length values of 1.5 × 10-2 mm and 7.5 mm, respectively. Given a fiber strength of 3500 MPa and a fiber-matrix bond strength of 7 MPa for this composite, which of the following equations should be used to determine the tensile strength in the direction of fiber alignment? Ooom (1 V₂) +oj Vj 0 - = 0;v/₁ (1 - 1) + (1 - V₁) 21

length values of 1.5 × 10-2 mm and 7.5 mm, respectively. Given a fiber strength of 3500 MPa and a fiber-matrix bond strength of 7 MPa for this composite, which of the following equations should be used to determine the tensile strength in the direction of fiber alignment? Ooom (1 V₂) +oj Vj 0 - = 0;v/₁ (1 - 1) + (1 - V₁) 21

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Calculate the density of a composite made with 35% Kevlar-49 fibers in an epoxy resin (ρ = 1.1 kg/m3, E = 2.5 GPa). For Kevlar-49, Ef = 131 GPa; density = 1440 kg/m3
Estimate the transverse modulus (ET), of the glass-epoxy composite with a fiber volumefraction of 25%. Modulus of elasticity of glass fiber and epoxy is 70 GPa, and 3.5 GPa,respectively. Assume that fibers have a circular cross-section.
Original question: The nominal engineering constants of a unidirectional graphite epoxy ply are given in Table below for a fiber volume fraction of 60 percent. The fiber volume is reduced to 55 percent. Estimate the engineering constants for this reduced fiber volume fraction. New question needing to be answered: Repeat with a reduced fiber volume fraction of 40 percent representative of lower fiber volume fraction materials. Table:
What fiber fraction would be required for a composite with titanium fibers in a polycarbonate matrix (E = 2.5 GPa) to have the fibers handle 85% of a longitudinal tensile load? (Titanium Ef = 116 GPa )
If the tensile strength of the Kevlar 49 fibers is 3.8 GPa and that of the epoxy resin is 75.9 MPa, calculate the tensile strength of the composite material in Q3b(i). Calculate the fraction of load carried by the Kevlar 49.
The compressive strength of aramid fiber is about one-eighth of its tensile stress. Estimate the smallest diameter of a rod on which the aramid fiber can be wound without causing kinks, etc. on its compression side.
Boron coated with SiC reinforced aluminum containing 40 vol.% fibers is animportant high temperature, light weight composite material. Estimate the density, modulus of elasticity, and tensile strength of composite parallel to the fiber axis. Also estimate the modulus of elasticity of composite perpendicular to the fibres.
A reinforced plastic sheet is to be made of a matrix with a tensile strength of 60MN/m^2 and a continuous glass fibre with a modulus of 76GN/m^2.If the resin ratio by volume is 70% and the modular ratio of the composite is 25, estimate the tensile strength and modulus of the composite.
Boron coated with SiC reinforced aluminium containing 40 vol.% fibers is animportant high temperature, light weight composite material. Estimate the density,modulus of elasticity and tensile strength of composite parallel to the fiber axis. Alsoestimate the modulus of elasticity of composite perpendicular to the fibres.
Question 1 A composite material consists of 40% parallel carbon fibres with a Young’s modulus of 405 GPa in a matrix of epoxy resin with a Young’s modulus of 2.5 GPa. Calculate the Young’s modulus of the composite in the parallel and in the perpendicular directions of the fibres. Use the graphical method seen in class to show the possible value of the overall young modulus of your composite material.
When answering the following questions , ensure that you explain in terms of both the microscopic and macroscopic structure of the materials. A) polymer - explain the difference in structure between a thermoplastic and thermoset material and explain how the structure accounts for the key generic properties of those polymers. B) composite material - for a particular composite and a fibre reinforce composite , explain the difference in structure and whst structual features dictate the properties of the material.
Alice is conducting a tensile test on continuous fiber alignment compositesamples. She found that the results are different in the longitudinal andtransverse directions of the samples. Explain why this happens with the aid ofdiagram.