Determine the load on the specimen that causes yielding.Express your answer to three significant figures and include appropriate units.The stress-strain diagram for a steel alloy having anoriginal diameter of 0.40 in. and a gage length of9 in. is shown in the figure below. (Figure 1)?Py =ValueUnitsSubmitRequest AnswerPart CFigure< 1 of 1Determine the ultimate load the specimen will support.Express your answer to three significant figures and include appropriate units.o (ksi)80HA?7060ValueUnits50Pu =4030SubmitRequest Answer2010€ (in./in.)0 0.04 0.08 0.12 0,16 0,20 0,24 028O 0.0005 0.001 0.0015 0.002 0.0025 0.0030.0035Provide Feedback

Answered: Image /qna-images/answer/1ef1c79f-5f75-4cfe-9d94-d8441ce6da14.jpg

Answered: The stress-strain diagram for a steel…

The stress-strain diagram for a steel alloy having an original diameter of 0.40 in. and a gage length of 9 in. is shown in the figure below. (Eigure 1)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

To determine the nominal or engineering stress and strain experienced by a specimen of a material while it is subjected to a tension test, and to be able to read important values from a conventional stress-strain diagram obtained from the test.A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 73.0 ksi , e = 101.0 ksi g=83.0ksi, and h=0.15in/in Part A - Nominal or engineering strain in the rod Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.5 in . Express the nominal strain in inches per inch to three significant figures. Part B - Nominal or engineering stress in the specimen Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 8.0 kips ,…
During a test, a copper specimen alloy having a diameter of 10.2 mm is applied with a tensile load of 8900 N. Given a maximum allowable elongation of 0.25 mm, determine the maximum length (mm) of the specimen before deformation.
To determine the nominal or engineering stress and strain experienced by a specimen of a material while it is subjected to a tension test, and to be able to read important values from a conventional stress-strain diagram obtained from the test. A tension test is being conducted on a steel-rod specimen with a gauge length of L0=50 mm and initial diameter of d0=13 mm. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 506 MPa , e = 689 MPa , g = 585 MPa , and h = 0.146 mm/mm . A) Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 53.0 mm . B) Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 16.0 kN , find the nominal stress experienced by the rod. C)Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 60 % - Percentage of Reduction in Area = 36 % - Final length after fracture = 35.2 mm - Final Diameter after fracture = 3.54 mm & - Ultimate stress = 439 MPa iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
A bar made of carbon-steel of size 12mm x 20mm has a yield stress of 400 MPa and ultimate tensile strength of550 MPa. Tha gauge length of the specimen tested under tension loading is 350mm. a. Determine its elongation when a tension load of 75 KN is applied. b. Determine the maximum load the bar can take before it fractures. Take Youngs Modulus of steel as 200,000 MPa
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
For a steel element with a 0.2% steel characteristic, a stress test was applied and the analysis of the data thrown by the material is required in terms of a variation of force and the respective deformations. Determine the following: A.Determine the percentage elongation at the point where the part develops the fracture. B.Construct the “Stress-Strain” diagram C.Maximum tensile strength of the part.
Sketch the typical engineering stress-strain diagram behaviour to fracture point, F and the tensile strength TS, together with the geometry of the deformed specimen at various point along the curve.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 61 % - Percentage of Reduction in Area = 43 % - Final length after fracture = 34.8 mm - Final Diameter after fracture = 4.2 mm & - Ultimate stress = 433 MPa Determine the Initial length, Initial diameter and Maximum load. SOLUTION: i) Initial Length (in mm) = Answer for part 1 ii) Final Area (in mm2) = Answer for part 2 iii) Initial Area (in mm2) = Answer for part 3 iv) Initial Diameter (in mm) = Answer for part 4 v) Ultimate Load (in N) = Answer for part 5
During a test, a steel specimen alloy{ E =207GPa } by having a diameter of 10.6 mm is applied with a tensile load of 8700 N. Given a maximum allowable elongation of 0.5 mm, determine the maximum length (mm) of the specimen before deformation
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 44 % - Final length after fracture = 36.3 mm - Final Diameter after fracture = 4.39 mm & - Ultimate stress = 359 MPa Determine the Initial length, Initial diameter and Maximum load. SOLUTION: i) Initial Length (in mm) = ii) Final Area (in mm2) = iii) Initial Area (in mm2) = iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 66 % - Percentage of Reduction in Area = 38 % - Final length after fracture = 34.6 mm - Final Diameter after fracture = 4.43 mm & - Ultimate stress = 364 MPa Determine the Initial length, Initial diameter and Maximum load. ii) Final Area (in mm2) = iii) Initial Area (in mm2) =