Elastic Recovery After Plastic Deformation A cylindrical specimen of a brass alloy 6.8 mm (0.27 in.) in diameter and 80.1 mm (3.16 in.) long is pulled in tension with a force of 4760 N (1070 Ibf); the force is subsequently released. Compute the final length of the specimen at this time. The tensile stress-strain behavior for this alloy is shown in Animated Figure 7.12. Part 1 What is the applied stress at 4760 N in MPa? O = i MPa

Elastic Recovery After Plastic Deformation A cylindrical specimen of a brass alloy 6.8 mm (0.27 in.) in diameter and 80.1 mm (3.16 in.) long is pulled in tension with a force of 4760 N (1070 Ibf); the force is subsequently released. Compute the final length of the specimen at this time. The tensile stress-strain behavior for this alloy is shown in Animated Figure 7.12. Part 1 What is the applied stress at 4760 N in MPa? O = i MPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A student conducted an experiment to determine the behavior of poly (ethylene) and poly (tetrafluo-roethylene) to stress. The tables below depict the results of his experiments. Part 1.1Plot the stress-strain curves for both types of material. Calculate their respective Young’s moduli (E). Howdo they compare? Part 1.2From their respective plots, determine their approximate strain energy before plastic deformation begins.How do they compare? Part 1.3What do these calculations of young’s modulus and strain energy tell us about the properties of bothmaterials? Compare the properties of both materials using these calculations.
A ductile specimen that has an initial length of 10 cm is tested under uniaxial loading. If the test is under tension and the nominal strain is 21.9%, please calculate the true strain in %.
Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm2 when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson’s ratio for both metallic rods. Justify your answer with reasons.
A cylindrical specimen of aluminum having a diameter of 19 mm (0.75 in.) and length of 200 mm(8.0 in.) is deformed elastically in tension with a force of 48,800 N (11,000 lbf). Using the data inTable 6.1, determine the following:(a) The amount by which this specimen will elongate in the direction of the applied stress.(b) The change in diameter of the specimen. Will the diameter increase or decrease? (Complete Answer, Thank you)
A specimen of copper having a rectangular cross section 1.20 in. x 1.5 in.) is pulled in tension with 20,000lbf force, producing only elastic deformation. Calculate the resulting strain.
20. The young’s modulus of nickel is 209 gpa. Determine the length of the bar (in mm) when a force of 6.82kn is applied to a 12.5mm x 7.5mm bar originally 900 mm long without causing plastic deformation.
You must perform mechanical tests with a linear elastic material (the material follows Hooke's law) applying forces (tension) in the range 0 to Fmax/2 for Sample A and between 0 to Fmax for Sample B. The samples are made of same material but have different geometries (see illustration). (a) Which of the two samples receives the maximum stress (σmax)? (b) Which of the two samples will have the larger length change (ΔLmax)? (c) Plot the expected curves for the two samples in the force-length and stress-strain planes. (d) Clearly indicate the values that the variables force, length, stress, and strain take at the beginning and end of each curve.
Stress Strain-Behavior A specimen of aluminum having a rectangular cross section 10 mm × 12.7 mm(0.4 in.× 0.5 in. ) is pulled in tension with 35,500 N (8000 lbf) force, producing onlyelastic deformation. Calculate the resulting strain.
A three-point bending test is performed on a silicon carbide block that is 10 cm long, 1.5 cm wide, and 0.6 cm thick, and that is supported by two separate supports.7.5 cm. The sample breaks when a bending of 0.09 mm is recorded. The flexural modulus of silicon carbide is 480 GPa. Assume that no plastic deformation has occurred. Calculate: (a) The force that caused the fracture and(b) Flexural strength.
A Copper specimen of circular cross-section is subjected to a tensile test. The data obtainedare:Length of Specimen = 329 mm;Diameter of Specimen = 39 mm;Load at Yield Point = 130 kN;Maximum Load = 219 kN;Load at fracture = 118kNDetermine the following:1) Find initial area of the test specimen2) Yield Stress3) Ultimate Stress4) Fracture stress5) Find the strain for 0.058mm elongation.6) Mark Yield stress, Ultimate stress and Fracture stress on a Stress-Strain diagram.
A commercially-pure copper wire originally 10.00 m long is pulled until its final length is 10.10 m. It is annealed, then pulled again to a final length of 10.20 m. What is the engineering strain associated with each of the two steps in the process? What is the true strain for each step? What are the total engineering and true strains for the combined steps? Finally, what agreement (if any) is there between the total strains calculated as the sum of two steps of 0.10 m vs. a single step of 0.20 m?
A titanium alloy specimen with an elastic modulus of 107 GPa and 3.9 mm in original diameter will experience elastic deformation when applied to a tensile load of 2695.2 N. Calculate the maximum length the specimen would reach if the maximum allowable elongation is 0.4 mm.