26 - (CLO-1) A sand core used to form the internal surfaces of a brass casting experiences a buoyancy force of 21 kg. The volume of the mold cavity forming the outside surface of the casting = 6800 cm3. What is the weight of the final casting? Ignore considerations of shrinkage (Sand density = 1,6 g/cm3 and brass density=8,62 g/cm3). a) 28,71 b) 32,82 c) O 22,07 1811500 d) 16,35

26 - (CLO-1) A sand core used to form the internal surfaces of a brass casting experiences a buoyancy force of 21 kg. The volume of the mold cavity forming the outside surface of the casting = 6800 cm3. What is the weight of the final casting? Ignore considerations of shrinkage (Sand density = 1,6 g/cm3 and brass density=8,62 g/cm3). a) 28,71 b) 32,82 c) O 22,07 1811500 d) 16,35

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q1. A mold sprue is 20 cm long, and the cross-sectional area at its base is 2.5 cm2 .The sprue feeds a horizontal runner leading into a mold cavity whose volume is 1560 cm3. Determine:(A) velocity of the molten metal at the base of the sprue(B) volume rate of flow(C) time to fill the mold.
14 Which one of the following feature in sand casting process allows molten metal into cavity? a. Gates b. Vents c. Drag d. Runners )
In a room 12'-4" by 13'-9" with 8'-0" high ceilings, there is one door 3'x7' and two windows 4' square. Assume there is no waste in materials, and round off your answer to the next larget unit. A. How much wall surface in square feet is there to paint? B. What is the floor area? C. How many gallons of paint will be required to cover the walls with 2 coats of paint if each gallon covers 200 square feet of surface? D. How many lineal feet of cove base floor trim will be required?
Hello! Can you answer these two questions? Thanks. 1. I. In evaluating the moment of a planar lamina, a horizontal strip cannot be used as a representative area.II. The moment of any planar lamina is the product of the mass of the region and its centroid. a. Both statements are true b. Both statements are false c. Statement I is true, the latter being false d. Statement I is false, the latter being true 2. I. The reaction kinetics of order 0 cannot be evaluated using the concept of integration.II. If the order of reaction is 1 in PFR, given ?, and % conversion, the initial amount is not necessary to find ?. a. Both statements are true b. Both statements are false c. Statement I is true, the latter being false d. Statement I is false, the latter being true
Q2 /A/ In casting experiments performed using a certain alloy and type of sand mold, casting made of steel with shape as disk, with diameter =700mm and 30mm thickness , it took 20sec for a solidify Determine the value of the mold constant in Chvorinov's rule
11 Which one of the following feature in sand casting process allows molten metal into cavity? a. Gates b. Drag c. Vents d. Runners Clear my choice
In a process of metal casting, the final product’s volume is 1275 cm3. Casting waste, scrap allowance, and shrinkage allowance are 8%, 12%, and 3.5%, respectively. The metal supplier pays $0.5/kg, irrespective of the type of metal. Determine the material cost, if the following metals are used for casting:a. Aluminum (ρ = 2.7 g/cm3 ; cost = $1.85/kg)b. Grey Iron (ρ = 6.8 g/cm3; cost = $1.38/kg) Calculate the overall efficiency of the economic conversion of raw materials.
In a green sand moulding process, uniform ramming leads to (a) less chance of gas porosity (b) uniform flow of molten into the mould cavity C)greater dimensional stability of the casting (d) less sane expansion type of casting defect
Ram a farmer, managed to grow shaped-watermelons inside glass cases ofdifferent shapes. The shapes he used were: a perfect cube, hemi-spherical, cuboid,cylindrical along with the normal spherical shaped watermelons. Thickness of the skinwas same for all the shapes. Each of the glass cases was so designed that the totalvolume and the weight of the all the water-melons would be equal irrespective of theshape. A customer wants to buy water-melon for making juice, for which the skin of the water-melon has to be peeled off, and therefore is a waste. Which shape should the customer buy?
A aluminium alloy casting has a cylindrical geometry with 100mm in diameter and weighs 3200 gram. This casting takes 7.5 min to completely solidify. Another smaller and lighter cylindrical-shaped casting with the same diameterto-length ratio weighs 1800 gram. This casting is made of the same aluminium alloy and the same conditions of mold and pouring were used. Determinea) The mold constant in Chvorinov’s Rule,b) The dimensions of the lighter castingc) The total soldification time of the lighter casting. The density of aluminium alloy= 2.7 gram/cm3and n=2
5 The line separating the two parts of mold (cope and drag) is called___. a. Riser b. Parting line c. Gate d. Runners
A calcite sample that is 2" in diameter and 1 ft in length was dried completely. When It was submerged in water, it displaced 524 cm3 of water. What is the porosity of the sample?