2. Please complete the table below. Please fill the name of the phases after the indicated heat treatment. Phases before Cooling speed or heat Phases after heat treatment heat treatment treatment process Pearlite Slow / Annealing Pearlite Austenite Moderate cooling Austenite Quenching Austenite Quenching + Tempering

2. Please complete the table below. Please fill the name of the phases after the indicated heat treatment. Phases before Cooling speed or heat Phases after heat treatment heat treatment treatment process Pearlite Slow / Annealing Pearlite Austenite Moderate cooling Austenite Quenching Austenite Quenching + Tempering

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter26: Welding Metallurgy

Section: Chapter Questions

Problem 27R: What are the three steps in precipitation hardening?

See similar textbooks

Similar questions

Below is shown the isothermal transformation diagram for a 0.45 wt% C iron-carbon alloy. List the microconstituent(s) present for the heat treatment labeled (a)-(c) on this diagram. It is not necessary to state the proportion(s) of the microconstituents. I would love an explaiation aswel on how i whould read this diagram. Thanks
Copper-Nickel alloy is widely applied in industry. (a) List at least three applications where Cu-Ni alloy is used; (b) How many components and phases are shown in the below phase diagram? (c) For a mixture of 40 wt% Cu and 60 wt% Ni at 1320 oC, what phases are present? Identify theamount of these phases by applying “lever rule”.
When alloys A, B, and C are gently cooled from 1000 o C in the following temperature ranges, sketch their microstructures. (equilibrium cooling). List every phase present in the microstructures. Comment on the constituent phases of the resulting alloy and its mechanical characteristics. Please keep it brief.
Choose the corect answer -A vertical line in the phase diagram represents a.an intermetallic compound b.a eutectic phase c.a eutectoid phase Match each statement with a letter -In the peritectoid reaction -In the Peritectic reaction: -In the Monotectic reaction: -In the Eutectoid reaction: -In the Eutectic reaction: a. a liquid phase transforms into two solids when it is cooled down b. a solid phase transforms into two different solids when it is cooled down c. a liquid phase transforms into a new liquid phase and a solid phase d. Two solid phases transform into a new single solid phase e. A solid phase and a liquid phase transforms into a solid phase
the PCS containing 0.4%C was quenched hardened in water, amd tempered at 400oC. sketch and identify the phases of the microstructure pf the stell at rhe following states a) above the upper critical point just before quenching in water b) after quenching I’m water prior to tempering C) after tempering
Given a blank phase diagram, label the solid, liquid, and gas phases for a pure substance. Give the approximate temp. and pressure of the triple point, and determine what the substance's phase would be at a given temperature and pressure. Can you provide an example?
In a binary phase diagram ( pressure omitted) what is the maximum number of phases that can coexist for at least one degree of freedom?
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
Using the TTT diagram for eutectoid steel, draw the specified cooling path on the diagram. Indicate what phases you expect in the final product with percentage of each phase. Assume the material has been fully austenitized before cooling. a. Water cool to room temperature b. Hot quench in molten salt to 690°C and then cooled isothermally for 2 hours: c. Hot quench to 610°C hold 3 minutes and water quench
Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5
1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. calculate the amount of pro eutectoid product, where applicable (at the bottom) A) quenched in cold water to 650 C in 0.1 seconds, then held at 650 C for 5 seconds, then quenched to 400 C, held at 400C for 60 seconds, and finally quenched to room temperature B. Necessary Steel Phase Diagram Calculations to determine the amount of pro eutectoid product:
The Fe – Au solid – liquid T – xB phase diagram can be viewed as the intersection of asolid – phase miscibility gap with a solid – liquid phase – transition loop having aminimum at xAu = 0.8. The miscibility gap intersects the phase transition loop at xAu =0.1 and at xAu = 0.3. Fe has a higher melting point than Au. Sketch the phase diagramand label all the areas.