2) Find the strains in the 1-2 coordinate system (local axes) in a unidirectional boron/epoxylamina with 50% fiber volume fraction, if the stresses in the 1-2 coordinate systemapplied to are ơ1 = 6 MPa, ơ2 =2 MPa, and T12 = -4 MPa. Use the properties of the givenunidirectional lamina in the book and assume plane stress conditions for the lamina.

Given data: Standard data for boron/epoxy is

Find the strains in the 1-2 coordinate system (local axes) in a unidirectional boron/epoxy lamina with 50% fiber volume fraction, if the stresses in the 1-2 coordinate system applied to are Ơi = 6 MPa, ơ2 =2 MPa, and T12 = -4 MPa. Use the properties of the given unidirectional lamina in the book and assume plane stress conditions for the lamina.

Find the strains in the 1-2 coordinate system (local axes) in a unidirectional boron/epoxy lamina with 50% fiber volume fraction, if the stresses in the 1-2 coordinate system applied to are Ơi = 6 MPa, ơ2 =2 MPa, and T12 = -4 MPa. Use the properties of the given unidirectional lamina in the book and assume plane stress conditions for the lamina.

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter7: Analysis Of Stress And Strain

Section: Chapter Questions

Problem 7.6.2P: An element of aluminum is subjected to tri- axial stresses. Calculate the strains in the element in...

See similar textbooks

Similar questions

An element of aluminum is subjected to tri- axial stresses. Calculate the strains in the element in and directions if the stresses are -20 MPa, 28 MPa, and -18 MPa. respectively. Assume E = 70 GPa and v = 0.33. Also, find the strain energy density of the element.
Determine the strain energy per unit volume (units of psi) and the strain energy per unit weight (units of in ) that can be stored in each or the materials listed in the accompanying table, assuming that the material is stressed to the proportional limit. DATA FOR PROBLEM 2.7-5 Material Weight Density (lb/in3) Modulus of Elasticity (ksi) Proportional Limit (psi) Mild sleel 0.284 30,000 36,000 Tool steel 0.284 30,000 75,000 Aluminum 0.0984 10,500 60,000 Rubber (soft) 0.0405 0.300 300
A 4.75-in, outside diameter polyethylene pipe designed to carry chemical waste is placed in a trench and bent around a quarter-circular 90° bend (see figure). The bent section of the pipe is 52 ft long. Determine the maximum compressive strain If the normal strain cannot exceed 6.1 × 10-3 , what is the maximum diameter of the pipe? If d = 4.75 in., what is the minimum acceptable length of the bent section of the pipe?
A joint between two glass plates A and B is filled with a flexible epoxy that bonds securely to the glass. The height of the joint is/p = 0.5 in, its length is L = 30 in, and its thickness is/ = 0.5 in. Shear force of I' = 25 kips is applied to the joint. Calculate the displacement of the joint if the shear modulus of elasticity G of the epoxy is 100 ksi. Calculate the average shear strain in the epoxy.
A solid spherical ball of magnesium alloy (E = 6.5 × l0-6 psi, v = 0.35) is lowered into the ocean to a depth of 8000 ft. The diameter of the ball is 9.0 in. (a) Determine the decrease ?d in diameter, the decrease, ?V in volume, and the strain energy U of the ball. (b) At what depth will the volume change be equal to 0.0324% of the original volume?
An clement of material subjected to plane strain (see figure) has strains of x=280106 , y=420106 , and xy=150106 . Calculate the strains for an element oriented at an angle = 35°. Show these strains on a sketch of a properly oriented element.
A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?
(a) Solve part (a) of the preceding problem if the pressure is 8.5 psi, the diameter is 10 in., the wall thickness is 0,05 in., the modulus of elasticity is 200 psi, and Poisson's ratio is 0.48. (b) If the strain must be limited to 1.01, find the maximum acceptable inflation pressure
A circular aluminum tube of length L = 600 mm is loaded in compression by forces P (see figure). The outside and inside diameters are d2= 75 mm and d1= 63 mm, respectively. A strain gage is placed on the outside of the lube to measure normal strains in the longitudinal direction. Assume that E = 73 GPa and Poissons ratio is v = 0.33. (a) IF the compressive stress in the tube is 57 MPa, what is the load P? (b) If the measured strain is e = 78 J X 10-6, what is the shortening
Solve the preceding problem if the cross- sectional dimensions are b = 1.5 in. and h = 5.0 in., the gage angle is ß = 750, the measured strains are = 209 × 10-6 and B = -110 × 10, and the material is a magnesium alloy with modulus E = 6.0 X 106 psi and Poisson’s ratio v = 0.35.
An element of aluminum is subjected to tri-axial stresses. Calculate the strains in the element in x, y, and z directions lithe stresses axayand az are -2000 psi, 3500 psi, and 2700 psi, respectively. Assume E = 10,000 ksi and v = 0.33. Also, find the unit volume change of the element.
The normal strain in the 45n direction on the surface of a circular tube (sec figure) is 880 × 10 when the torque T = 750 lb-in. The tube is made of copper alloy with G = 6.2 × 106 psi and y = 0.35. If the outside diameter d2of the tube is 0.8 in., what is the inside diameter dt? If the allowable normal stress in the tube is 14 ksi, what is the maximum permissible inside diameter d?