Part BThe stress-strain diagram for a steel alloy having anoriginal diameter of 1.0 in. and a gage length of7 in. is shown in the figure below. (Eigure 1)Determine the load on the specimen that causes yielding.Express your answer to three significant figures and include appropriate units.HAPy- ValueUnitsSubmitRequest AnswerPart CFiguret oft>Determine the ultimate load the specimen will support.Express your answer to three significant figures and include appropriate units.NO706050P. -ValueUnits403020SubmitBequest Answer10(in/in)o G04 0m 12 016 020 024 02a aa omamsProvide Feedback

Answered: Image /qna-images/answer/ab30f6e7-c8f3-4ad5-9c3b-1c957fe92fe3.jpg

Part B The stress-strain dagram for a steel aloy having an original diameter of 1.0 in. and a gage length of 7 in. is shown in the figure below (Eigure 1) Determine the load on the specimen that causes yielding Express your answer to three significant figures and include appropriate units. Py Value Units Submit Request Answer Part C Figure Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. 70 P.- Value Units 30 20 Submit Bequest Answer o G04 0m 12 66 030 4 tin/in) Provide Feedback

Part B The stress-strain dagram for a steel aloy having an original diameter of 1.0 in. and a gage length of 7 in. is shown in the figure below (Eigure 1) Determine the load on the specimen that causes yielding Express your answer to three significant figures and include appropriate units. Py Value Units Submit Request Answer Part C Figure Determine the ultimate load the specimen will support. Express your answer to three significant figures and include appropriate units. 70 P.- Value Units 30 20 Submit Bequest Answer o G04 0m 12 66 030 4 tin/in) Provide Feedback

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter2: Axially Loaded Members

Section: Chapter Questions

Problem 2.5.1P: The rails of a railroad track are welded together at their ends (to form continuous rails and thus...

See similar textbooks

Similar questions

The rails of a railroad track are welded together at their ends (to form continuous rails and thus eliminate the clacking sound of the wheels) when the temperature is 60°F. What compressive stress ?? =6.5×10-6 /? is produced in the rails when they are heated by the sun to 120"F if the coefficient of thermal expansion a = the modulus of elasticity E = 30 × 106 psi?
Determine the strain energy per unit volume (units of psi) and the strain energy per unit weight (units of in ) that can be stored in each or the materials listed in the accompanying table, assuming that the material is stressed to the proportional limit. DATA FOR PROBLEM 2.7-5 Material Weight Density (lb/in3) Modulus of Elasticity (ksi) Proportional Limit (psi) Mild sleel 0.284 30,000 36,000 Tool steel 0.284 30,000 75,000 Aluminum 0.0984 10,500 60,000 Rubber (soft) 0.0405 0.300 300
A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?
A standard Vickers Hardness test was conducted on a metal specimen.Determine the Vicker’s hardness number and the tensile stress of thespecimen. The applied load was 10 kgf, and the standard indentor left anindentation with diagonal d = 0.217 mm. Assume that the metal is hard.
A bar made of carbon-steel of size 6mm x 14mm has a yield stress of 300 MPa and ultimate tensile strength of 500 MPa. Tha gauge length of the specimen tested under tension loading is150mm a. Determine its elongation when a tension load of 30 KN is applied. b. Determine the maximum load the bar can take before it fractures. Take Youngs Modulus of steel as 200,000 MPa.
A tensile specimen havign a diameter of 6 mm and a gauge length of 50 mm was tested to fracture and the stress-strain diagram is show. Poisson's ratio of material, v = 0.3 Determine the load P that the sample is subjected to when a stress of 300 MPa is applied. What is the instantaneous diameter of the sample given a longitudinal strain of 0.002?
A cylindrical specimen of a titanium alloy having original diameter of 2.96 mm experiences elasticdeformation when a tensile load of 2500 N is applied. Compute the maximum length of the specimenbefore deformation if the maximum allowable elongation is 0.43 mm. Note: Etitanium = 107 GPa.
For a number of points during a tension test on Man-Ten steel, engineering stress and strain data are given in Table. Also given are minimum diameters measured in the necked region in the latter portions of the test. The initial diameter was 6.32 mm. (a) Determine the Young’s modulus; (b) Determine the true stress and strain throughout; (c) Calculate the true plastic strain for the beyond yielding.
An engine parts is being tested with a load of 60000 lb. The allowable tensile stress is 10000 psi, modulus of elasticity of 40x106 psi. If the original length of specimen is 42 inches with elongation not exceeding 0.0015 in, what diameter of the specimen is rejected? a. 4.2 in b. 3.0 in c. 2.5 in d. 5.17 in
Given a example of copper specimen that has had a tensile test conducted on it. Diameter of 6.4mm Max force of 11112.5N Max extension of 7.79mm Calculate: 1) modulus of elasticity 2) tensile strength 3) the ductility, in percent elongation 4) yield strength at a strain of 0.002
1. A cylindrical steel specimen, with an initial diameter of 7mm, has elongated by 40% at the point when it starts to neck down. The load at the start of necking is 35 kN. What is the true stress at the ultimate tensile stress? The answer is 1273, but I'm not getting that. Please answer soon and neatly. Don't copy or I will dislike u many.
Sketch the typical engineering stress-strain diagram behaviour to fracture point, F and the tensile strength TS, together with the geometry of the deformed specimen at various point along the curve.