5- For a Material A, the stress at which plastic deformation begins is 325 MPa, and the modulus of elasticity is 107 GPa. a) What is the maximum load that may be applied to a specimen with a cross-sectional area of 235 mm without plastic deformation? b) If the original specimen length is 210 mm, what is the maximum length to which it may be stretched without causing plastic deformation? c) Calculate the resilience value?

5- For a Material A, the stress at which plastic deformation begins is 325 MPa, and the modulus of elasticity is 107 GPa. a) What is the maximum load that may be applied to a specimen with a cross-sectional area of 235 mm without plastic deformation? b) If the original specimen length is 210 mm, what is the maximum length to which it may be stretched without causing plastic deformation? c) Calculate the resilience value?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

a)How new stronger materials are designed for specific applications. b) Given a stress‐strain diagram for material, how can one identify the elastic region, plastic region, fracture point, elasticity, and the yield strength? c)Given a stress‐strain diagram for a material, how can you determine if the material is ductile or brittle?
2) For a brass alloy, the stress at which plastic deformation begins is345 Mpa and the modulus of elasticity is 103GPa.a) What is the maximum load that can be applied to a specimen with area130mm² cross section without plastic deformation? b) If the original length of the specimen is 76 mm, what is themaximum length to which it can be stretched without causing deformationplastic?
what is elastic deformation of a material
Help me answer these following questions please, thanks! DEFINE STRESS, STRAIN AND ELASTIC MODULI. WHAT ARE THEIR RELATIONSHIPS? DIFFERENTIATE ELASTICITY FROM PLASTICITY
What is the linear variation in the shear strain?
What is the unit of strain?
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. Initial Cross-sectional Area 2.01 mm2. The Diameter of the Specimen 1.59 mm. Final Length of the Specimen 42.92 mm. Stress at the elastic load 8955.22 N/mm2. Find: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. FIND: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
b) Write the Advantages of Stress, Strain diagram in your own words
What is unit of shear strain?
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)
For a brass alloy, the stress at which plastic deformation begins is 345 MPa and the modulus of elasticity is 103 GPa.a. What is the maximum load that may be applied to a specimen with a cross-sectionalarea of 130 mm2 without plastic deformation?b. If the original specimen length is 76 mm, what is the maximum length to which it may be stretched without causing plastic deformation?