A solid cylinder of diameter D and height equal to D, and a solid cube of side L are being sand cast by using the same material. Assuming there is no superheat in both the cases, the ratio of solidification times of the cylinder to the solidification time of the cube is

A solid cylinder of diameter D and height equal to D, and a solid cube of side L are being sand cast by using the same material. Assuming there is no superheat in both the cases, the ratio of solidification times of the cylinder to the solidification time of the cube is

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter26: Welding Metallurgy

Section: Chapter Questions

Problem 12R: What is a eutectic composition?

See similar textbooks

Related questions

Q: spherical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular…

Q: 2b) Figure 3 shows a cooling curve of Cadmium (Cd). Determine (i) the solidification temperature;…

A: As per company policy, we are restricted to solve only three sub-part of one question at a time.…

Q: A true centrifugal casting operation is to be performed in a horizontal configuration to make cast…

A: Given →L=105cm, d0=20cm out a diameter t=1.25cm, N=500 rev/ min

Q: Explain in detail different components of a gating system in sand mold casting

A: The main components of the gating system in sand mold casting are described below:(1) Pouring…

Q: Which one is better for the casting structure (a) and (b) in the following figures? Why?

A: 4) Concept: Option-B is better casting structure. Explanation: Option-B has 1.Symmetrical structure…

Q: #3:(b) Explain in detail different components of a gating system in sand mold casting.

Q: a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a…

A: Rectangle length = L = 200 mm Width = W = 100 mm Thickness = t = 18 mm Solidification time of…

Q: Given: Three metal pieces being cast have the same volume of but different shapes: One is a sphere,…

A: Given, n = 2

Q: A slab of size 300 x 300 x 50 mm is reguire to be cast from a molten steel using a top riser of 170…

A: The freezing ratio is calculated by dividing the total surface area of the casting by the total…

Q: A slab of size 300 x 300 x 50 mm is require to be cast from a molten steel using a top riser of 170…

Q: Two cubical castings of the same metal and sizes of 2 cm side and 4 cm side are moulded in green…

A: Given:Side of 1st square= 2 cmSide of 2nd square= 4 cmSolidification time, T1=2 mins

Q: A cylindrical riser with diameter-to-length ratio = 1.0 is to be designed for a sand casting mold.…

A: Givendl ratio of cylindrical riser=1.0mold constant,K=19.5 min/in2time taken by riser to freeze=time…

Q: A horizontal true centrifugal casting process is used to make brass bushings with the following…

Q: what are the stages of solidifaction in a casting process? when do those happen?what is under…

Q: 2. A disk-shaped part is to be cast out of aluminum. The diameter of the disk 500 mm and its…

Q: Explain in detail different components of a gating system in sand mold casting..

Q: Explain the gating system in casting with neat diagram . What are the elements of the gating…

A: Elements of the gating system -spruce -pouring cup -gates -runner -spruce well

Q: Volume of a cube of side L and volume of a sphere of radius r are equal Both the cube and the sphere…

A: Given:Surface area of sphere=4πr2Surface area of cube=6L2

Q: Imagine that you work in a foundry and are asked to calculate the solidification time of particular…

A: In the casting process, molten metal is poured into a mould and liquid metal fills up the cavities…

Q: 25. A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a…

Q: (b) In casting experiments performed using a certain alloy and type of sand mould, for which n can…

Q: 10. Volume of a cube of side / and volume of a sphere of radius rare equal Both the cube and the…

A: Given:Side of the cube= lradius of the sphere= r

Q: Design an efficient riser system for the casting shown in Figure 9-31. Be sure to include a sketch…

A: We have to write Design an efficient riser system for thecastin

Q: ). Sand casting is one of the basic process in metal casting. Illustrate a schematic diagram of a…

Q: In sand casting, the volumetric size of the pattern is (a) bigger than, (b) same size as, or (c)…

A: Basics of Casting are used.

Q: whether the riser can prevent macroporosity in the casting based on calculation applied to the riser…

A: here is module of riser is greater than module of casting it wil capable to prevent all…

Q: With a solidification factor of 0.97 × 10° s/m², the solidification time (in seconds) for a…

A: Given:Solidification factor, k=0.97×106 s/m2Diameter of sphere, D=200 mm or 0.2 mradius of sphere,…

Q: Which ingot has greater mechanical resistance? Why? Explain in detail what occurred during…

A: Given image : the image is showing two different ingot which shows the grain struture where one is…

Q: Problem 1 Suppose we want to cast a magnesium bar 20x20x45 mm³. We are to use a mid gating (exactly…

A: Given: The casting volume, V = 20x20x45 mm3 The diameter to height ratio of the riser, D/H = 1/1.2…

Q: A sphere with a diameter of 75 mm solidifies in three (3) minutes in a sand-casting operation. Using…

Q: Under uniform cooling, a spherical casting of 25 mm diameter undergoes volumetric solidification…

A: Given, Original diameter = d =25 mm Volumetric solidification shrinkage = Vs = 2.5 % = 0.025…

Q: The relation between dendrite arm spacing (X) and the solidification time (t) is given by X Al"

Q: Explain the function of a riser in sand mold casting process. Please sen me answer in detail in…

A: The riser is a part of the casting that is above the casting. Riser should be placed at appropriate…

Q: Compare the solidification times for each section of the part and the sprues presented. Determine…

Q: A vertical true centrifugal casting process is used to produce bushings that are 200 mm long and 200…

A: GIVEN DATA - L=200mm N=500rpm WE HAVE TO CALCULATE INSIDE DIAMETER AT TOP OF BUSHING

Q: Based on the data given in Question 7, what will be the total solidification time for a hemisphere…

A: Finding the value of 'n' and 'Cm'

Q: In casting experiments performed using a certain alloy and type of sand mold, casting made of steel…

A: Given data: The diameter of the disk is, d=700 mm. The thickness of the disk is, h=30 mm. The time…

Q: Copper alloy will cast by using mold have sphere shape attached with plate shape. The sphere shape…

A: Data given - D = 5 cm = 0.05 m Solidification time = roll number × 10-5 Plate dimension = 0.3 cm…

Q: A disk-shaped part is cast out of aluminium with a diameter of 630 mm and a thickness of 16 mm. If…

Q: (a) Which variables affect the total solidification time for casting process? Justify your answer…

A: For solution refer below images.

Q: What is sand casting? Explain the steps in sand casting process with neat diagram and indicate all…

A: Sand casting is the casting process in which sand is used as the molding material. In sand casting…

Q: With a solidification factor of 0.97 x 106 s/m², the solidification time (in seconds) for a…

A: Given:d=200 mm,r=100 mm or 0.1 m

Q: h, is placed on the top of the mold cavity of a closed type sand mould as shown in the figure. of…

Q: identify the part which is used to create a hollow shapes in sand casting. O a. Riser O b. Runner O…

Q: Copper alloy will cast by using mold have sphere shape attached with plate shape. The sphere shape…

Q: In sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is…

Q: A jeweler wishes to produce 24 gold rings in one investment-casting operation, as illustrated in…

Question

I need the answer as soon as possible

A solid cylinder of diameter D and height equal
to D, and a solid cube of side L are being sand
cast by using the same material. Assuming there
is no superheat in both the cases, the ratio of
solidification times of the cylinder to the
solidification time of the cube is

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

. A round casting is 0.2 m in diameter and 1 m in length. Another casting of the same metal iselliptical in cross section, with a major-to-minor axis ratio of 2, and has the same length andcross sectional area as the round casting. Both pieces are cast under the same conditions.What is the difference in the solidification times of the two castings?
With a solidification factor of 0.97 x 106 s/m², the solidification time (in seconds) for a spherical casting of 200 mm diameter is...
On the continuous growth, Calculate the interfacial undercooling if the melting temperature is 600 K and the latent heat of melting is given as 30 kJ/kg? (Assume the driving force for solidification as 45 kJ/kg?
For the solidification of nickel, calculate the critical radius r* and the activation energy ΔG* if nucleation is homogeneous. Values for the latent heat of fusion and surface free energy are -2.53×109 J/m3 and 0.255 J/m2, respectively. The supercooling value ΔT for the homogeneous nucleation of Ni is 319 oC. The melting point for Ni is 1455 oC.
(a) A spherical casting of diameter 10 cm has a cylindrical riser 5 cm in diameter and 10 cm high. Predict with suitable explanation whether the riser can prevent macroporosity in the casting based on calculation applied to the riser design.
A 5 cm cube solidifies in 4.6 min. Assume n=2. Calculate (a) the mold constant in Chvorinov’s rule and (b) the solidification time for a 1.25 cm X 12.5 cm X 15 cm bar cast under the same conditions
In sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
Explain the working of principles of the die casting process which is most preferred of the high production rate?
A cylinder with a diameter of 40 mm and height of 80 mm solidifies in 3 minutes in a sand casting operation. What is the solidification time if the cylinder height is doubled? What is the time if the diameter is doubled?
80 kg of aluminum is to be heated to a pouring temperature of 750°C. The unit melting and pouring energy of the metal = 1035 J/g. Thermal efficiency of the furnace = 65%. How much time is required to heat the metal from 25°C to the pouring temperature if the electric induction furnace generates 100 kW?
What is the critical value of G to avoid constitutional supercooling for the directional solidification of an Al-Cu alloy, containing 3 wt.% copper, at a rate of 0.05 mm/s? For these alloys, k = 0.14, m = -2.6oC/wt% and D = 3x10-5 cm 2 /s. Here G is the thermal gradient into the liquid phase, k is the partition coefficient of the alloy, and D is the diffusivity of solute in the liquid phase.