Answer whats in the image, please and thank you Compute the expected properties of modulus of elasticity (Ec) of a composite made from S-glass fibers and a Polyester matrix. Thevolume fraction of fibers is 30%. (Unit is psi.)Properties of Sample Matrix and Filler MaterialsTensile strengthTensile modulusSpecific weightksiMPa10° psiGPaIbinIN/mMatrix materials:PolycsterЕрохуAluminum10690.402.760.04712.7181240.563.860.04712.74531010.0* 690.10027.1Titanium170117016.51140.16043.4Filler materials:S-glassCarbon-PANCarbon-PAN (high-strength)Carbon (high-modulus)600414032405650220012.586.20.0924.447033.5402310.06417.48202760.06517.73251006900.07821.2Aramid500345019.01310.05214.1

Answered: Image /qna-images/answer/29a5e9e4-8156-48cb-898a-f2ceb90c320e.jpg

Answered: Compute the expected properties of…

Compute the expected properties of modulus of elasticity (Ec) of a composite made from S-glass fibers and a Polyester matrix. The volume fraction of fibers is 30%. (Unit is psi.)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Make introduction First paragraph: Generally, explain thermoplastic fundamental and their demand in…

A: These are a kind of plastics which can be recycled under the influence of heat many a times and…

Q: List three main classification of engineering Fibre-reinforced composites. Name one example of both…

A: List three main classifications of engineering Fibre-reinforced composites. Name one example of both…

Q: 3. The geometry of the reinforcing phase in a composite greatly determines the overall properties.…

Q: For a continuous and aligned fiber-reinforced composite, the modulus of elasticity in the transverse…

A: Given Data: Modulus of elasticity of matrix phase, Em=3.78 GPa

Q: In sandwich composites, core material dissipates most shear stresses caused by O Longitudinal forces…

A: FORCES THAT CAUSES MOST SHEAR STRESSES IN SANDWICH COMPOSITES ARE TRANSVERSE FORCES

Q: Please calculate UD composite material averaged mechanical constants EL; Er; VEr; Gu Fiber and…

Q: d%3D50 nm, di = 4 nm, and ECNT oisson's ratio for this composite using strength of material

A: data providded Em=1.9 GPaEf = 900 GPa Vm =matrix volume fraction =0.98Vf =fiber volume fraction…

Q: Compute the modulus of elasticity for a composite which uses High Modulus Carbon fibers and…

A: Given: TO calculate the modulus of elasticity of the composite.

Q: Example 1 A continuous and aligned glass fiber-reinforced composite consists of 40 vol% of glass…

Q: An epoxy matrix is reinforced with 40 vol% E-glass fibers to produce a 2-cm diameter composite that…

Q: Describe the difference in mechanical properties as a function of temperature between a highly…

A: Plastics are used for various types of industrial work as well as day-to-day life.

Q: Problem 4 Calculate the tensile modulus of elasticity of a unidirectional…

Q: A continuous-aligned composite lamina is to be designed to have Ec,L= 200 GPa, Ec,T = 10 Q3. GPa and…

A: Hello. Since your question has multiple sub-parts, we will solve first three sub-parts for you. If…

Q: Compare and contrast properties of thermoplastics, thermosetting materials, and elastomers.

A: Question (A) is Solved here. For Question (B), Please Post this Question.

Q: Relate the changes of mechanical properties of polymer if the temperature increase. I. Decrease…

A: Concept: 1) Here they asked about mechanical properties, so youngs modulus and tensile strength will…

Q: i) Write down the constituent materials used in the manufacture of composites.

A: A composite material is composed of at slightest two materials, which combine to provide…

Q: In a polymer-polymer composite, the weight percentage of the polymer 1 and polymer 2 are 20% and 80%…

Q: Please tell in detail about macroscopic composites.

