•Find the Miller indices for the points in the cubic unit cell below: Note: J is on the left face of the cube, H is on the right face, Kis on the front face and I is on the back face A G H K G E . .. ..

•Find the Miller indices for the points in the cubic unit cell below: Note: J is on the left face of the cube, H is on the right face, Kis on the front face and I is on the back face A G H K G E . .. ..

Understanding Motor Controls

4th Edition

ISBN:9781337798686

Author:Stephen L. Herman

Publisher:Stephen L. Herman

Chapter44: Semiconductors

Section: Chapter Questions

Problem 4RQ

See similar textbooks

Related questions

Q: Na transforms from bcc to hcp when temperature is 23K. Assuming the density remains fixed and the…

A: Given, The lattice spacing in BCC is, aBCC=4.23 A0

Q: 10. Lithium crystallizes in a bcc structure with an edge length of 3.509 Å. Calculate its density.…

Q: a) Determine the miller indices for the directions in the cubic unit cell?

A: Given:

Q: A) Lithium crystallizes in the body-center cubic structure with an edge length of 350.9 pm.…

Q: One slip system for the BCC crystal structure is {110}(111). In a manner similar to Figure 7.6b,…

Q: Calculate the atomic packing factor for a material with body centred cubic structure.

A: Given: Body Centred Cubic structure

Q: Silver crystallizes as fcc structure. If the density of silver is 10.51g/cm3. Calculate the volume…

Q: Calculate the number of vacancies per cubic meter for some metal, M, at 749°C. The energy for…

A: No. of vacancies per cubic meter = ?temperature = 749°cenergy formation = 0.84 eV/atomdensity = 8.18…

Q: Choose the correct examples of face centered cubic structure in the following options.

A: Ans is Gold and Aluminum.

Q: Q 5: In the cubic cell unit find: A- Miller's indices of the directions shown in Figure (4) B-…

A: Miller indices: It is a set of three number which shows the orientation of a set of parallel planes…

Q: in cubic structure Write down the CORRECT direction that is perpendicular to the miller indices…

A: There are 4 directions that are perpendicular to the miller indices[0,0,1] are 1 1 0,-1-1 0,-1 1…

Q: Vanadium has the Body-Centered Cubic (BCC) crystal structure shown in the figure below. The radius…

A: Given bcc vanadium r=0.132nm

Q: Given the crystal plane, give the miller index

A: Direction of black arrow in Miller indices Tail side: a1 = 0 a2 = 0 a3 = 0 c = 1 Head Side: a1 =…

Q: Q2. Find Atomic packing factor for Simple Cubic, Body Centered Cubic, Face centered Cubic and…

Q: Sodium chloride (NaCl) is a ceramic that has the following crystal structure. Given: R(Na*)= 0.098…

A: NaCl has a FCC crystal unit cell,

Q: Determine the Miller indices for the direction shown in cubic cell. Use the minus symbol to…

Q: Calculate the number of vacancies per cubic meter for some metal, M, at 850°C. The energy for…

A: We have to find Calculate the number of vacancies per cubic meter

Q: 1- Determine miller indices of direction A, B an Can planes A, B an C in figures below,…

A: Hello. Since you have posted multiple questions and not specified which question needs to be solved,…

Q: Calculate the atomic radius in cm for the following= BCC metal with a. 0.85634 nm

Q: Explain why there is no face-centered tetragonal Bravais lattice.

A: FACE CENTERED CELL In complete unit cells, there are also atoms or ions in the middle of all six…

Q: Show how to get this indices miller bravais for a HCP structure, right from the 3 indices used on…

Q: Platinum is a metal having a FCC crystal structure with a density p= 21.45 kg/m3. Calculate the…

Q: 9. Calculate the planar atomic density for the (100), (110) and (111) planes for a BCC (body…

A: Planar density is given as - Densityρ =Number of atomsArea of plane

Q: Molybdenum has a BCC crystal structure, an atomic radius of 0.1363 nm, and an atomic weight of 95.94…

Q: The expression linear atomic density is derived for the FCC [111], [100] vectors in terms of radius…

A: FCC,100Planer density PD100=Number of atoms in plane 100area of plane 100Since in plane FCC100…

Q: Calculate BC, FC and FE Rod forces in the lattice system?

Q: Iron exhibits an allotropic behavior change of solid state structure in such a way that when it is…

Q: Q 7(a): Derive planar density expressions for FCC (100) and (111) planes in terms of the atomic…

Q: Given that molybdenum (Mo) with atomic weight 95.94 g/mol and density 10.2 g/cm3 assumes a…

Q: If the atomic radius of a metal that has the facecentered cubic crystal structure is 0.137…

A: In face centered cubic structure one atom is located at the center of the faces of cube

Q: Calculate the lattice constant of the alloy you found in part (a). Assume the alloy and its end…

A: Given data, The alloy is Zinc Blende (ZnS) Atomic radius of ZnS, aZnS=5.409 A° To determine, the…

Q: Calculate the planar densities of Li+1 and Cl-1 ions on the (111) plane for LiCl, which has the NaCl…

A: Given, LiCl has NaCl type structure. So at 4 corners we have Li+ atoms and at remaining 4 corners we…

Q: Indices of direction. If [hkl] are indices of a set of directions relative to lattice vectors a, as,…

A: Hedonism is a theory of values which states that pleasure is intrinsically valuable and pain is…

