tensile test uses a circular test specimen that has a gage length of 50 mm and diameter 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length = 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility.

tensile test uses a circular test specimen that has a gage length of 50 mm and diameter 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length = 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm2 when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson’s ratio for both metallic rods. Justify your answer with reasons.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A tensile test is being conducted on a steel-rod specimen with a gauge length of L0=4.0 in and an initial diameter of d0=0.75 in. If the final length of the rod at fracture is Lt= 5.53 in, find the percent elongation of the rod at fracture
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
A mild steel bar went through a tensile test conducted at the University of San Carlos Mechanical Engineering Laboratory. The following data was obtained from the test: i. Diameter of the steel bar = 30 mm ii. Gauge length of the bar = 200 mm iii. Load at the elastic limit = 250 kN iv. Extension at a load of 150 kN = 0.21 mm v. Maximum load = 380 kN vi. Total extension = 60 mm vii. Diameter of the rod at the failure = 22.5 mm Determine the Young’s modulus, the stress at the elastic limit, the percentage elongation, and the percentage decrease in area.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
Mild Steel is tested in the laboratory. The data obtained are:Length of Specimen = 320 mmDiameter of Specimen = 30 mmElongation under a load of 20 kN = 0.055 mmLoad at Yield Point = 130 kNMaximum Load = 210 kNLoad at fracture = 115 kNLength of Specimen at failure = 380 mmDiameter of Specimen at failure = 17.5 mm Calculate: (1).Young’s Modulus (2). Yield Stress (3). Ultimate Stress
39) A tensile test specimen has a gauge length=2in. and a diameter of 0.875in. Yielding occurs at a load of 35,500lbs. The corresponding gauge length = 2.0113in. (neglect the .2% yield point). The maximum load of 45,000lbs is reached at a gauge length of 2.543in. If fracture occurs at a gauge length of 2.673in, determine the percent elongation at fracture (Round to the nearest whole %)
A tensile test is conducted on a mild steel bar. The following data was obtained from the test : diameter of the steel bar= 3cm, Gauge Length of the bar = 20cm, Load at Elastic limit= 250kN, Extension at a load of 150kN= 0.21 mm, Maximum Load = 380kN, Total Extension= 60mm, Diameter of the rod at failure=2.25cm, determine young's modulus?
A) An engineer works for a company that has many gray cast iron rods of different diameters and would like to design an equivalent rod that could handle a force of P= 10.0 kipkip without fracturing. What is the minimum diameter that this new rod must have to support P? B)A tensile test is being conducted on a steel-rod specimen with a gauge length of L0 = 4.0 in and an initial diameter of d0 = 0.75 in. If the final length of the rod at fracture is Lf= 5.53 in , find the percent elongation of the rod at fracture.