• In compression test a greater load is necessary to cause yielding than that required in tension test for the same sample. State the reason Advantages of Stress Strain curve. Sources of errors in the experiment. Reasons for the barrel shape of the tested specimen and how could we minimize this defect. • The conditions required to achieve a reliable compression test.

• In compression test a greater load is necessary to cause yielding than that required in tension test for the same sample. State the reason Advantages of Stress Strain curve. Sources of errors in the experiment. Reasons for the barrel shape of the tested specimen and how could we minimize this defect. • The conditions required to achieve a reliable compression test.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Draw a typical stress vs strain tensile test curve for the following material and label the axis. A typical brittle material subjected to a tensile stress that has been applied to the material till the sample breaks. 1- label the axis and draw the curve for a brittle material. 2- indicate the maximum strength of the material. 3- show on the portion of the curve where young's modulus can be calculated.
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation.
The magnitude of the shear stress to cause yielding in a torsion test and the magnitude of the normal stress to cause yielding in a uniaxial tensile test are usually equal". Is this true or false?
A sheet of aluminium alloy is reduced in thickness by 25% following a rolling operation. Tensile test specimens were cut from the sheet before and after rolling. Sketch the tensile test curves for both specimens, making reference to the differences if any, in Young’s modulus, the elastic limit and the level of ductility
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
A tensile test specimen has a starting gage length 50 mm and a cross-sectional area 200 mm2. During the test, the specimen yields under a load of 30,000 N (this is the 0.2% offset) at a gage length of 52 mm.The maximum load of 63,000 N is reached at a gage length of 57 mm just before necking begins. Final fracture occurs at a gage length of 63.5 mm. Determine (a) yield strength, (b) modulus of elasticity, (c) tensile strength, (d) engineering strain at maximum load, and (e) percent elongation.
Briefly discuss the differences between the Engineering Stress versus Engineering Strain and the True Stress versus True Strain Diagrams for the test specimen. Briefly explain why the two plots are different. When is the use of Engineering Stress versus Engineering Strain invalid?
Tensile test under 40,000 N load was applied to a low carbon steel with a sample diameter of 6 mm. As the diameter of the specimen under load decreases to 5 mm, calculate a) Engineering stress and% elongation values, b) Actual stress and% elongation values.
A specimen with an initial diameter of 12 + b* was tested under tensile conditions and a maximum load of 60 kN was recorded together with a %65 of strain. What should be the load to be applied in order to obtain a strain of %30
Briefly comment on the values obtained for the Elastic Modulus, Yield Strength, Ultimate Strength and Toughness of the test specimen as compared to values of various comparable materials found in the literature. Is the test material comparatively strong? Is it stiff? Is it tough? Yield strength is 186Mpa, elastic modulus is 44.8GPa And the ultimate strength is 238.7mpa
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A hot rolled steel tension test sample has a diameter of 6 mm and the original gage lenght of 30 mm. In a test to fracture, the stress and strain data below were obtained. Complete table.