Q: Molybdenum, a BCC metal has an atomic radius of 0.136 nm. (a) Calculate the d-spacing for the (211)…

Q: A metal crystallizes in the face‑centered cubic (FCC) lattice. The density of the metal is 12020…

Q: Draw the [1 1 0], [-1 1 0], [ 0 -1 -1] directions for FCC and prove they are crystallographically…

A: [ 1 1 0 ] => Miller Indices

Q: Suppose one has measured the lattice parameter a of face-centred cubic (fcc)-Fe as a function of the…

A: Use the tie-line rule as the most convenient method. According to this method, the volume of the…

Q: Vanadium has the Body-Centered Cubic (BCC) crystal structure. The edge length "a" of the unit cell…

A: It is given that Vanadium at room temperature of 20°C is having a BCC structure. In a BCC structure,…

Q: B) Consider the tetragonal unit cell (a) Sketch the correct direction as shown Fig.1(a) below…

Q: Determine the Miller indices of the cubic crystal plane that intersects the following position…

A: given position coordinates(points): (1, ½, 1), (½, 0, ¾), and (1, 0, ½) To determine the Miller…

Q: The equilibrium fraction of lattice sites that are vacant in an metal at 900 0C is 6.17 x 10-5. a)…

Q: calculate the planar density atoms per square millimeter for the following crystal planes in body…

A: No of atoms in plane = 2 Area of plane = √2 a2 Density = atoms/area 1 nm = 10-6 mm

Q: A hypothetical tetrahedral crystal has the following lattice parameters: a = b = 0.40 nm, c = 0.5…

A: Given details: a=b=0.4 nmc=0.5 nmα=β=γ=90°

Q: Explain Face centered cubic structure with neat diagram and calculate the atoming packing…

Q: Rough sketch of crystal planes

A: Draw the intercept of the plane as shown below.

Q: Suppose we introduce one carbon atom for every 100 iron atoms in an interstitial position in BCC…

A: Since there is one atom of carbon per 100 atoms of iron, there will be 1/50 C per unit cell because…

Q: 9. Equations 7.1a and 7.1b, expressions for Burgers vectors for FCC and BCC crystal structures, are…

A: For FCC,r=a22For aluminum metal,r=0.1431nma=22ra=22(0.1431)a=0.4047nmFor BCC,r=a34For chromium…

Q: Consider the planes with Miller indices (100), (001) and (111). The lattice is FCC and the indices…

Q: If the atomic radius for Pb- 0.175nm and the crystal structure is FCC, calculate the atoms numbers…

A: Calculated number of Atom in unit cell. And relation between atomic radius and lattice constant and…

Q: Identify the correct example for Face Centered Cubic structure from the following options Select…

A: Since you have asked multiple questions in a single request, we would be answering only the first…

Concept explainers

The Space Lattice and Unit Cells

Every matter consists of atoms, molecules, and ions. If these atoms, molecules, and ions (micro-particles) are represented in a three-dimensional space-occupying certain specific points in space, then these arrangements are termed as space lattices and the specific points which are being occupied by atoms, molecules and ions are termed as lattice points. The atoms, molecules, and ions at the lattice points are generally grouped in a regular fashion and repeat periodically at the three-dimensional space.

Question

Find the Miller indices for the points in the cubic unit cell
below:
Note: J is on the left face of the cube, H is on the right face,
Kis on the front face and I is on the back face
A
C
F
D
G
D
E
H
K
В
J
E
K

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step by step

Solved in 4 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Principal Metallic Crystal Structures and Crystal Structure Analysis

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Show how to get this indices miller bravais for a HCP structure, right from the 3 indices used on cubic structures (hkl).
Niobium (Nb) and Vanadium (V) have the BCC crystal structure, and Ag forms a substitutional solid solution at room temperature. Calculate the unit cell edge length (nm) for a 25 wt% Nb-75 wt% V alloy
Calculate the planar densities of Li+1and Cl-1ions on the (111) plane for LiCl, which has the NaCl crystalstructure. Ionic radii are 0.078 nm and 0.181 nm for Li+and Clrespectively
Obtain the Miller indices of a plane which intercepts at a, b/2, 3c in a simple Cubic unit cell. Draw a neat diagram showing the plane.(Where a, b, c are lattice parameters
Calculate the fraction of vacant lattice sites for pure copper at 1080oC. The value of the activation energy to create a vacancy in copper is 0.90 eV, its density is 8.94 g/cm3 and its melting point is 1085oC.
Calculate the number of vacancies per cubic meter in gold (Au) at 900C. The energy for vacancy formation is 0.98 eV/atom. Furthermore, the density and atomic weight for Au are 18.63 g/cm3 (at 900C) and 196.9 g/mol, respectively.
in cubic structure Write down the CORRECT plane indices that is perpendicular to the miller indices (002)
Determine the Miller indices for the following planes, show the procedure you follow to obtain the index
Determine the Miller Indices of Direction C and D in an HCP crystal.
If the atomic radius for Pb- 0.175nm and the crystal structure is FCC, calculate the atoms numbers in the unit cell, find the relation between atomic radius and lattice constant and what is the atomic packing factor
in cubic structure Write down the CORRECT direction that is perpendicular to the miller indices [001]
Determine the possible crystal structure of Zinc Blende structure (ZnS), if the radii are as follows Zn+2 = 0.074 and S-2 = 0.184.