calculate the true strain in %.arrow_forwardA specimen of copper having a rectangular cross-section of 15.2 mm by 19.1 mm is pulled in tension with 44,500 N force, producing only elastic deformation. Calculate the resulting strain. Note that the modulus of elasticity of copper is 117 GPa.arrow_forwardHow can the principal normal strains and maximum in-plane shear strain be determined?arrow_forward
- Stress can be related to strain. Explain by using experimental methods?arrow_forwardDefine plane stress and plane strain, making clear which, if any, of the stresses are zero in each case.arrow_forwardWhat results do we get when shear stress is applied to homogeneous isotropic material?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY