A horizontal true centrifugal casting process is used to make brass bushings with the following dimensions: length = 10 cm, outside diameter = 15 cm, and inside diameter = 12 cm. (a) Determine the required rotational speed in order to obtain a G-factor of 70. (b) When operating at this speed, what is the centrifugal force per square meter (Pa) imposed by the molten metal on the inside wall of the mold? %3D

A horizontal true centrifugal casting process is used to make brass bushings with the following dimensions: length = 10 cm, outside diameter = 15 cm, and inside diameter = 12 cm. (a) Determine the required rotational speed in order to obtain a G-factor of 70. (b) When operating at this speed, what is the centrifugal force per square meter (Pa) imposed by the molten metal on the inside wall of the mold? %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A true centrifugal casting operation is to be performed in a horizontal configuration by Durban Foundry to make cast iron pipe sections. The sections will have a length = 95 cm, outside diameter = 20 cm, and wall thickness = 1.00 cm. If the rotational speed of the pipe = 490 rev/min, Determine the G-factor, b) Is the operation likely to be successful?
True centrifugal casting is performed horizontally to make large diameter copper tube sections. The tubes have a length = 2.0 m, outside diameter = 0.4 m, and wall thickness = 30 mm. (a) If the rotational speed of the pipe = 600 rev/min, determine the G-factor on the molten metal. (b) Is the rotational speed sufficient to avoid "rain?" (c) What volume of molten metal must be poured into the mould to make the casting if solidification shrinkage and contraction after solidification are considered? Solidification shrinkage for copper = 3.5%, and solid thermal contraction = 6.5%.
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
Determine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.
q#8. Explain in detail different components of a gating system in sand mold casting..
A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min
a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
Why is the feeder used in the casting process? What is its significance and how should it be designed? In shapeinterpret by drawing.
Q#3:(b)Explain in detail different components of a gating system in sand mold casting.
where are the die cores placed in die casting?
A vertical centrifugal casting process is used to produce bushings that are 0.2 m outside diameter and 0.2 m in long. If the rotational speed during solidification is 500 rpm, determine the inside diameter at the bottom of the bushing if the diameter at the top is 0.084 m. * Add file
A aluminium alloy casting has a cylindrical geometry with 100mm in diameter and weighs 3200 gram. This casting takes 7.5 min to completely solidify. Another smaller and lighter cylindrical-shaped casting with the same diameterto-length ratio weighs 1800 gram. This casting is made of the same aluminium alloy and the same conditions of mold and pouring were used. Determinea) The mold constant in Chvorinov’s Rule,b) The dimensions of the lighter castingc) The total soldification time of the lighter casting. The density of aluminium alloy= 2.7 gram/cm3and n=2