Hilda, Layla, and Saber were experimenting with a carbon steel rod in the chemistry laboratory. Hilda learned that the carbon steel has a strain hardening ratio of 0.841, yet it breaks at a force of 45 N. Layla and Saber calculated the 15 mm2 rod's yield limit. The information they got was lacking because they have failed to borrow an SEM, but they were able to calculate the spacing of the atoms. Determine the spacing of the atoms if the shear modulus is 0.3 GPa and the interatomic space is equal to 1.8 Å.

Hilda, Layla, and Saber were experimenting with a carbon steel rod in the chemistry laboratory. Hilda learned that the carbon steel has a strain hardening ratio of 0.841, yet it breaks at a force of 45 N. Layla and Saber calculated the 15 mm2 rod's yield limit. The information they got was lacking because they have failed to borrow an SEM, but they were able to calculate the spacing of the atoms. Determine the spacing of the atoms if the shear modulus is 0.3 GPa and the interatomic space is equal to 1.8 Å.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Bronze alloy, the following true stresses produce the corresponding plastic true strains, before to necking: On the basis of this information, compute the true stress necessary to produce a true strain of 0.25 and then find the engineering stress and strain at this point. True stresses (MPa) True strain 354 0121 70 018
An 8-cm-square bar of steel is found to contain a1-mm corner crack, oriented perpendicular to the length ofthe bar. If an axial stress is applied from 0 to 420 MPa at afrequency of once every 10 minutes, how long will it take forthe rod to fracture? The properties of the bar are:KIC = 90 MPa √m , σys = 1500 MPa, and the crack growthrelation is da/dN = 2 x 10-37 ΔK4, with da/dN and ΔKbeing given in units of m/cycle and Pa √m , respectively
10. A torsion test shows that the shear modulus of an aluminumspecimen is 4.6 x 106psi. When the same specimen is used in atensile test, the modulus of elasticity is found to be 12.2 x 106psi. Find the Poisson’s ratio for the specimen.
3. Molybdenum has a BCC crystal structure, an atomic radius of 0.1363 nm, and an atomic weight of 95.94 g/mol. Compute its theoretical density.4. For a brass alloy, the stress at which plastic deformation begins is 345 MPa and the modulus of elasticity is 103 GPa.a. What is the maximum load that may be applied to a specimen with a cross-sectionalarea of 130 mm2 without plastic deformation?b. If the original specimen length is 76 mm, what is the maximum length to which itmay be stretched without causing plastic deformation?
From the work of D. C. Jillson, Trans. AIME 188, 1129 (1950), the following data were taken relating to the deformation of zinc single crystals. The crystals have a normal cross-sectional area of 122 x 10-6 m2. ϕ = angle between loading axis and normal to slip plane λ = angle between loading axis and slip direction F = force acting on crystal when yielding begins a. Identify the slip system for this material. b. Calculate the resolved shear τRSS and normal σn stresses acting onthe slip plane when yielding begins. c. From your calculations, does τRSS or σn control yielding? d. Plot the Schmid factor versus the normal stress P/ A0 acting on the rod. At what Schmid factor value are these experimentally-measured yield loads at a minimum? Does this make sense?
A 50 mmm long circular rod of the AISI 1015 hot rolled steel with a diameter of 12.5 mm is loaded in tension to failure. From the test it is learnt that the yield strength = 315 MPa, the tensile strength = 420 MPa, the elongation at fracture = 39% and the reduction in area = 51%. It is also observed that 45% of the total elongation was uniform in nature prior to the onset of necking. a) What is the true strain at fracture? b) Calculate the true stress at the point of onset of plastic instability c) What is the the strength coefficient K for this steel?
A cylindrical specimen of aluminum having a diameter of 19 mm (0.75 in.) and length of 200 mm(8.0 in.) is deformed elastically in tension with a force of 48,800 N (11,000 lbf). Using the data inTable 6.1, determine the following:(a) The amount by which this specimen will elongate in the direction of the applied stress.(b) The change in diameter of the specimen. Will the diameter increase or decrease? (Complete Answer, Thank you)
Calculate is the largest size (mm) internal through crack that a thick plate of aluminum alloy 7075-T651 can support at an applied stress of: (a) three-quarters of the yield strength, and (b) one-half of the yield strength Assume Y = 1. Given: KIC = 24.2 MPa (sq. rt.(m) and σys = 495 MPa
You are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?
information: "When performing a tensile test of a metal, these values were found for stress and strain. the yield strength (YS) is stress at 0.2% plastic strain" The task: A 5 meter long rod of this material is loaded axially with a stress of 244 MPa.i. How long is the rod under load?ii. Then the bar is relieved, how long is it now?
During stress-strain test, the unit deformation at a stress of 35 MPa was observed to be 167 x 10^-6 m/m and at a stress of 140 MPa it was 667 x 10^-6. If the proportional limit was 200 MPa, what is the modulus of Elasticity (GPa)? What is the strain corresponding to a stress of 80 MPa?
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.