Q.1. For hypoeutoctoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature

Q.1. For hypoeutoctoid plain carbon steel (select %C content yourself), determine the phases that are present, the compositions of these phases, and the percentages or fractions of the phases. Make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: a) Just above the austenite transformation temperature

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Using the TTT diagram for eutectoid steel, draw the specified cooling path on the diagram. Indicate what phases you expect in the final product with percentage of each phase. Assume the material has been fully austenitized before cooling. a. Water cool to room temperature b. Hot quench in molten salt to 690°C and then cooled isothermally for 2 hours: c. Hot quench to 610°C hold 3 minutes and water quench
1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. calculate the amount of pro eutectoid product, where applicable (at the bottom) A) quenched in cold water to 650 C in 0.1 seconds, then held at 650 C for 5 seconds, then quenched to 400 C, held at 400C for 60 seconds, and finally quenched to room temperature B. Necessary Steel Phase Diagram Calculations to determine the amount of pro eutectoid product:
Using the time-temperature-transformation diagram, what steel phases would you generate by cooling from 900ºC A. quenching in cold water to 520ºC in 0.5 second, holding the sample temperature constant for 1000 seconds at 520ºC, and then quenching to room temperature B. cooling down to room temperature over a period of 2 weeks?
1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. calculate the amount of pro eutectoid product, where applicable (at the bottom) A.) quenched in cold water to 380 C in 0.1 seconds, then held at 380 C for 30 seconds, then quenched to room temperature B.) cooled in air at 2 C/minute to 600oC, then quenched to room temperature C. quenched in cold water to 550 C in 0.1 seconds, then held at 550 C for 2 seconds, then quenched to room temperature D. Necessary Steel Phase Diagram Calculations to determine the amount of pro eutectoid product:
For a steel with a 0.2 wt%C, what is the mass fraction and composition of phases at 600 (Please draw connections on the graph)
Quenching a hypereutectoid steel from a two-phase region of austenite and cementite; the phases present in the microstructure are
(11.10) Suppose that a steel of eutectoid composi- tion is cooled to 550°C (1020°F) from 760°C(1400°F) in less than 0.5 s and held at this temperature. (a) How long will it take for the austenite- to pearlite reaction to go to 50% comple- ton? To 100% completion? (b) Estimate the hardness of the alloy that has completely transformed to pearlite? 11.12) Briefly cite the differences between pearl- rp. bainite, and spheroidite relative to crostructure and mechanical properties?
Part C. Which type of phase transformation is important in heat treatment of steels? (circle one)Peritectic Eutectic Eutectoid Incongruent meltingAt what temperature and overall composition wt% C, does it occur?Write the reaction equation for this transformation, and briefly describe the nature of each of the three important phases that are involved.
The Fe – Au solid – liquid T – xB phase diagram can be viewed as the intersection of asolid – phase miscibility gap with a solid – liquid phase – transition loop having aminimum at xAu = 0.8. The miscibility gap intersects the phase transition loop at xAu =0.1 and at xAu = 0.3. Fe has a higher melting point than Au. Sketch the phase diagramand label all the areas.
Illustrate the equilibrium reactions that exist in an iron carbon phase diagram with the required particulars.
When alloys A, B, and C are gently cooled from 1000 o C in the following temperature ranges, sketch their microstructures. (equilibrium cooling). List every phase present in the microstructures. Comment on the constituent phases of the resulting alloy and its mechanical characteristics. Please keep it brief.
The iron-carbon phase diagram is usually shown for a metastable system. What does this mean, and why do we use the phase diagram for the metastable system?