4. The following data were obtained from a standard tensile stress test on a mild steel specimen. Graph the result and determine proportional limit stress and Young's Modulus. STRESS (Mpa) STRAIN (1 x 104) 69 3.6 138 6.8 207 10.2 276 13.0 345 18.4 414 27.2 462 41.8

4. The following data were obtained from a standard tensile stress test on a mild steel specimen. Graph the result and determine proportional limit stress and Young's Modulus. STRESS (Mpa) STRAIN (1 x 104) 69 3.6 138 6.8 207 10.2 276 13.0 345 18.4 414 27.2 462 41.8

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 142 kN. - Length of the specimen is 23 mm. - The yield strength is 82 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN, iv) Young's Modulus if the elongation is 1.6 mm at 15 kN and (v) Final diameter if the percentage of reduction in area is 20 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm)
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 146 kN. - Length of the specimen is 25 mm. - The yield strength is 83 kN/mm2. - The percentage of elongation is 40 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.1 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 18 kN, iv) Young's Modulus if the elongation is 1.3 mm at 18 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution: Initial Cross-sectional Area (in mm2) The Diameter of the Specimen (in mm) Final Length of the Specimen (in mm) Stress at the elastic load (in N/mm2) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. Find: 1)Stress at the elastic load (in N/mm2) 2)Young's Modulus of the Specimen (in N/mm2) 3)Final Area of the Specimen at Fracture (in mm) 4)Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. THE QUESTION IS : FIND THE Final Diameter of the Specimen after Fracture (in mm)????