If the amount of the added carbon to pure iron is 2.2%C, its purity 78%, what is the expected composition of carbon steel, assuming the rate of conversion 0.9. *
Q: (a) Discuss the following iron based alloys with their applications in engineering: i. Low Carbon…
A: 1.Low Carbon steels Low carbon steels are principally composed of ferrite, a solid solution phase of…
Q: In white cast iron, the carbon is in combined form as .. O cementit O iron O silicon O cementite
A: White cast iron displays white fractured surfaces due to the presence of an iron carbide…
Q: In a tabular format, compare (a) Composition and heat treatment, (b) microstructure, for different…
A: Composition is the mixture of two ingredients or elements. For different cast irons mostly silicon…
Q: he figure shows two work pieces of steel of 0.3 %C nd 1.3 %C with different dimensions. compare…
A: For structure 1: The carbon percentage is 0.3% which means it will be more ductile and the structure…
Q: in a tabular format compare microstructure,for different cast irons and steel
A: Types Nature Form Comments Ferrite Soft and ductile In the form of flakes Cementite(Fe3C)…
Q: Determine the quenching and normalizing process temperatures of 2 different steels containing 0.6% C…
A: TO DETERMINE THE QUENCHING AND NORMALIZING PROCESS :- QUENCHING :- For hypo-eutectoid steel…
Q: Explain why a 92% copper – 8% nickel can or cannot be age hardened.
A: Age hardening: Age hardening is a heat treatment process that is used to increase the yield strength…
Q: heat -treatment: a-Draw on the same graph paper the (Hardness- Distance from quenched end) curve for…
A: Vicker's Hardness Test: The Vickers hardness test is a test performed to quantify the hardness of…
Q: Quenching is employed to harden metallic materials. Explain the process of transforming PLAIN CARBON…
A: i) Martensite transformation is a diffusionless process, the crystal structure of martensite is BCT.…
Q: 1) Give a brief explanation why the solubility of C is higher in y-iron than in alpha-iron
A: Gamma iron is a type of iron that has a Face-centered-cubic structure and is stable between the…
Q: -If the amont of the aded Carlbon is 2.2%s purity 78%) to 6000 kg iron . what is the e xepected…
A: Amount of the added carbon to pure iron = 2.2% Carbon Purity = 78% Mass of iron = 6000 kg rate of…
Q: b) When this furnace-cooled AISI 1040 steel reaches room temperature, identify 1) the phase(s)…
A: Solution: Given Data:
Q: 18. What is the range of carbon concentrations for steels? 4.3...6.67% 0.8...6.67% 0.8...2.14%…
A: For low carbon steel , 0.05 to 0.26% For medium carbon steel, 0.29 to 0.54% For High carbon steel,…
Q: Slowly cooled in furnace from 800 oC. 2- Cooled in air from 800 oC. 3-Quenched from 900 oC in water.
A: For solution refer below images.
Q: The hypoeutectoid steel contains less than 0.83%C and the hypereutectoid steel contains more than…
A: In iron carbon diagram, when the carbon percentage is less than 0.83 % then hypoeutectoid steel is…
Q: 11.14), specify the na- nure of the final microstructure (in terms of microconstituents present and…
A: given; from TTT diagram; (a) Cool rapidly to 700°C (1290°F), hold for 104 s, then quench to room…
Q: Draw Iron - Iron Carbide Phase diagram and show the following: 1- Temperature, phases and carbon…
A: As per the guideline only first 3 sub-parts should be answered.
Q: Name the microstructural products of a eutectoid iron-carbon alloy (0.76 wt% C ) that is first…
A: Material Science
Q: the transformation of a hypereutectoid plain-carbon
A: Required transformation of a hypereutectoid plain-carbon steel (0.4 percent C) with slow cooling.
Q: I. HSLA steels are developed to replace gray irons II. In normal atmospheres, HSLA steels are more…
A: HSLA :- High strength low alloy steels High strength low alloy steels are typ of steels which…
Q: What is the% C ratio of two different steels with 80% and equal austenite content at 724 C? please…
A: With the help of iron-carbon diagram,at 724oC & 80% austenite, carbon percentage will be: 0.9%…
Q: Q1a) A sample of an aluminum alloy has a tensile strength of 275 MPa, What will be the maximum…
A: Tensile strength, is the maximum load that a material can support without fracture when being…
Q: 1. What is Age Hardening and how does it differ from Quench Hardening?
A: Age Hardening
Q: Estimate the quench rate (in °C/s) needed to avoid pearlite formation in 1.13 wt % C steel. Note…
A: Question is based on material science and can be solved as
Q: Abul Khair (AKS) steel industry produced steel sample (austenite phase) which has 1.4% C for some…
A: As From the Iron -Carbon Diagram we had concluded that ***As per our company policy we are supposed…
Q: 1. Explain how Jominy test results can be used to validate a particular steel grade for a specific…
A: Jominy test is used to measure the hardenability of the steel.
