A Brinell hardness measurement of 650 HBN, using a 10-mm-diameter indenter and a 2950 kg load on am aluminum plate. Determine the indentation diameter. O a. 2.683 mm O b. 2.836 mm Oc. 2.368 mm d. 2.386 mm

A Brinell hardness measurement of 650 HBN, using a 10-mm-diameter indenter and a 2950 kg load on am aluminum plate. Determine the indentation diameter. O a. 2.683 mm O b. 2.836 mm Oc. 2.368 mm d. 2.386 mm

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: In the Brinell hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down the…

A: Given details: P=1200kgD=6mmBHN=586 formula used: BHN=2PπDD-D2-d2

Q: In the BrinelI hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down the…

Q: 2. Compute the tensile strength and ductility (%EL) of a cylindrical copper rod if it is cold worked…

Q: A mild steel material is subjected to a Brinell hardness test with an applied force of 8145 N using…

Q: A mild steel material is subjected to a Brinell hardness test with an applied force of 7459 N using…

A: Given: The applied force is F=7459 N, The indentor (steel ball) diameter is D=11 mm, Brinell…

Q: A 4ft long rod with a 0.29 inch diameter is subjected to a 10,130lb tensile load. What is the…

Q: (a) Derive the value of Brinell hardness using a hard spherical indenter, which was developed by…

A: Solution: Note: Dear Student! As per our guidelines, we are only allowed to answer a single…

Q: In tensile testing a tensile load is applied to the specimen until it O a. bend O b. fractures O C.…

Q: The ability of a material to undergo large permanent deformation with the application of a tensile…

A: Elasticity: It is the ability of the material which allows to return to its original shape and size…

Q: In hardness test, a force of 3000 kgf applied using steel ball of 10 mm, the result hardness value…

Q: What type of indenter is used in a Rockwell 'C' hardness test? Select one: O a. rhombus shaped O b.…

A: Type of indenter used in a Rockwell 'C' hardness test,

Q: Determine the indentation diameter and the surface area of indentation of a copper material…

A: Given: BHN = 955 D = 10 mm W = 9.4 kN Thus, F=Wg=9.4×1039.81=958.2 kg

Q: Q3 a) How the hardness of a mild steel specimen is determined using a Brinell hardness testing…

A: Since you have posted multiple independent questions we will solve the first question for you To get…

Q: 12. True or false? In Brinell hardness test, the depth of indentation must not be too great relative…

A: Given that True or false? In Brinell hardness test, the depth of indentation must not be too great…

Q: If 80% of samples has a compressive strength greate than x, calculate the value of x (to 1 decimal…

Q: ure 1 shows a compound bar with three different diameters, d1-9mm, d2-22mm, and d3-14mm machined…

Q: In tensile test the percentage of elongation was 29.8%. If the final length reached to 84.37mm, so…

Q: A cylindrical specimen of a brass alloy 13.6 mm in diameter has an ultimate tensile stress of 496…

Q: HW Calculate the mean depression diameter in Brinell hardness test when the BHN=255 kg/mm2, and the…

Q: b- 10 mm diameter of Brinall hardness ball when the load 500 kgr and HB= 300 determined the diameter…

A: Given: Diameter of the ball=10mmBrinall hardness =300Loading=500kg.f

Q: If the area under the stress and strain curve is less then it is concluded that the material has low…

A: The area under stress and strain curve represent the toughness of the specimen material.

Q: Determine the indentation diameter and the surface area of indentation of a copper material…

A: (i) Write a value of the Brinell Hardness Number (BHN). BHN=902 Write a diameter of the…

Q: 7. In the Brinell hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down…

Q: Determine the load, in kN, on a 25-mm diameter, 1200 cm long steel shaft if its maximum elongation…

Q: 1. A 10-mm-diameter Brinell hardness a steel alloy when a load of 500 kg was used. Compute the…

Q: (1) A tensile stress is to be applied along the long axis of a cylindrical brass rod that has a…

A: Solution of problem-1: The data given is,

Q: 2. A steel bar, whose cross section is 0.60 inch by 4.10 inches, was tested in ension. An axial load…

Q: What will be the length of given mild steel rod after applying 100 kips force/load ?. If the…

A: Given, Force applied = P = 100 kips = 100 x 103 lb Diameter of rod = d = 0.5 in Length of rod = L =…

Q: Necking in cast iron is seen when it is subjected to a tensile test. Select one: O True O False

Q: The diminutions of the mild steel impact test sample as shown in fig the notched depth is 2mm…

A: Given Data: The notched depth is d =2 mm. The impact energy absorption is E = 80 J. The area under…

Q: (i) Determine the Force applied on an aluminum specimen subjected to Brinell hardness test. If the…

A: Given data:- Surface area = 34 mm2 Brinell hardness number = 1234 Find :- Force applied = ?

