The requirements and material properties of an air entrained concrete mix are given below.Calculate the weights of the components of 1 m3 of concrete.Water content: 200 kg/m3Air content: 7.5%W/C: 0.45 (By Weight).Dry aggregate volume in 1 m3 concrete mixture: 0.44 m3Specific Gravity (g/em3 )water absorption capacity (%)Total Moisture (%)Cement3.15Fine aggregate(saturated surfacedry)2.651.35.5Coarse aggregate(saturated surface dry)2.70.51.5Dry unit weight of coarse aggregate is 1,500 kg / m3. 'kind

The flow of fluid includes movement of an unbalanced fluid. As long as unequalled forces are in…

The requirements and material properties of an air entrained concrete mix are given be Calculate the weights of the components of 1 m3 of concrete. Water content: 200 kg/m3 Air content: 7.5% W/C: 0.45 (By Weight) Dry aggregate volume in 1 m3 concrete mixture: 0.44 m3

The requirements and material properties of an air entrained concrete mix are given be Calculate the weights of the components of 1 m3 of concrete. Water content: 200 kg/m3 Air content: 7.5% W/C: 0.45 (By Weight) Dry aggregate volume in 1 m3 concrete mixture: 0.44 m3

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Designing a concrete that will be exposed to groundwater, the chemical analysis of which is given in Table 1. is requested. a) For 1 m3 of concrete, assuming the air gap is 1%, according to the relevant impact class specified in TS EN 206 Calculate the amount of material needed. (Maximum grain size of A1, A2, A3 aggregates to be used in the mixture) has a diameter of 16 mm and is in SDYK state, and the physical properties and mixing ratios of the aggregates are given in Table 2.) b) The ratio of cement kneading water to be used in production is 28%, volumetric shrinkage of cement paste Calculate the shrinkage that will occur in the concrete, assuming that the absolute volume of cement is 1%. from shrinkage Find the tensile stress that will occur in the concrete due to Whether cracks will occur in the concrete due to shrinkage, Considering the static elasticity modulus (secant modulus) of the concrete given below in the “stress-strain” diagram. take it and check it. Note: In the…
In proportioning a concrete mix, the coarse and fine aggregates had the following properties respectively; Coarse: Dry weight: 800lb, 3,2% MC, 2.0% AC, Fine: Dry weight 350 lb, 1.2% MC, 2.9% AC. How much should the water be adjusted to account for the agregate moisture?
Concrete was mixed with the following ingredients: 20.7 kg of cement, 39.2 kg of sand,60.9 kg of gravel, and 14.6 kg of water. The sand has a moisture content of 3.3% andan absorption of 4.7%. The gravel has a moisture content of 3.6% and an absorptionof 4.5%. Since water absorbed in the aggregate does not react with the cement or improve the workability of the plastic concrete, what is the water–cement ratio of this mix according to the American Concrete Institute’s weight mix design method? If a water–cement ratio of 0.5 is required using the same materials and ingredients but different amount of mixing water, what is the weight of the mixing water to use?
Concrete was mixed with the following ingredients: 20.7 kg of cement, 39.2 kg of sand, 60.9 kg of gravel, and 14.6 kg of water. The sand has a moisture content of 3.3% and an absorption of 4.7%. The gravel has a moisture content of 3.6% and an absorption of 4.5%. Since water absorbed in the aggregate does not react with the cement or improve the workability of the plastic concrete, what is the water–cement ratio of this mix according to the American Concrete Institute’s weight mix design method? If a water–cement ratio of 0.5 is required using the same materials and ingredients but different amount of mixing water, what is the mass of the mixing water to use?
Students in the materials lab mixed concrete with the following ingredients:9.7 kg of cement, 18.1 kg of sand, 28.2 kg of gravel, and 6.5 kg of water. The sand has a moisture content of 3.1% and an absorption of 4.2%. The gravel has a moisture content of 3.4% and an absorption of 4.4%. Since water absorbed in the aggregate does not react with the cement or improve the workability of the plastic concrete, what is the water–cement ratio of this mix according to the American Concrete Institute’s weight mix design method? If a water–cement ratio of 0.5 is required using the same materials and ingredients but different amount of mixing water, what is the weight of the mixing water to use?
Q. Using the British methods, design a concrete mix to bear an average compressive strength of 35 MPa at 28 days, to cast a room slab with the following dimensions (5 width x 4 length x 0.2 depth m) and 200 mm space distance of reinforcement. Consider the following properties: o Cement used is type I Portland cement ® Required slump = 30 — 60 mm o Coarse aggregate: ® Crushed rocks * Maximum size of 40 mm, e The fine aggregate: * Crushed rocks = Falls in zone 3 o Assume zone A for figure 1 o AssumeK = 1.64
Read the question carefully and give me right solution according to the question. If you don't know the solution please leave it but don't give me wrong solution. Dry weight of coarse aggregate, fine aggregate and water for 1 m3 of one type of concrete requires 1100 kg, 680 kg and 175 liters, respectively. From laboratory test for, it is determined that absorption content of coarse and fine aggregates is 0.5% and 1.25%, respectively. Meanwhile, moisture content of coarse and fine aggregate is 0.75% and 1.0%, respectively. Determine weight of coarse aggregate, fine aggregate and water for one batch with volume of mixer of 800 liter.
A concrete mix has a ratio os 1:2:4 by mass. The properties of thematerials to be used are tabulated below.MATERIALS. SPECIFIC GRAVITYCEMENT 3.33SAND 2.65GRAVEL 2.67Cement weighs 40 kg per bag. Use 24 liters of water per bag of cement Compute the volume of cement solids per bag of cement in cu m.Compute for the required volume of sand solids per bag of cement.Compute for the volume of concrete that can be produced per bag of cement 0.1
Compute for the corrected amount of water needed in the concrete mix if the mass of fine and coarse aggregates are 650 kg and 780 kg, and both have an absorption of 1.5% and 2% respectively. Water/cement ratio is 0.50 and the mass of cement is 260kg.
A mix design requires 1160 kg/m3 of coarse aggregate (in dry condition), 599 kg/m3of fine aggregate (in dry condition) and 148 kg/m3 of water. The absorption capacityof the coarse aggregate is 0.4 % while the moisture content is 1.5%. The absorptioncapacity of the fine aggregate is 0.4 % while the moisture content is 4%. Pleaseanswer the following questions based on information given. a. What is the amount of Moist Coarse Aggregate? b. What is the amount of SSD Fine Aggregate? c. What is the amount of Moist Fine Aggregate? d. What is the amount of water after adjusting for moisture?
Students in the materials lab mixed concrete with the following ingredients: 22.1 lb of cement, 41.6 lb of sand, 57.5 lb of gravel, and 14.3 lb of water. The sand has a moisture content of 3.2% and an absorption of 5.5%. The gravel has a moisture content of 3.9% and an absorption of 4.6%. Since water absorbed in the aggregate does not react with the cement or improve the workability of the plastic concrete,a.what is the water–cement ratio of this mix according to the American Concrete Institute’s weight mix design method? b. If a water–cement ratio of 0.5 is required using the same materials and ingredients but different amount of mixing water, what is the weight of the mixing water to use?
: Prepare mix design for given data • The 28-day compressive strength should be 5000 psi, The slump should 2 inch and the maximum aggregate size should not exceed one inch ( 3/4 inch). The properties of the materials are as follows: • Cement : Type I, specific gravity = 3.15 • Coarse Aggregate: Bulk specific gravity= 2.70; absorption capacity = 0.5%; dry-rodded unit weight = 1500 kg/m3, surface moisture = 1.2 % • Fine Aggregate: Bulk specific gravity= 2.80 ; absorption capacity = 1.1%; fineness modulus = 2.80; surface moisture = 3*C.No/90 %