A fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite

A fiber-reinforced polymer composite under isostrain condition consists of 35%fibers and 65% polymer by volume. The moduli of elasticity of the fibers and thepolymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of thefibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter12: Composite Materials

Section: Chapter Questions

Problem 12.5P

See similar textbooks

Similar questions

In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?
"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite" Repeat for 45% fibers by volume.
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 45% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
A fiber-reinforced polymer composite under isostress condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the composite
"A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the fibers and the polymer are 50 * 106 psi and 0.5 * 106 psi, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite t Repeat under isostress condition.
Calculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area ofm300 mm2, what is the load carried by each of the fiber and the matrix phases? What is the strain sustained by each of the fiber and the matrix phases?
Calculate the modulus of elasticity of fiberglass under isostrain condition if the fiberglass consists of 70% E-glass fibers and 30% epoxy by volume. Also, calculate the percentage of load carried by the glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70.5 and 6.9 GPa, respectively. If a longitudinal stress of 60 MPa is applied on the composite with a cross-sectional area of 300 mm2, what is the load carried by each of the fiber and the matrix phases?What is the strain sustained by each of the fiber and the matrix phases?
A fiberglass composite consists of epoxy matrix reinforced with randomly oriented and uniformly distributed E-glass fibers. The modulus of elasticity of the glass fibers and the epoxy are 70 GPa and 6 GPa, respectively. Calculate the modulus of elasticity of the fiberglass if the volume percentage of fibers is (a) 25%, (b) 50%, and (c) 75%. Plot a graph showing the relationship between the modulus of elasticity of the fiberglass and the percent of fibers. Comment on the effect of the percent of glass fibers on the modulus of elasticity of fiberglass
A fiberglass composite consists of epoxy matrix reinforced with randomly oriented and uniformly distributed E-glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 10 * 106 psi and 1 * 106 psi, respectively.Calculate the modulus of elasticity of the fiberglass if the volume percentage of fibers is (a) 30%, (b) 50%, and (c) 70%. Plot a graph showing the relationship between the modulus of elasticity of the fiberglass and the percent of fibers. Comment on the effect of the percent of glass fibers on the modulus of elasticity of fiberglass.
A fiberglass composite consists of epoxy matrix reinforced with randomly oriented and uniformly distributed E-glass fibers. The moduli of elasticity of the glass fibers and the epoxy are 70 and 6 GPa, respectively. Calculate the modulus of elasticity of the fiberglass if the volume percentage of fibers is (a) 25%, (b) 50%, and (c) 75%. Plot a graph showing the relationship between the modulus of elasticity of the fiberglass and the percent of fibers. Comment on the effect of the percent of glass fibers on the modulus of elasticity of fiberglass.