A: Given Data : Macroscopic composite

Q: By giving examples, describe FOUR fiber factors that affects the mechanical performance of composite…

A: Given question : By giving examples, describe FOUR fiber factors that affects the mechanical…

Q: Estimate the transverse modulus (ET), of the glass-epoxy composite with a fiber volume fraction of…

A: Given data: Modulus of elasticity of glass fiber, Ef = 70 GPa. Modulus of elasticity of epoxy, Em =…

Q: Answer the following questions. i) Define the term composites. ( ii) Explain the fibre reinforced…

A: (i) The composites are the material composed from two or more different materials that, when…

Q: length values of 1.5 × 10-2 mm and 7.5 mm, respectively. Given a fiber strength of 3500 MPa and a…

A: Tensile strength is the highest load a material can withstand without cracking when stretched,…

Q: An electrical contact material is produced by infiltrating copper into a porous tungsten carbide…

Q: On the basis of fiber length and orientation, which of the following results to an 'isotropic'…

A: in fiber reinforcement, If we want unidirectional property (homogeneous) we should use continuous…

Q: Which of these models would best give a description of viscoelastic behavior for polymers? Explain…

A: According to the problem, the various models with their strain behaviors are shown in the given…

Q: Calculate the composite elastic modulus for polyester reinforced with 60% volume fraction of carbon…

A: Given:60% volume fraction reinforced polyester,Epolyester=2900 MPaEcarbon fiber=175000 MPa

Q: ) To calculate the tensile strength of the fibre, the cross-sectional area has to be determined.…

A: given:

Q: What is the tensile strength of a composite fibre when its diameter is 20 microns and its critical…

Q: Q4: The well-known that glass fibers are widely used in the manufacture of composite materials: 1.…

A: Benefits of Glass Fiber: They are durable and withstand low to high temperatures in the range -40oF…

Q: Compute the modulus of elasticity for a composite which uses High Modulus Carbon fibers and…

A: Given data as per question Volume fraction of fibers = 25% Volume fraction of matrix = 75%

Q: persistence length that can be obtained by bending the polymer to form a 90 degree turn

A: The persistence length is a basic mechanical property quantifying the bending stiffness of a…

Q: d) A carbon fibre reinforced composite is made using a volume fraction of 77% carbon. The material…

A: volume fraction of carbon fibre, Vf = 77% = 0.77 volume fraction of Epoxy material, Vm = 1-Vf =…

Q: Consider a polymer reinforced with Spectra 1000 fibers, with a fiber volume ratio of x = 15 %. For a…

A: Generally polymer reinforced composite has two essential components: 1) Fibers- These are the…

Q: compare and contrast mechanical properties of lead and plastic

A: Mechanical properties are the physical characteristics that a material shows when forces are…

Q: Calculate the percentage increase in the mechanical properties of reinforced nylon from the data…

Q: 1. Explain with drawing the addition polymerization for PVC.

Q: Briefly Explain the properties of polymer that is related to crystallinity.

A: Given Crystallinity To find Polymer properties of crystallinity

Q: Is the following figure showing continuous or noncontinuous fibers What are the differences in…

A: Fibreglass and carbon fibre are both well-known reinforcing materials. Within the realm of…

Q: Compute the ultimate strength for a composite which uses Aramid fibers and Polyester matrix. The…

A: In this question, we need to determine the tensile strength of the composite σc=σmVm+σfvf here, σm…

Q: Consider an aligned fiber reinforced-polymer matrix composite for which the constituent fibers have…

A: Tensile strength is the highest load a material can withstand without cracking when stretched,…

Q: ition temperatu

A: introduction: The glass transition temperature is the temperature range at which the polymer…

Q: If the tensile strength of the Kevlar 49 fibers is 3.8 GPa and that of the epoxy resin is 75.9 MPa,…

A: The tensile strength of the composite material is 2.422 GPa. The fraction of load carried by the…

Concept explainers

Engineering Drawing

Technical drawing has been around since ancient times. As in the ancient Renaissance, complicated drawings were created, including Leonardo da Vinci's drawing. Modern engineering drawing, including its specific orthographic projection with scale conventions, began in Europe (France) during the early stages of Industrialization. L.T. C. Rolt also made some of Marc's drawings for its block-making machinery (in 1799) that also may have contributed significantly to British engineering technology. Since he learned the art of presenting three-dimensional(3D) items in a two-dimensional(2D) plane, as we now term mechanical drawing. 