Q: Question 5 required to raise the load if the yield stress of steel is 300MPA. A lead of 5kN is to be…

Q: At the proportional limit, a 18 mm thick 84 mm wide bar elongates 6.9 mm under an axial load of 495…

A: The change in width of the bar is -0.1242 mm.

Q: What type of indentor is used in a Brinell hardness test? Select one: O a. rhombus shaped O b. None…

A: Hardness test focuses on measuring the hardness of a specimen by subjecting it to indentations with…

Q: The true stress (in MPa) versus true strain relationship for a metal is given by O = 1020 e0.4 The…

A: As per question given data σ=1020∈0.4∈=0.4initial area A =100mm^2 we have to determine the cross…

Q: Determine the following i) Diameter of the specimen, i) Final length of the specimen, iii) Stress…

Q: A round brass rod 30 mm in diameter and 200 mm long is subjected to a compressive force of 100 kN.…

Q: Grade 1020 steel has a yield strength of 42 ksi and an elastic modulus of 30 Mpsi. Another grade of…

Q: If specimen Ais tested using Rockwell C scale showed a value of HRC 45 while Specimen B when tested…

Q: B- Hardness test Brinell type was applied to copper alloy sample, 1 cm diameter steel ball was used…

Q: In a micro-Vickers hardness test, the diagonals of the indentation are 54 and 55 um when a load of…

A: d1 = 54 μm d2= 55 μm To find : Micro - Vickers harness (HV)

Q: 7. In the Brinell hardness test, if the load used 1200 kg, and the ball diameter 6 mm, write down…

A: Given Load(P)=1200kg, Diameter of the ball (D)=6mm, BHN=586

Q: The steel rod in Fig. is to be used to support an axial load of 18 kip. If Est = 29(103 ) ksi and…

A: Given data: The applied load, P = 18 kip. The modulus of elasticity, E = 29 × 103 ksi. The yield…

Q: 1. Define ultimmate tensile strength

A: As per our guidelines we are supposed to solve only one question if multiple questions are asked .…

Q: A mild steel material is subjected to a Brinell hardness test with an applied force of 7830 N using…

Q: Determine the force applied to a hardness specimen that has Brinell hardness number as 974 and the…

A: We have to find force

Q: 5. A member which does not regain its original shape after removal of the load producing deformation…

A: Let us first understand the meaning of each option. If the body does not allow any deformation under…

Q: Brinell hardness tester 10 mm diameter steel ball ,3000 kg applied load indicated hardness value of…

Q: ure 1 shows a compound bar with three different diameters, d1-9mm, d2-22mm, and d3-14mm machined…

A: P=30kN d1=9mm d2=22mm d3=14mm

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

Google Chrome
attempt.php?attempt=514085&cmid%=103093&page=3
My bookmarks v
es > ENGG1023-2020S2 > General > Assessment#2- Lab
曲
me
Calendar
Badges
All courses
A Brinell hardness measurement of 650 HBN, using a 10-mm-diameter indenter and a 2950 kg load on an
aluminum plate, Determine the indentation diameter.
O a. 2.683 mm
O b. 2.836 mm
O c. 2.368 mm
Od. 2.386 mm
Finish attempt
search
TOSHIBA
F5
F6
F7
F8
F9
F10
F11
F12
&
15
6 7
01
7 V
9.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

