The following data are obtained from the Charpy impact test of a copper specimen. a) Length of the square cross-section specimen = 70 mm %3D b) Each side (top & bottom) of the cross-section = 9.64 mm c) V- Notch thickness at middle of the specimen length = 1.06 mm d) Impact Strength = 279 kJ/m² Determine the Cross-sectional area at the top surface, Cross-sectional area at notch & Impact energy of the copper specimen.

The following data are obtained from the Charpy impact test of a copper specimen. a) Length of the square cross-section specimen = 70 mm %3D b) Each side (top & bottom) of the cross-section = 9.64 mm c) V- Notch thickness at middle of the specimen length = 1.06 mm d) Impact Strength = 279 kJ/m² Determine the Cross-sectional area at the top surface, Cross-sectional area at notch & Impact energy of the copper specimen.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. THE QUESTION IS : FIND THE Final Diameter of the Specimen after Fracture (in mm)????
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm) Initial Cross-sectional Area (in mm2)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. Initial Cross-sectional Area 2.01 mm2. The Diameter of the Specimen 1.59 mm. Final Length of the Specimen 42.92 mm. Stress at the elastic load 8955.22 N/mm2. Find: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. FIND: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 152 kN. - Length of the specimen is 20 mm. - The yield strength is 86 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 10 kN, iv) Young's Modulus if the elongation is 2.2 mm at 10 kN and (v) Final diameter if the percentage of reduction in area is 28 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 18 kN, iv) Young's Modulus if the elongation is 1.3 mm at 18 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution: Initial Cross-sectional Area (in mm2) The Diameter of the Specimen (in mm) Final Length of the Specimen (in mm) Stress at the elastic load (in N/mm2) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 142 kN. - Length of the specimen is 23 mm. - The yield strength is 82 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN, iv) Young's Modulus if the elongation is 1.6 mm at 15 kN and (v) Final diameter if the percentage of reduction in area is 20 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
Pleas very fast A square cross-section v-notched specimen of height 75 mm has each side of 13 mm has been selected to perform Charpy impact test. A v-notch of thickness 1.97 mm is made at the middle of the specimen length. Determine the cross-sectional area at notch. Cross-sectional area at notch (in mm2)
Your manager asked you to explain the difference between three-point bending test and four-pointbending test by using a standard specimen each one has the following dimensions:1. Force = 30 KN.2. Thickness= 5 cm.3. Width = 10 cm.4. Length = 25 cm.Calculate the stress on each specimen then justify your answer.
In a tensile test, initial length of the experimental specimen is ____________ the final length of the specimen.