Question

Answer whats in the image, please and thank you

Compute the expected properties of modulus of elasticity (Ec) of a composite made from S-glass fibers and a Polyester matrix. The
volume fraction of fibers is 30%. (Unit is psi.)
Properties of Sample Matrix and Filler Materials
Tensile strength
Tensile modulus
Specific weight
ksi
MPa
10° psi
GPa
Ibin
IN/m
Matrix materials:
Polycster
Ероху
Aluminum
10
69
0.40
2.76
0.047
12.7
18
124
0.56
3.86
0.047
12.7
45
310
10.0
* 69
0.100
27.1
Titanium
170
1170
16.5
114
0.160
43.4
Filler materials:
S-glass
Carbon-PAN
Carbon-PAN (high-strength)
Carbon (high-modulus)
600
4140
3240
5650
2200
12.5
86.2
0.09
24.4
470
33.5
40
231
0.064
17.4
820
276
0.065
17.7
325
100
690
0.078
21.2
Aramid
500
3450
19.0
131
0.052
14.1

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Estimate the transverse modulus (ET), of the glass-epoxy composite with a fiber volumefraction of 25%. Modulus of elasticity of glass fiber and epoxy is 70 GPa, and 3.5 GPa,respectively. Assume that fibers have a circular cross-section.
Glass fibres provide longitudinal reinforcement for a nylon material subject to tensile load. The fibre diameter is 20 μm and the volume fraction is 0.45. (Take Young’s modulus of glass fibres as 70 000 MPa and nylon as 2800 MPa)(i)Calculate the Young’s modulus of composite(ii)Determine the tensile strength in the glass fibre if the tensile strength of the composites and matrix is 14 MPa and 11.8 MPa, respectively
A flat body panel of a Lockheed Martin F25 is to produce using a unidirectional fiber/epoxy matrix composite with constituent properties: Ef1 = 230 GPa, Ef2 = 14 GPa, and Em = 3,50 GPa. Estimate the longitudinal moduli of the composite. The dimensions of this composite are 3 cm by 3 cm by 0,35 cm, weighing 3 g. After an acid digestion process, the remaining fibers weighed 1,7 g. From a separate test, the epoxy and fibers were found to be 1,2 and 1,9 g/cm3 , respectively. With these fiber and matrix constituents, what are the maximum possible values of E1 and E2?
Q#04 (a) : What are composite materials? Discuss the functions of Re-inforcing agent and matrix materials. (b) : Name different types of advanced fibres.
Question 1 A composite material consists of 40% parallel carbon fibres with a Young’s modulus of 405 GPa in a matrix of epoxy resin with a Young’s modulus of 2.5 GPa. Calculate the Young’s modulus of the composite in the parallel and in the perpendicular directions of the fibres. Use the graphical method seen in class to show the possible value of the overall young modulus of your composite material.
The compressive strength of aramid fiber is about one-eighth of its tensile stress. Estimate the smallest diameter of a rod on which the aramid fiber can be wound without causing kinks, etc. on its compression side. How to find the diameter based on bending moment and formula, MR = EI?
A large-particle composite consisting of tungsten particles within a copper matrix is to be prepared. If the volume fractions of tungsten and copper are 0.70 and 0.30, respectively, a) Compute the modulus of elasticity of this composite in the longitudinal direction. (The upper limit) and the modulus of elasticity in the transverse direction. (The lower limit), given the data that follow. Modulus of Elasticity (GPa) Copper 110 Tungsten 407 b) If the cross-sectional area is 280 mm2 and a stress of 60 MPa is applied in this longitudinal direction, compute the magnitude of the load carried by each of the fiber (tungsten) and matrix (copper) phases.
A 0 degree lamina of glass fiber-epoxy 3501 composite with fiber arranged withmax. volume fraction of fiber in a square array is subjected to a stress σx = 50MPa at theta =20 degrees. What are the resulting lamina strains [ε]xy and strains[ε]12? (Apply the Halpin-Tsai correction to transverse moduli and shear moduli)
Boron coated with SiC reinforced aluminum containing 40 vol.% fibers is animportant high temperature, light weight composite material. Estimate the density, modulus of elasticity, and tensile strength of composite parallel to the fiber axis. Also estimate the modulus of elasticity of composite perpendicular to the fibres.
When a beam 6 m long with a cross-sectional area of 19.4 cm2 is subjected to a compression force of 16 x 104 N, its length is shortened by 4.5 mm. What is the Young’s Modulus for the beam?
An epoxy matrix is reinforced with 40 vol% E-glass fibers to produce a 2-cm diametercomposite that is to withstand a load of 25,000 N. Calculate the stress acting oneach fiber.
The compressive strength of aramid fiber is about one-eighth of its tensile stress. Estimate the smallest diameter of a rod on which the aramid fiber can be wound without causing kinks, etc. on its compression side.