6. Discuss the different types of volume change in concrete at early and long-term ages. 8. A center-point loading flexural test was performed on a concrete beam having a size of100×100×500 mm. The beam is sitting on two supports located at 25 mm from each edge ofbeam. If the failure load was 17.5 kN, find the flexural strength.9. Considering the two tests of flexure, 3-points and 4-points, which one is more suitable forbending test and why?10. The compression strength test was performed on several samples of concrete molded in fourtypes of molds cubes of 0.100 m×0.100 m ×0.100 m and of 0.150 m×0.150 m × 0.150 m, andcylinders having a cross section of d=100 mm by H=200 mm and d=150 mm by H=300 mm,respectively. If the weight of the samples and the loads at failure are as given in the Table. Bothcubes and cylinder samples are cast from the same concrete batch under the same conditionsand subjected to the same curing method.11. Calculate the density (in kg/m3) and the compressive strength…
Draw the tensile curves of the following materials, taking into account the appropriate elongation at break, modulus of elasticity and tensile stress, on the side stress-strain graph. a)Low carbon steel (Ecelik=200Gpa),(Syield=300MPa),(Stensile=400MPa) b)High carbon steel (Esteel=200GPa),(Stensile=700MPa) c)Aluminum (Ealuminum=70GPa), (Syield=200MPa),(Stensile=300MPa) d)Cast iron (Ecast iron=120GPa),(Stensile=200MPa)
calculate hardness (Brilnell Hardness, HB): Ø Tested material – bronze Ø Force loading the intender (constant value), P – 2452 N Ø The diameter of the carbide ball intender, D – 10 mm Ø The diameter (mean value) of the print, d – 2,00 mm
Which steel presents the maximum modulus of toughness UT? UT = ( (Sy − Sut) /2 ) ε f AISI 4142 and AISI 1020 AISI 1020 AISI 1095 and AISI 1020 AISI 4142 and AISI 1095
A piston, 9 cm in diameter, is used to increase the internal pressure in a cylinder from 0 to 50 MPa. The cylinder, which is made of peak-aged aluminum alloy (yield strength = 500 MPa, Kic = 35 MPaVm), has the following dimensions: length = 20 cm, inner diameter = 9 cm and outer diameter =1 1 cm. The piston-cylinder arrangement suffered a malfunction which caused the cylinder to burst. Post-failure analyses showed the presence of a defect in the form of an elliptical flaw 4.4 mm long at the inner wall, 1.5 mm deep and oriented normal to the hoop stress in the cylinder. Compute the magnitude of the pressure at which the cylinder burst.
The steel rod in Fig. is to be used to support an axial load of 18 kip. If Est = 29(103 ) ksi and sY = 50 ksi, determine the smallest diameter of the rod as allowed by the AISC specifications. The rod is fixed at both ends.
A tensile-testing apparatus is to be constructed that must withstand a maximum load of 293516 N. The design calls for two cylindrical support posts, each of which is to support half of the maximum load; the minimum yield and tensile strengths of this alloy are 343 MPa and 565 MPa or 82,000 psi respectively.what is required diameter? Take factor of safety is 2.3
Calculate is the largest size (mm) internal through crack that a thick plate of aluminum alloy 7075-T651 can support at an applied stress of: (a) three-quarters of the yield strength, and (b) one-half of the yield strength Assume Y = 1. Given: KIC = 24.2 MPa (sq. rt.(m) and σys = 495 MPa
A mild steel material is subjected to a Brinell hardness test with an applied force of 8145 N using a hardened steel ball indentor of 10 mm and it is found that the Brinell Hardness Number as 966. Determine the surface area of indentation and indentation diameter
A tensile-testing apparatus is to be constructed that must withstand a maximum load of 293516 N. The design calls for two cylindrical support posts, each of which is to support half of the maximum load. Furthermore, plain-carbon(1045) steel ground and polished shafting rounds are to be used; the minimum yield and tensile strengths of this alloy are 343 MPa and 565 MPa(82,000 psi), respectively. Specify a suitable diameter in mm for these support posts. Assume safety level is 2.3. Round your answer to 2 significant figures.
4 In hardness test, a force of 3000 kgf applied using steel ball of 10 mm, the result hardness value is (BHN=200+N) where N is your number in class. Calculate the mean depression w bli nöy :diameters (d)? N=92
– The weight is suspended from structural A–36 steel alloy and 2014-T6 aluminum alloy wires, eachhaving the same initial length of 10 ft and cross-sectional area of 7×10–3 in2 (Figure Q1). If the weight is increasedgradually, determine which wire yields first? Explain which material model and yield criterion you will use? Justifyyour choices