JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump., After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. How could JJ do this well? JJ needs this size ceramic rod for experiments.

JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump., After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. How could JJ do this well? JJ needs this size ceramic rod for experiments.

Fundamentals Of Analytical Chemistry

9th Edition

ISBN:9781285640686

Author:Skoog

Publisher:Skoog

Chapter34: Miscellaneous Separation Methods

Section: Chapter Questions

Problem 34.14QAP

See similar textbooks

Similar questions

11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from thefurnace, JJ was upset to find a big hard lump. Explain to JJ what happened. (10 points)12) Continue to Question 9, After grinding up to the lump, someone told JJ to add a sintering aidand deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch indiameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments. Number 12 please the information in question 11 is applicable.
JUST PART B PLEASE! 11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. b) After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments.
11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. b) After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments.
A single crystal Ni (in FCC) alloy bar is uniaxially pulled along [-123]. The bar starts to yield at σ =100MPa by slipping on (111)[-101] which hence is the most favorable slip system.
Give the five examples for glass forming materials. What is the role of modifiers in glass making. what advantages intermediates bring in glass formation? Marks Note- take your time but please give proper answer.
Microstructure of a steel contain 100% coarse pearlite it carbon content is reported to be 0.65% is it possible? And why ?
A device to understand how iron behaves at high temperatureswe want to design. This device (with 1% accuracy) allows the change in volume (heating) of a 1cm 3 iron cube.the resulting polymorphic transformation) must be able to feel. HMK structure in iron 911 0 C and latticeparameter 0.2863 nm. At 913 0 C, it has YMK structure and its lattice parameter is 0.3591 nm. Of measuring instrumentDetermine the accuracy tolerance it needs (i.e. at least how many cm 3 to detect a changemust). It is necessary to use at least 6 digits after the comma in this question. Hint: YMK first andFor HMK, the volume of an atom is found and then, using the number of atoms in each structure, the ironThe question can be started by finding the different volumes.
For a Copper-Nickel (Cu-Ni) alloy of composition 25 wt % Ni and 75 wt % Cu at 1200 OC (Point B), refer to the phase diagram provided in Figure 2 and answer the following. (i) What is composition of liquid phase? (ii) What is composition of solid phase? (iii) What fraction of the system is liquid for a 25% Ni alloy at 1250 OC? (iv) What fraction of the system is solid for a 25% Ni alloy at 1250 OC?
packed columns the stationary phase is: (a) packed in the column (b) coated inside the column (c) a & b are correct (d) none of them
The bonding strength at the coating and substrate interface can significantly affect the performance of the coating. What are the processing parameters in CVD that affect the interfacial bonding strength and how do they affect the bonding strength? How can you test the bonding strength? What are the possible approaches for you to maximize the bonding strength for Boron Carbide coating material?
We collected a clastic muscovite grain from the shale at sample K. The 40Ar/40K ratio is 0.65. What is the age of the grain?
The addition of dimethylglyoxime, H2C4H602N2, to a solution containing nickel(Il) ion gives rise to a precipitate: Nickel dimethylglyoxime is a bulky precipitate that is inconvenient to manipulate in amounts greater than 135 mg. The amount of nickel in a type of permanent-magnet alloy ranges between 22% and 38%. Calculate the sample size that should not be exceeded when analyzing these alloys for nickel.