Engineering material casting help 5. What does the thickness of an aluminum alloy casting (length = 12 in. and width = 8 in.)have to be, in order to produce a tensile strength of 44 ksi? The mold constant in Chvorinov's rulefor aluminum alloys cast in a sand mold is 45 min/in².Tensile strength (ksi)5046423026Tensilestrength0% Elongation13025205% Elongation00.0050.0100.015Secondary dendrite arm spacing (cm)Secondary dendritearm spacing (cm)10-110-210-310-40.1TTS=C1nV=C_(H)*ACopperZinc alloysAluminum alloys10 100 1,000 10,000 100,000Solidification time (s)

Answered: Image /qna-images/answer/0b237bf5-eea7-4f13-a175-b4386bdb4762.jpg

5. What does the thickness of an aluminum alloy casting (length = 12 in. and width = 8 in.) have to be, in order to produce a tensile strength of 44 ksi? The mold constant in Chvorinov's rule for aluminum alloys cast in a sand mold is 45 min/in². 50 46 $ Tensile strength (ksi) 38 30 26 I 0 Tensile strength % Elongation T 30 C 20 5 9 0.005 0.010 0.015 Secondary dendrite arm spacing (cm) % Elongation Secondary dendrite arm spacing (cm) 10-2 10-3 10-4 0.1 1 T7s = C₂ (4) TTS Cm A Copper Zinc alloys Aluminum alloys 10 100 1,000 10,000 100,000 Solidification time (s)

5. What does the thickness of an aluminum alloy casting (length = 12 in. and width = 8 in.) have to be, in order to produce a tensile strength of 44 ksi? The mold constant in Chvorinov's rule for aluminum alloys cast in a sand mold is 45 min/in². 50 46 $ Tensile strength (ksi) 38 30 26 I 0 Tensile strength % Elongation T 30 C 20 5 9 0.005 0.010 0.015 Secondary dendrite arm spacing (cm) % Elongation Secondary dendrite arm spacing (cm) 10-2 10-3 10-4 0.1 1 T7s = C₂ (4) TTS Cm A Copper Zinc alloys Aluminum alloys 10 100 1,000 10,000 100,000 Solidification time (s)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q2 /A/ In casting experiments performed using a certain alloy and type of sand mold, casting made of steel with shape as disk, with diameter =700mm and 30mm thickness , it took 20sec for a solidify Determine the value of the mold constant in Chvorinov's rule
a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
Determine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.
‏Q1 . Draw and explain five casting defects in sand casting process . Q2 . Explain hot working process with respect to microstructure . Also draw the diagram of microstructure.
A cubical casting of 100 mm side is to be made from steel using an Al pattern (master pattern). For preparing the master pattern, a wooden pattern is used. Determine the dimensions of master pattern and wooden pattern. Use shrinkage allowance (mm/mm) for steel and Al as 0.021 and 0.013 respectively
In sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .
In turbine blade casting, how is a single-crystal structure achieved? Select one or more: a. By using a curving coil-like channel in the casting mould b. By removing grain boundaries by hot working and recrystallisation c. By careful control of the temperatures of the mould d. By introducing impurities into the molten alloy in the mould
2. What are the general defects found in casting processes? Name and briefly describe two.
3:(b) Explain in detail different components of a gating system in sand mold casting.
When designing patterns for casting, patternmakers use special rulers that automatically incorporate solid shrinkage allowances into their designs. For example, a 12-in. patternmaker’s ruler is longer than 1 foot. How long should a patternmaker’s ruler be for making patterns for (a) aluminum castings and (b) high-manganese steel?
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
138) Which one is needed to produce perforated parts using casting technique?a) lower degreeb) high degreec) spadesd) runnere) feeder 139) what is the crystal structure of iron?a) Hexagonal tight-packed structureb) volume-centered cubicc) face-centered cubicd) simple cubice) Ortok141) How is the elastic modulus calculated?A) With the strain rate of strainB) The ratio of shear strength to deformationC) the ratio of strain to strainD) the ratio of tensile strength to strainE) by the ratio of yield strength