a) Give the order of pozzolanic activity (from the highest to the lowest) of the materials the properties of which are given below. b) Among the four materials given below, which one is expected to have the highest self-cementitious property? Why? Property Class F Clay Class C Silica fume fly ash fly ash siO,+Al,O,+Fe;03 Blaine fineness (m2/kg) 88 81 74 95 400 1000 300 10000

a) Give the order of pozzolanic activity (from the highest to the lowest) of the materials the properties of which are given below. b) Among the four materials given below, which one is expected to have the highest self-cementitious property? Why? Property Class F Clay Class C Silica fume fly ash fly ash siO,+Al,O,+Fe;03 Blaine fineness (m2/kg) 88 81 74 95 400 1000 300 10000

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 4ETSQ

See similar textbooks

Similar questions

Q.4. Give a reason for the following facts: 1- Ceramics fail after only about 0.1% strain under tensile test. 2- Porosity is an inherent defects in ceramics. 3- Ceramics carbides consider ideal choice for ceramic abrasives. 4- Orthoclase has the advantage over other types of feldspar.
Given your understanding of what initiates and controls failure in materials, which of the following will increase the failure strength or lifetime of a test piece or component and why? a. Decreasing the difference between the maximum and minimum stress values, as this effects the stress concentration factor b. Decreasing the temperature below the brittle-ductile transition temperature, to make it harder C. Polishing to reduce surface defects Od. Increasing its volume, to give a larger cross sectional area Oe. Increasing the grain size so there are less grain boundaries to initiate failure
strength of materials w/solution
A material has modus of rigidity 250 GN/m and bulk modulus of 450 GN/mm. What will be the value of poison's ratio.
Q7> Ductile-to-brittle transition temperature (DBTT) is a very important parameter in the design of metallic materials for engineering applications. It has been well known that most of BCC and HCP metals show the DBT phenomenon; however, there is no DBTT in FCC metals. (a) Explain the reason in terms of deformation and fracture. You must compare the BCC and FCC. (b) The ductile fracture surface consists of many dimples. Explain their formation mechanism from the concept of point defects. (c) There are two types in the brittle fracture. Explain and Compare them.
a) Which of the two materials has the greater hardness? b) Which of the two materials is more resilient? c) Indicate on the curves the yield strength and yield strength of each material.
Explain why the experimental strength of materials are lower than their theoretical strengths. BI4 Pagr
Two previously undeformed cylindrical specimens of an alloy are to be strain hardened by reducing their cross-sectional areas (while maintaining their circular cross sections). For one specimen, the initial and deformed radii are 15?? and 12??, respectively. The second specimen, with an initial radius of 11??, must have the same deformed hardness as the first specimen. Compute the second specimen’s radius after deformation.
(b) The difference between the theoretical and measured fracture strengths of brittle materials is explained by the presence of small flaws or cracks. In terms of these pre-existing flaws or cracks, briefly describe the occurring phenomena when a brittle material fractures in tension. (i) (ii) Explain why ductile materials do not fail in a brittle manner even though they have small flaws and crack present. If so, explain the process of ductile fracture of the materials.
A copper rod is deformed using a uniaxial tensile force of 16000 N. Deformation continues until sufficient strain hardening has occurred such that the applied force is too small to allow further deformation. After deformation, the rod has a diameter of 0.01 m and a length of 1.5 m. Assume that copper follows the strain hardening lawwith K of 310 MPa and n=0.54 Please calculate the true strain after the deformation ?
Example: the low cycle fatigue of a certain steel is given by life cycle equation-2: (of/E)=0.005 E=0.07 b= -0.08 c= -0.7 a. What is the value of the transition fatigue life, in this case 2 N/when Ɛɛ = Ep b. What is the total strain amplitude at the transition fatigue life?