Question 3The diameter of an extruder barrel is 65 mm and its length is 1.75 m. The screw rotates at 55rev/min. The screw channel depth is 5.0 mm, and its flight (helix) angle is 18°. The headpressure at the die end of the barrel is 5x10° Pa. The viscosity of the polymer melt is given as100 Pa-s. Calculate the volume flow rate of polymer in the barrel.The drag flow is given by the equation:Qa = 0.5 n2 D² N d̟ sinp cospThe back pressure flow is given by the equation:Pn D dễ sin²oQb127LThe details of the extruder screw are given in figure 3.1W.PerpendicularchannelwidthHelixangle(O)PitchChannel depth deAxial|light|widthAxialchannelwidthPerpendicularfight-Direction of mass flow-Figure 3.1. Schematic illustration of a typical "Archimedean" extruder screw.widthRootdiameterdiameter

Given Diameter, d = 65 mm Length, L = 1.75 m Viscosity = 100 Pa. s

The diameter of an extruder barrel is 65 mm and its length is 1.75 m. The screw rotates at 55 rev/min. The screw channel depth is 5.0 mm, and its flight (helix) angle is 18°. The head pressure at the die end of the barrel is 5x10° Pa. The viscosity of the polymer melt is given as 100 Pa-s. Calculate the volume flow rate of polymer in the barrel.

The diameter of an extruder barrel is 65 mm and its length is 1.75 m. The screw rotates at 55 rev/min. The screw channel depth is 5.0 mm, and its flight (helix) angle is 18°. The head pressure at the die end of the barrel is 5x10° Pa. The viscosity of the polymer melt is given as 100 Pa-s. Calculate the volume flow rate of polymer in the barrel.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An extruder barrel has a diameter of 110 mm and a length of 3.0 m. The screw channel depth = 7.0 mm, and its pitch = 95 mm. The viscosity of the polymer melt is 105 Pa-s, and the head pressure in the barrel is 4.0 MPa. What rotational speed of the screw is required to achieve a volumetric flow rate of 90 cm3/s?
I only need the answer to question 2. I provided the correct answer for question 1 1)An extruder barrel has a diameter of 4.0 in and an L/D ratio of 28. The screw channel depth = 0.25 in, and its pitch is 4.8 in. It rotates at 60 rev/min. The viscosity of the polymer melt is 100 x 10-4 lb-sec/in2. What head pressure at exit is required to obtain a net volume flow rate of 150 in3/min? Assume that you are extruding 1/2 in PVC pipe (schedule 40) using the conditions above. -2193 lb/in2 2) How long would it take to extrude a 30 foot section? Be sure to note in your solution where you got your dimensions for the PVC pipe.
An extruder barrel has a diameter of 4.0 in and an L/D ratio of 28. The screw channel depth = 0.25 in, and its pitch is 4.8 in. It rotates at 60 rev/min. The viscosity of the polymer melt is 100 x 10-4 lb-sec/in2. What head pressure at exit is required to obtain a net volume flow rate of 150 in3/min? Assume that you are extruding 1/2 in PVC pipe (schedule 40) using the conditions above. How long would it take to extrude a 30 foot section? Be sure to note in your solution where you got your dimensions for the PVC pipe.
An extruder has barrel diameter and length of 150 mm and 3.1 m, respectively. The screw rotational speed = 55 rev/min, channel depth = 8 mm, and flight angle = 18°. The plastic melt has a shear viscosity = 175 Pa-s. Determine: (a) the extruder characteristic, (b) the shape factor Ks for a circular die opening with diameter = 4.0 mm and length = 15 mm, and (c) the operating point (Q and p).
In a single-barrel extrusion system, the operator observes that the extrudate (made of polyethylene, PE) is being processed at a speed of 0.5m/s with a final diameter of 0.5cm. The screw pitch is 1cm, the barrel diameter is 1.5cm, the barrel length is 10cm, the screw channel depth is 0.3cm and the screw is rotating at 10RPM. a. Find the head pressure on the die given that the polymer has a viscosity of 300Pa.s. Note that the swell ratio of PE is 1.2. b. Find the length of the die opening.
Viscosity is an important property of a polymer melt in plastics shaping processes. Upon what parameters does viscosity depend?
a.State and describe the termi. co-extrusion b. Differentiate between single and twin-screw extruders by describing three distinguishing features in each. c. Dealinate three advantages in the application of extrusion cooking.
A medical pump weighs 220 lb. and has a critical acceleration of 50 g. The item measures 9x9x17 in. Using ARCEL Resin 2.2 lb/ft3. Find the necessary thickness and design the shape (length and width) of foam needed for each face of the item if it is expected that the item will suffer at most two face drops from a height of 24 inches in the distribution environment. Provide justification for your answer.
Describe the features of a screw extruder and its functions in molding of plastics.
Provide an sustanable and economical block flow diagram of rigid polyurethane foam from lignin.
The graph below gives a plot of force versus total sample length in a tensile test of a polymer. The sample is cylindrical, with an initial diameter of 1 cm and an initial length of 10 cm. From the data below, calculate the modulus, yield stress, yield strain, tensile strength, and % elongation.
A polymer straight propeller with a diameter = 15in(measured diameter = 382mm) and pitch = 5.6in(142.24mm). A drawing is given below for the propeller. Explain the diameter of the propeller, pitch of the propellerand the drawing given.