In a non-acid catalyzed step-growth polymerization between A-A and B-B monomers, the A groups are titratable by aqueous base (1 N) and [A-A] [B-B) = 6 mol.kg-1. a) What is the DP if it takes 100 mL of base to neutralize the reaction mixture at 700 minutes of reaction time (assuming the initial total weight 500 g)?.

In a non-acid catalyzed step-growth polymerization between A-A and B-B monomers, the A groups are titratable by aqueous base (1 N) and [A-A] [B-B) = 6 mol.kg-1. a) What is the DP if it takes 100 mL of base to neutralize the reaction mixture at 700 minutes of reaction time (assuming the initial total weight 500 g)?.

Organic Chemistry

8th Edition

ISBN:9781305580350

Author:William H. Brown, Brent L. Iverson, Eric Anslyn, Christopher S. Foote

Publisher:William H. Brown, Brent L. Iverson, Eric Anslyn, Christopher S. Foote

Chapter29: Organic Polymer Chemistry

Section: Chapter Questions

Problem 29.19P

See similar textbooks

Similar questions

Question 1 a. Briefly describe what is thermoplastic, thermoset plastic and elastomer. Give examples to clarify your answers. b. Briefly discuss the effect of thermodynamic on polymerization. c. What are important factors influencing the properties of polymers? Question 2 a. Discuss the suitable initiator to start an addition polymerization. b. Define what is auto-acceleration, what causes this effect and how to minimize this effect. c. Briefly discuss emulsion and suspension polymerization techniques. Question 3 a. Discuss the differences between condensation and addition polymerization. b. What requirement should be provided to achieve high yield and high molecular weight of polymer by condensation reaction? c. What is interfacial polymerization? Question 4 a. Describe biopolymer and synthetic polymer. Give examples to support your answer b. Briefly discuss the classification of polymers. c. Why polymers are widely used in our daily life? Question 5 a. Describe TWO (2) important…
What is the fraction of monomers (p) that have been used in a stepwise polymerisation reaction if the reaction solution started with a monomer concentration of 1.58 mol L-1 and now has a concentration of 0.231 mol L-1?
8. When an equilibrium step-growth polymerization is 99% complete, what fraction of the reaction mixture is still monomer (a) on mole basis and (b) on weight basis ?
Draw/sketch and describe a three dimensional representation of a isotactic polyvinyl bromide with a degree of polymerization equal to 6
A synthetic polymer was produced via addition polymerization to a degree of polymerization of 925 and an average molecular weight of 40,700 g/mol. Of those listed below, which is most likely that polymer? Explain and support
a copolymer is made up of 40.01% polystyrene 20.38% acrylonyl and 31.51% polybutadiene a) Calculate the Molar Fraction b) the Degree of Polymerization if there is a weight of 320, 000 gr of copolymer c) carry out the polymerization reaction d) What is the name of this polymer and e) Mention some applications of some monomer
An alternating copolymer is known to have a number averagemolecular weight of 100,000 g/mol and a number average degree ofpolymerization of 2210. If one of the mers is ethylene, which of styrene,propylene, tetrafluoroethylene and vinyl chloride (Figure 1c) is the othermer? Show your calculations.
Sketch and label the expected stress-strain curves at room temperature for lightly cross-linked poly(butadiene) and reinforced poly(methyl methacrylate). Compare the behaviour of each specimen in terms of modulus and toughness.
5.6 Nylon-11 is poly(Ω-aminoundecanoic acid). In the polymerization of Ω-aminoundec-anoic acid, H2N(CH2)10COOH, to produce this polymer, what weight fraction of the reaction mixture will have the structure –[-NH–(CH2)10–CO-]100– when 99% of the functional groups have reacted ? [Ans. 0.0037]
Chain branching is not as common with anionic polymerization as it is with free-radical polymerization and cationic polymerization. Compare the relative stabilities of the intermediates in this mechanism with those you drew for chain branching in the cationic polymerization of styrene. Explain why chain branching is less common in this anionic polymerization.
6. Nylon-11 is poly(Ω-aminoundecanoic acid). In the polymerization of Ω-aminoundec-anoic acid, H2N(CH2)10COOH, to produce this polymer, what weight fraction of the reaction mixture will have the structure –[-NH–(CH2)10–CO-]100– when 99% of the functional groups have reacted ?
1.Discuss the suitable initiator to start an addition polymerization. 2.Define what is auto-acceleration, what causes this effect and how to minimize this effect. 3.Briefly discuss emulsion and suspension polymerization techniques.