Q: List two processes (annealing, quenching hot work, carburizing, ion exchange, cold rolling,…
A: Following are the processes - Precipitation heat treatment - This method helps to increase the…
Q: In a eutectoid steel the following microstructures are required for different application. Suggest…
A: Professor bain heated some steel samples having an eutectoid composition at a tenperature at which…
Q: 1)What is types of cast iron? Explain detail with; a)Elemental composition b)Production method…
A: 1 2
Q: Three separate heat treatments were applied to Ç1040 steel as quenching, quenching + tempering and…
A: Objective: The explanation of the modulus of elasticity, yield strength, toughness and resilience in…
Q: Plot the Iron-Iron Carbide phase diagram and answer the following: a) Show the heating ranges for…
A: Phase Diagram- It provides the information concerning the phase changes in many alloys system…
Q: Q3/ Compare Gray And Malleable Cast Irons Concerning (A) Composition, (B) Heat Treatment (C)…
A: Gray cast iron has a high dampening capacity and is corrosion resistant. However it is brittle,…
Q: In the plane carbon steel, microstructure consists of bright ferrite and dark cementite
A:
Q: For a 1095 steel alloy, what would the percent of each phase be at 730°C and 725°C?
A: Given alloy is steel 1095, for this steel percentage of the carbon present inside the steel is…
Q: 1) Give a brief explanation why the hardness of hardend steel will decrease with tempering
A: As per our guidelines we are suppose to answer only first question. 1. Tempering is done after…
Q: What is the reason for martensite hardness?
A:
Q: Using the Cu-Ag Phase diagram shown below, answer the following questions: Which of the following…
A: Given Cu-Ag phase diagram To find At 25% wt of silver(Ag)
Q: Individual study skills: Based on the micro structures, if parentage of carbon increased in plain…
A: Steels are the alloys with composition mainly carbon and iron and other constituents such as Ni, Cr,…
Q: By using the following figure, suppose aluminum alloy and carbon steel have the same tensile…
A: As, from the given graph it is clear that energy absorption for fcc material is very high.
Q: Write down the percentage of C and other alloying elements of the steel given the short designations…
A: 10CrMo910 C Si Mn P S Cr Mo N Cu 0.08 - 0.14 max 0.5 0.4 - 0.8 max 0.02 max 0.01 2 - 2.5 0.9 -…
Q: Make use of drawings of segments of the Fe-Cr phase diagram to illustrate the reason for the…
A:
Q: Increasing the degree of graphite nodularity produces an improvement in .cast iron elongation, due…
A:
Q: Compare the carbon content of steels and cast irons . Looking at an iron carbon phase diagram ,…
A: Solution:
Q: Explain and/or describe the following microstructures of iron/steel , how they affect the iron/steel…
A: Iron/steel alloys are very complicated microstructure as well as it influenced by composition,…
Q: Q1. Fill the blanks 1- The formation of metal alloys system consist of ,1..,2..,3...,4..,5...,6...…
A:
Step by step
Solved in 2 steps
- On the right side of the iron-carbon diagram, what kind of metal is found when the carbon content is over 2 percent?a 285kg alloy containing 70% lead is to be added with amounts of pure lead to make an alloy which is 90% lead. Determine the needed amount of pure lead to satisfy the requirementDuring Basic Oxygen Process to manufacture low carbon stainless steel, 600 kg of cast iron (6%of carbon) will be mixed with 300 kg of household scrap of steel (3% of carbon) and scrap from car contains 1% of carbon to generate 955 kg of steel with 0.1% of carbon. Calculate the total amount of car scrap and total carbon removed with the slag. Assume the other metals are innegligible quantity.
- 12-70 A steel is heated until 40% austenite, with a carbon content of 0.5%, forms. Estimate the temperature and the overall carbon content of the steel.1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementiteCalculate the critical radius of precipitates for which an Al--Mg alloycontaining 10% Mg will be strengthened by Orowan looping instead of particle shear. Use the following data:γAl2Mg = 1.4 J/m2,G Al = 26.1GPa,rAl = 0.143 nm.
- Explain briefly How rock (iron ore) converted to iron using the blast furnace.Copper-Nickel alloy is widely applied in industry. (a) List at least three applications where Cu-Ni alloy is used; (b) How many components and phases are shown in the below phase diagram? (c) For a mixture of 40 wt% Cu and 60 wt% Ni at 1320 oC, what phases are present? Identify theamount of these phases by applying “lever rule”.1)What is types of cast iron? Explain detail with;a)Elemental compositionb)Production methodc)Properties (Characteristic)d)Microstructers