For the system shown in Figure 1A. The fillet of 6 mm radius for this member is critical. Considering points C and D in Figure 1B, calculate a conservative value of n, if: Sut = 295 MPa Suc = 899 MPa Consider the material to be brittle. 100 М, — Fz. 100 Мy 3 Fx. 200 Fx F2 T-Fx. 100 200 Fz Fx -d = 30 r = 6 AMx d = 45 My T All dimensions in "mm" Figure 1A Figure 1B where (take the nearest integer): ID N 75 ID N 120 F, ID is your student ID number.

For the system shown in Figure 1A. The fillet of 6 mm radius for this member is critical. Considering points C and D in Figure 1B, calculate a conservative value of n, if: Sut = 295 MPa Suc = 899 MPa Consider the material to be brittle. 100 М, — Fz. 100 Мy 3 Fx. 200 Fx F2 T-Fx. 100 200 Fz Fx -d = 30 r = 6 AMx d = 45 My T All dimensions in "mm" Figure 1A Figure 1B where (take the nearest integer): ID N 75 ID N 120 F, ID is your student ID number.

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter1: Tension, Compression, And Shear

Section: Chapter Questions

Problem 1.7.1P: A high-strength steel bar used in a large crane has a diameter d = 2.00 in. (sec figure). The steel...

See similar textbooks

Similar questions

The rails of a railroad track are welded together at their ends (to form continuous rails and thus eliminate the clacking sound of the wheels) when the temperature is 60°F. What compressive stress ?? =6.5×10-6 /? is produced in the rails when they are heated by the sun to 120"F if the coefficient of thermal expansion a = the modulus of elasticity E = 30 × 106 psi?
A high-strength steel bar used in a large crane has a diameter d = 2.00 in. (sec figure). The steel has a modulus of elasticity E = 29 × 10 psi and Poisson’s ratio is v = 0.29. Because of clearance requirements, the diameter of the bar is limited to 2.001 in. when it is compressed by axial forces. What is the largest compressive load Pmaxthat is permitted?
If a key material has an ultimate strength of 120 ksi and a yield strength of 80 ksi and factor of safety N=2, what would be the design compressive stress in ksi? (a) 40 ksi (b) 60 ksi (c) 160 ksi (d) 240 ksi
10.3. Consider the state of stress shown below that exists at a location within a component made up ofa brittle material, where this brittle material has tensile and compressive ultimate strengths ofσ UT = 170 MPa and σ UC = 850 MPa, respectively. Has the material failed at this location in thecomponent? Please include a free body diagram.
See the set of bars for made of a material that has a yield strength of 350 MPa, determine the minimum h1 and h2 dimensions required. Apply a safety factor F.S. = 1.5 without flow. Each bar is 12 mm thick
An engine parts is being tested with a load of 60000 lb. The allowable tensile stress is 10000 psi, modulus of elasticity of 40x106 psi. If the original length of specimen is 42 inches with elongation not exceeding 0.0015 in, what diameter of the specimen is rejected? a. 4.2 in b. 3.0 in c. 2.5 in d. 5.17 in
If d=40 mm, L=796 mm, F=29 kN, T=1.7 kNm and fail stress=156 MPa, calculate the apparent factor of safety for this loading condition. Give your answer to 2 decimal places.
Given: Metal Specimen diameter x-sectiion (circular)= 0.55 in Gage Length= 2.030 in Fracture bccurved at 28,500 pounds final length= 2.30 in Final diameter= 0.43 in Determine: a) Ultimate tensile stress in ksi
Two rods are connected to each other and are restrained at top and bottom. The top portion is steel with modulus of elasticity equal to 200x10^3 MPa and coefficient of thermal expansion equal to 11.7x10^-6/C, the bottom is made up of brass with modulus of elasticity equal to 105x10^3 MPa coefficient of thermal expansion equal to 20.9x10^-6/"C. The temperaturé rose to 50°C from normal condition introducing stresses in the bar. Determine the force induced in the bar. Note: Final Answer in 4 decimal places.
A spherical tank contains an internal pressure of 3.0 MPa, the diameter is 16 m, the yield stress is 490 MPa. and the factor of safety is 2.5. Determine the required thickness I to the nearest millimeter.
A soft steel specimen has a BHN of 150, find the equivalent 29 tensile strength in MPa. A. 393 B. 503 C. 443 D. 533 What is the value of strain at yield point of 1-inch diameter C1030 as rolled steel in the stress-strain curve? A. 0.0012 B. 0.0015 C. 0.0017 D. 0.0022 A copper column of annular cross section has an outer diameter of 0.5 m. and is subjected to an axial loading of 5 kips. The allowable compressive stress is 2 ksi. Compute the wall thickness. A. 1.15 m B. 2m C. 0.8 m D. 1 m
An ASTM cast iron has minimum ultimate strengths of 32 kpsi in tension and 95 kpsi in compression. Find the factors of safety using Coulomb Fragile Mohr (CMF) and Modified Mohr (MM) theories for the following stress state. σx = −3 kpsi, σy = −9 kpsi, τx y = −4 kpsi