Which of the following describes galvanic corrosion? Select one: a. Two metals/alloys of different compositions are coupled while exposed to an electrolyte. b. Oxidation and reduction reactions occur randomly over the surface. c. Localized corrosion that may be initiated at a surface defect. d. Corrosion that results from a difference in concentration of ions or dissolved gases in the electrolyte. e. Corrosion that occurs preferentially along grain boundaries. f. Corrosion resulting from the combined action of chemical attack and mechanical abrasion or wear. g. One element is preferentially removed as a result of corrosion. h. Corrosion resulting from the combined action of an applied tensile stress and a corrosive environment.

Which of the following describes galvanic corrosion? Select one: a. Two metals/alloys of different compositions are coupled while exposed to an electrolyte. b. Oxidation and reduction reactions occur randomly over the surface. c. Localized corrosion that may be initiated at a surface defect. d. Corrosion that results from a difference in concentration of ions or dissolved gases in the electrolyte. e. Corrosion that occurs preferentially along grain boundaries. f. Corrosion resulting from the combined action of chemical attack and mechanical abrasion or wear. g. One element is preferentially removed as a result of corrosion. h. Corrosion resulting from the combined action of an applied tensile stress and a corrosive environment.

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter10: Oxidation, Degradation, Corrosion, Electroprocessing, Batteries, And Fuel Cells

Section: Chapter Questions

Problem 10.8P

See similar textbooks

Similar questions

The rate of corrosion in a galvanic cell can be reduced by: a. Increasing the temperature of the galvanic cell. b. Reducing the surface area of the anode in comparison to the cathode. c. Reducing the surface area of the cathode in comparison to anode. d. Increasing the ion concentration in the electrolyte.
This corrosion is due to the variation in difference in potential of the metals * O Uniform Galvanic Inter-granular O Stress
2. In a copper-nickel system as shown in figure, an alloy composition of 35 wt% Ni was cooled down from the temperature of 1300°C. Sketch the expected microstructures at the point a, b, c, d and e and briefly describe the development of these microstructures in the equilibrium cooling. L. L (35 Ni) 1300 L (32 Ni) a (46 Ni) a(43 Ni) L (24 Ni) d 1200 1100 20 30 40 50 Composition (wt% Ni) Temperature (°C))
A galvanized steel sheet has a zinc coating 20 um thick. The corrosion current density is found to be 4m A/cm2. What is the corresponding duration of rust resistance provided by this system?
Does the size of an ion affect the magnitude of the activity for varying ionic strengths? Does the activity coefficient depend on whether the ion is a cation or an anion?
8 Induction hardening and flame hardening are two heat treatment methods that can be used to increase wear resistance of a material's surface while keeping the inner core tough. Which of the following is true? (A) Induction hardening uses an electric current. (B) Flame hardening requires a longer quench time. (C) Induction hardening has a lower operating temperature. (D) Flame hardening results in smaller grains in its structure. jes (A) emsed anilisted (81) sig auc agniwash evilosque (0) grinore 2 (C)
Q.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature b) The austenite transformation temperature 10°C c) The eutectoid transformation temperature +10°C d) The eutectoid transformation temperature 10°C
At 170°C, what is the maximum solubility (a) of Pb in Sn and (b) of Sn in Pb? The lead-tin phase diagram is shown in the Animated Figure 9.8. (a) wt% Pb (b) i wt% Sn
Environmental temperature has different influences on metals conductivity. Which one of the following statements is the most accurate? a. Copper conductivity increases significantly with the increase in temperature b. Electrical resistance of zinc increases at lower temperatures c. Electrical resistance of Iron increases dramatically at higher temperatures d. Electrical conductivity of aluminium increases dramatically at higher temperatures
Which of the following is not a cause of energy loss in pipes? O Boundary friction O Changes in pipe diameter or geometry O The presence of control valves or fittings O Pipe temperature
For alloys of two hypothetical metals A and B, there exist an a, A-rich phase and a ß, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Fraction Fraction Alloy Composition a Phase B Phase 60 wt% A - 40 wt% B 0.59 0.41 30 wt% A - 70 wt% B 0.13 0.87 (a) a phase wt% A (b) B phase wt% A