1. A tensile test was conducted on a metal "505" specimen and the following stress-strain curveswere generated, both curves generated from the same set of data. Use the graphs to fill in themechanical properties of the material tested in the box below. Don't forget units!Stress vs StrainStress, psiStress, psi800007000060000500004000030000200001000000.0080000700006000050000400003000020000100000.0200.000 0.0020.040.0040.060.0060.080.10StrainStress vs Strain0.0080.12Elastic Modulus, E:0.2% Offset Yield Strength, oo:Tensile Strength, ou:Breaking Strength, of:% Elongation:0.140.010 0.012 0.014Strain0.160.180.016 0.0180.200.020

Elastic Modulus (Young's Modulus): The elastic modulus represents the stiffness of a material and is…

1. A tensile test was conducted on a metal "505" specimen and the following stress-strain curves were generated, both curves generated from the same set of data. Use the graphs to fill in the mechanical properties of the material tested in the box below. Don't forget units!

1. A tensile test was conducted on a metal "505" specimen and the following stress-strain curves were generated, both curves generated from the same set of data. Use the graphs to fill in the mechanical properties of the material tested in the box below. Don't forget units!

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 152 kN. - Length of the specimen is 20 mm. - The yield strength is 86 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 10 kN, iv) Young's Modulus if the elongation is 2.2 mm at 10 kN and (v) Final diameter if the percentage of reduction in area is 28 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. Find: 1)Stress at the elastic load (in N/mm2) 2)Young's Modulus of the Specimen (in N/mm2) 3)Final Area of the Specimen at Fracture (in mm) 4)Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. THE QUESTION IS : FIND THE Final Diameter of the Specimen after Fracture (in mm)????
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 159 kN. - Length of the specimen is 29 mm. - The yield strength is 82 kN/mm2. - The percentage of elongation is 47 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 19 kN, iv) Young's Modulus if the elongation is 2.8 mm at 19 kN and (v) Final diameter if the percentage of reduction in area is 21 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm) Initial Cross-sectional Area (in mm2)
Given the following stress-strain graph:a. is the modulus of elasticity of "A-514" greater, less or equal to the one of "A-572"?b. from the previous question, make an estimatio for both of them, check that the graphic comes in %c. If we were to test these materials in a universal tension equipment, which one would withstand more load?d. If we were to test these materials in a universal tension machine, which one would elongate the most before fracturing? would elongate the most before fracturing? e. Of the 6 materials shown, do any behave as brittle materials? f.
1. What are the elastic modulus (E) and the Poisson's ratio () used to indicate? 2. Illustrate the differences between actual stress and engineered stress with strain, and also describe their underlying physical concepts. 3. If the engineering strain is 2% for a specific state of uniaxial stress, what is the real strain? Please solve for all in full detail and step by step
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. Initial Cross-sectional Area 2.01 mm2. The Diameter of the Specimen 1.59 mm. Final Length of the Specimen 42.92 mm. Stress at the elastic load 8955.22 N/mm2. Find: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. FIND: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
In a forming process the diameter of the specimen is 1 cm and its length changes from 50 mm to 60 mm. Show the maximum force value on the graph of Force vs. True Strain plotted in Excel Program or any plotting program not by hand using the flow stress equation given below. σ= Kεn and σ=F/A Where the parameters are σ : True Stress in MPa K: Strength Coefficient, K=210 in MPa ε : True Strain, ε=ln (l/l0) n: Strain Hardening Exponent, n=0.27 F: Force in 10 A : Area in mm2 Take at least 3 digits after the decimal point. Specify the units. You can use Excel or any plotting program not by hand then paste your graph into the solution section.