7.41 The average grain diameter for a brass mate- O rial was measured as a function of time at 650°C, which is shown in the following table at two dif- ferent times: Time (min) Grain Diameter (mm) 40 5.6 x 102 100 8.0 x 10-2 (a) What was the original grain diameter? (b) What grain diameter would you predict after 200 min at 650°C?

7.41 The average grain diameter for a brass mate- O rial was measured as a function of time at 650°C, which is shown in the following table at two dif- ferent times: Time (min) Grain Diameter (mm) 40 5.6 x 102 100 8.0 x 10-2 (a) What was the original grain diameter? (b) What grain diameter would you predict after 200 min at 650°C?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

138) Which one is needed to produce perforated parts using casting technique?a) lower degreeb) high degreec) spadesd) runnere) feeder 139) what is the crystal structure of iron?a) Hexagonal tight-packed structureb) volume-centered cubicc) face-centered cubicd) simple cubice) Ortok141) How is the elastic modulus calculated?A) With the strain rate of strainB) The ratio of shear strength to deformationC) the ratio of strain to strainD) the ratio of tensile strength to strainE) by the ratio of yield strength
In the Figure below, the tensile breaking strength, (sigma mark)tenstile-breaking = 140 Mpa breaking strength at compression (sigma mark)compression-breaking = 460 Mpa pouring Machine part made of iron is shown. to the piece P=25 kN forces are acting. piece for t=26 mm Calculate reliability according to Coulomb - Mohr theory ?
A clean and dry core rock sample weighing 425 g was 100%saturated with brine solution.The new weight is 453 g. The core sample is 12 cm long and 4 cm in diameter with a porosity of the rock sample is 0.173. Calculate the specific gravity to the brine which is used to measure the porosity
Briefly explain the ASTM grain-size standard
S/N Grain Diameter (mm) Strength (MPa) 1. 0.015 170 2. 0.025 158 3. 0.035 151 4 0.050 145 Determine The constants in the Hall-Petch equation; and The grain diameter to obtain strength of 200 Mpa.
The yield strength for an alloy that has an average grain diameter of 4.1 × 10-2 mm is 131 MPa. At a grain diameter of 7.6 × 10-3 mm, the yield strength increases to 246 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa?
A machinist was tasked to insert an aluminum piston into a steel cylinder. The inside diameters of the cylinder and of the piston are 0.500 m and 0.4998 m, respectively, at 25 ℃. To what temperature must they be heated to obtain a perfect fit?
1. There are three slip systems on a FCC octahedral plane, i.e. one of the {111} planes. Assume a2 MPa tensile stress is applied along the [100] direction of a gold single crystal, whose criticalresolved shear stress is 0.91 MPa at room temperature. Demonstrate quantitatively thatmeasurable slip will not occur on any of the three slip systems containing the (111) plane as aresult of this applied tensile stress. (Hint: Schmid’s law) 2. Identify the Burgers vector (using vector notation) of a screw dislocation that can cross-slipbetween (111) and (111) planes of an FCC crystal (Hint: Use Weiss zone law). 3. Why are dislocations not considered thermodynamic equilibrium defects like vacancies?Explain by describing the relative interplay between entropy and enthalpy affecting the Gibbsfree energy of the dislocations-containing material system.
From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the uniformity coefficient.
Determine the ASTM grain size number if 90 grains per square inch are measured at a magnification of 55×. In this problem, you are asked to find the ASTM grain size number given the number of grains per square inch and the magnification. Solve Equation 4.18 (below) for G.
Briefly explain the ASTM grain-size standard. Draw a stress-strain curve for a ductile metal and mention plastic region and 5 important parameters (or points) in your curve. Additionally, explain these parameters (if necessary provide the corresponding equations).
Discuss the relationship between the grain size and hardness