A solid square rod is cantilevered at one end. The rod is 0.6 m long and supports a completely reversing transverse load at the other end of ±1.7 kN. The material is AISI 1080 hot-rolled steel. If the rod must support this load for 5 x 104 cycles with a design factor of 1.5, what dimension should the square cross section have? Neglect any stress concentrations at the support end.

A solid square rod is cantilevered at one end. The rod is 0.6 m long and supports a completely reversing transverse load at the other end of ±1.7 kN. The material is AISI 1080 hot-rolled steel. If the rod must support this load for 5 x 104 cycles with a design factor of 1.5, what dimension should the square cross section have? Neglect any stress concentrations at the support end.

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter8: Applications Of Plane Stress (pressure Vessels, Beams, And Combined Loadings)

Section: Chapter Questions

Problem 8.5.32P

See similar textbooks

Similar questions

A M20 × C4 bolt of mild steel is having yield stress of 320 MPa and factor of safety 3. The safe static tensile load in kN will be
A hollow, short compression member, of normalized cast steel (ASTM A27-58, 65 ksi), is to support a load of 1500 kips with a factor of safety of 8 based on the ultimate strength. Determine the outside and inside diameters if Do = 2Di
A rod is subjed by a compressive load of 60,000 lb with shock. It is made of AISI 3140 OQT 800°F. Determine the diameter of the solid rod in inches based on the ultimate strength.
Which of the following is the design stress for a piston rod where the axial load is completely reversed if the surface of the rod is ground and the surface finish factor is 0.9? Assume no stress concentration. Use a factor of safety of 2 and an endurance limit of 250 MPa. The load factor for completely reversed axial load is 0.85.
Determine the safe tensile load for fine series bolts of (a) M 24and (b) M 38. Assume that the bolts are not initially stressed and take the safe tensile stress as 450MPa.
10.20: Design a 3-m- long rod subjected to a tensile load of 67.5 kN. Using a factor of safety of 2.5 based on the yield stress, calculate the required rod diameter if it is to be made of (a) steel with a yield stress of 310 MPa. (b) aluminum alloy with a yield stress of 240 MPa.
A round steel rod made of structural steel, AISI C1118, As rolled is to be used as a column, centrally loaded with 15 kips; N= 2.75. Determine the diameter for (a) L= 20 in. (b) L= 5 in. (c) the same as (a) and (b) except that the material is AISI 9850, OQT 1100 F. Is there any advantage in using this material rather than structural steel?
(a) Explain FIVE (5) factors that may influence the optimum column design under an axial compressive load. (b) A 3.6 m long pin-ended column is formed from an A-36 steel circular hollow section with an outer diameter of 75 mm. Determine the minimum thickness, t (to the nearest integer in mm) of the circular hollow section so that the column can safely support the load of 200 kN without buckling. If the outer diameter of the steel circular hollow section is reduced to 62 mm and the ends are pinned-fixed supported, analyse whether the column with the same applied load and the sectional thickness computed above will cause a buckling failure.
An ASTM cast iron, grade 30, has ultimate strength at tension Sut = 350 MPa, and at compression Suc = 1150 MPa. it carries static loading resulting in the stress state listed below at the critical locations. Using the static failure analysis estimate the factor of safety. σA = 127 MPa, σB = -264 MPa.
The figure gives the cross-section of a grade 25 cast-iron pressure vessel. A total of N bolts are to be used to resist a separating force of 150 kN. (a) Determine kb, km, and C. (b) Find the number of bolts required for a load factor of 2 where the bolts may be reused when the joint is taken apart. (c) With the number of bolts obtained in part (b), determine the realized load factor for overload, the yielding factor of safety, and the load factor for joint separation. Use (SI) units as it applies
A shortcompression memberwith Do= 2.5Di is to support a dead load of 25 tons. The material is to be 4130 steel, WQT 1100 °F. Calculate the outside and insidediameters on the basis of a yield strength of 114 ksi and a factor of safety of 3.
A round cross-sectional bar d= 39 mm is cut from steel of Sut = 715 MPa. The bar is loaded with a completely reversed stresses. What is the strength of failure (in MPa) If only 10 4 cycles are needed? (Take fully corrected Se = 358 MPa, no need to use modification fcactors) (accepted answer range +/- 5 MPa)