11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. (10 points) 12) Continue to Question 9, After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments. Number 12 please the information in question 11 is applicable.

11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. (10 points) 12) Continue to Question 9, After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments. Number 12 please the information in question 11 is applicable.

Principles of Instrumental Analysis

7th Edition

ISBN:9781305577213

Author:Douglas A. Skoog, F. James Holler, Stanley R. Crouch

Publisher:Douglas A. Skoog, F. James Holler, Stanley R. Crouch

Chapter23: Potentiometry

Section: Chapter Questions

Problem 23.12QAP: What arc the advantages of microfabricated ISEs? Describe typical applications of this type of...

See similar textbooks

Similar questions

JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from thefurnace, JJ was upset to find a big hard lump., After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. How could JJ do this well? JJ needs this size ceramic rod for experiments.
Give the five examples for glass forming materials. What is the role of modifiers in glass making. what advantages intermediates bring in glass formation? Marks Note- take your time but please give proper answer.
JUST PART B PLEASE! 11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. b) After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments.
11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. b) After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments.
1. "Band structure" of "Hatom chain" and "H mole chain" are drawn as "graphs" and "intermediate process". Describe it in detail.
We collected a clastic muscovite grain from the shale at sample K. The 40Ar/40K ratio is 0.65. What is the age of the grain?
Microstructure of a steel contain 100% coarse pearlite it carbon content is reported to be 0.65% is it possible? And why ?
Can elastic hose use for pumping and transferring concentrated solution of CH3COOH for long time? If not let explain why and propose at least two types of material which are properly used in this case.
A water sample was analyzed for Fe content using the iron-phenanthroline method. The following data were obtained from the analysis:(photo) Determine the value of the slope (m), y-intercept (b), and the coefficient of determination (r2) m = 0.1128; b = -4.0 x 10-5; r2 = 0.9880 m = 0.1128; b = - 3.0 x 10-3; r2 = 0.9762 m = 0.1128; b = - 3.0 x 10-3; r2 = 0.9880 m = 0.1128; b = -4.0 x 10-5; r2 = 0.9762
6.1) At the composition of 0.77% by weight C, identify the phase(s) presentat 950 degrees C 6.2) When the specimen is at 950 degrees C, what is the maximum C composition at which a single phase Austenite is stable?6.3) If we slowly cool a Fe-C alloy with 0.77% by weight C, austenitized at950 degrees C, to just below the eutectoid temperature of 727 degrees C, give the weight percentage and composition of the phases present based on the phase diagram given above6.4) If we cool very quickly a Fe-C alloy with 0.77% by weight C,austenitized at 950 degrees C, to room temperature, give the weight percentage and composition of the phase(s) present
Explain and elaborate.
A device to understand how iron behaves at high temperatureswe want to design. This device (with 1% accuracy) allows the change in volume (heating) of a 1cm 3 iron cube.the resulting polymorphic transformation) must be able to feel. HMK structure in iron 911 0 C and latticeparameter 0.2863 nm. At 913 0 C, it has YMK structure and its lattice parameter is 0.3591 nm. Of measuring instrumentDetermine the accuracy tolerance it needs (i.e. at least how many cm 3 to detect a changemust). It is necessary to use at least 6 digits after the comma in this question. Hint: YMK first andFor HMK, the volume of an atom is found and then, using the number of atoms in each structure, the ironThe question can be started by finding the different volumes.