A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]

A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter12: Composite Materials

Section: Chapter Questions

Problem 6ETSQ

See similar textbooks

Similar questions

In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?
An epoxy is randomly reinforced with E-Glass fibers with 0.0012 in. diameter, 0.5 in. length, 0.5 * 106 psi ultimate tensile strength, and 7.2 ksi shear strength. Does this fiber length fully strengthen the composite? What is the minimum fiber length that would make the composite continuously reinforced?
Calculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers.The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively. Repeat for 35% carbon fibers by volume.
Calculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers. The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively.
A bar having the cross section shown has been formed by securely bonding brass andaluminum stock. Using the data given below, determine the largest permissible bendingmoment when the composite bar is bent about a horizontal axis.
Please explain about modulus of elasticity of the composite versus fiber volume fraction.
~Three decimal places. Find the Moment of inertia of the composite section about the x-axis if the x-axis were lowered one inch (1 inch) below the present location.
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65% polymer by volume. The moduli of elasticity of the filers and the polymer are 50 X 10 psi and 0.5 x 10® psi, respectively, and the Poison's ratios of the fibers and the polvmer are 0.25 and 0.41, respectively. Calculate the following: a. modulus of elasticitv of the composite. b. percentage of load carried by the fibers c. Poison's ratio of the composite
. Explain the importance of fiber orientation on the mechanical properties of fiberreinforced composites
State five different imperfections that may be found in lumber, and brieflydefine them.
Find examples of composite made by each casting methods.
Calculate the modulus of elasticity of carbon–epoxy composite under isostrain condition if the composite consists of 40% carbon fibers and 60% epoxy by volume. Also, calculate the percentage of load carried by the carbon fibers.The moduli of elasticity of the carbon fibers and the epoxy are 350 and 3.5 GPa, respectively. Repeat under isostress condition.