An airplane part is to be designed from view point of Fracture Toughness for which two materials are available. Consider Y=1.2 and ow =400 MPa, calculate (a) maximum internal crack length under the given condition for each material type. (b) How much stress on Aluminum part can be increased/decreased to comply with the critical crack length of 3 mm. 1/2 Кiс, МPа m Aluminum (7075-T3) 30 Titanium Ti-6Al-4Va 55

An airplane part is to be designed from view point of Fracture Toughness for which two materials are available. Consider Y=1.2 and ow =400 MPa, calculate (a) maximum internal crack length under the given condition for each material type. (b) How much stress on Aluminum part can be increased/decreased to comply with the critical crack length of 3 mm. 1/2 Кiс, МPа m Aluminum (7075-T3) 30 Titanium Ti-6Al-4Va 55

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPa√m is exposed to a stress of 1030 MPa. Will this specimen experience fracture if it is known that the largest surface crack is 0.5 mm long? Why or why not? Assume that the parameter Y has a value of 1.0.
8.a) Calculate the theoretical fracture strength of a brittle material wherein fracture occurs by propagation of an elliptically shaped 0.25 mm surface crack with a 1.2 × 10-3 mm tip radius under an applied 1200 MPa stress. b) If the specific surface energy for a material is 0.30 J/m2 and its elastic modulus is 69 GPa, calculate the minimum stress required for propagation of a surface crack 0.05 mm in length. Based on this calculation, estimate the materials fracture toughness.
Draw the stress strain diagram for a ductile and brittle material and what is the difference in it? What do you understand by strain hardening? What do you mean by percentage reduction in area? Explain the steps in ductile fracture. Explain the modes of failure in tension test.
Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface crack of length 0.20 mm and that has a tip radius of curvature of 0.001 mm when a stress of 1450 MPa is applied. The question is attached. The answer is not 29000. WileyPlus marks it as incorrect.
Some aircraft component is fabricated from an aluminium alloy that has a plane strain fracture toughness of 35 MPa√m. It has been determined that fracture results at a stress of 250 MPa when the maximum (or critical) internal crack length is 2.0 mm. For this same component and alloy, show that whether fracture will or will not occur if the stress level is at 325 MPa and the maximum internal crack length is 1.0 mm.
1. Explain what is meant by the term fast fracture, stating its causes, and give two examples from which it might occur. 2. Briefly describe, with the aid of a sketch in each case, the appearance of a fracture surface that has undergone (i) ductile tearing and (ii) cleavage.3. Explain, with the aid of a diagram, how a crack propagates by ductile tearing within the plastic zone of an engineering metal.4. Explain, with the aid of diagrams, how crack propagation is affected by the presence of the fibers in glass fibre reinforced resins.5. With the aid of a sketch, describe and explain the fracture surface characteristics of a metal component that has undergone fatigue failure. 6. By referring to graphical representations of fatigue test results, explain the terms S-N curve, Fatigue Limit and Endurance Limit. Please answer all parts
. Suppose that a wing component on an aircraft is fabricated from analuminum alloy that has a plane strain fracture toughness of 40 MPa√m. It has been determined that fracture results at a stress of 365MPa when the maximum internal crack length is 2.6 mm. For thissame component and alloy, compute the stress level at whichfracture will occur for a critical internal crack length of 4.0 mm.
The Kic value of a steel is M within a square root of 186 MPa. If the stress to which the steel is exposed is 800 MPa, what is the maximum crack length that can be tolerated? (Take Y = 1.1)
Some aluminum aircraft components have a KIc = 35 MPa(m)1/2. It has been determined that failure occurs at a stress of 250 MPa when the critical internal crack length is 2 mm. Will this component achieve failure at a stress of 325 MPa when the critical internal crack length is 1.1 mm?
Consider a steel plate with a through-thickness edge crack like the one shown in Fig. 6.21f. The plate width (W) is 75 mm, and its thickness (t) is 12.0 mm. Furthermore, the plane-strain fracture toughness and yield strength values for this material are 80 MPa m1/2 and 1200 MPa, respectively. If the application in which the plate is used is expected to cause a stress of 300 MPa along the axis perpendicular to the crack, would you expect failure to occur if the crack length a is 15 mm? Explain.
1.) Assume that a wing component on an airplane is made of an aluminum alloy with a plane strain fracture toughness of It was found that when the maximum internal crack length is 2.5 mm, breakage occurs at a load of 365 MPa. Find the stress level at which a critical internal crack length of 5.0 mm will fracture for the identical component and alloy. 2.) An S-five ninety alloy specimen nine hundred mm long will be subjected to eighty MPa tensile stress at eight hundred and fifteen degrees celcius. Later after five thousand of hours, compute its elongation. Consider a sum of one point five mm in the both immediate and main creep elongations. - Please answer this 2 and indicate the givens. Thank you
An Al2O3 specimen is being pulled in tension. The specimen contains flaws having a size of 100 µm. (a) If the surface energy of Al2O3 is 0.8 J/m2, what is the fracture stress? Use the Griffith criterion. E = 380 GPa. (b) Using your vast fracture mechanics knowledge and advanced equations, estimate the fracture stress if the fracture toughness is 4 MPa m1/2. Assume two positions for flaw: in the center of an infinite body and at the edge.