At the proportional limit, a 18 mm thick 84 mm wide bar elongates 6.9 mm under an axial load of 495 kN. The bar is 1.4 m long. If Poisson's ratio is 0.3 for the material, determine the change in width (in mm) of the bar. Hint: Your answer will be in the format: -XXXXX Note: Do not include units in your answer. Answer: -1479

At the proportional limit, a 18 mm thick 84 mm wide bar elongates 6.9 mm under an axial load of 495 kN. The bar is 1.4 m long. If Poisson's ratio is 0.3 for the material, determine the change in width (in mm) of the bar. Hint: Your answer will be in the format: -XXXXX Note: Do not include units in your answer. Answer: -1479

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test for an aluminum alloy, the sample is 2 inches long and 0.5 inches in diameter. The proportional portion of the tension stress-strain diagram for an aluminum alloy is shown below. Now that the axial stress of the sample under a tensile load of 9 kips is below material's proportional limit, please calculate the elongation of the sample under the tensile load of 9 kips: ____ inch. Pay attention to units and calculate your answer to 4 decimal place.
In a standard tensile test a steel rod of 7/8 in. in diameter is subjected to a tension force of 17 kips. Determine the ratio of the shear modulus to the modulus of elasticity of a material whose Poisson's ratio is 0.25.
A bar of 6-mm in diameter is only allowed to decrease at a maximum of 3.96% of its total length. What is the maximum force (Newtons) that can be applied? Consider the shear modulus = 602 MPa, and the Poisson's ratio as 0.20. Express your answer in three decimal places.
A copper specimen subjected to the Brinell Hardness Test using hardened steel ball indenter of diameter 12 mm and the indentation diameter 3.87 mm is measured using an optical magnifying lens with a ruler. Draw the Brinell Hardness Test setup neatly and determine the force applied on the specimen. Take Brinell Hardness Number for copper as 807. Calculate: 1-Surface Area of Indentation (in mm2) 2-Applied Force (in N)
For the steel bar shown in the fig. determine a) the total elongation of the bar b) the length of themiddle segment to have zero elongation of the bar c) the diameter of the last segment to have zeroelongation of the bar.
A 40 mm diameter steel bar is subjected to a tension test. Under a tension load of 276.46 kN, it was observed that the original gage length of 50 mm increased in length by 0.055 mm and the diameter decreased by 0.0105 mm. Compute the Poisson’s Ratio.
A tensile force of 100 kN is applied on a 0.02-m diameter and 2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to2.01 m. The true axialstrain is?
The bar shown in figure 1 is tested in the universal testing machine. It is observed that at a load of 40 kNthe total extension of the bar is 0.285 mm. Determine the Young’s Modulus of the material.
A cantilever beam, 80 mm wide by 290 mm high and 9 m long, carries a load that varies uniformly from zero at the free end to 1400 N/m at the wall. Determine the magnitude of the stress in a fiber 50 mm from the top of the beam at a section 5 m from the free end. Answer must be in MPa.
Determine the width and thickness of the leaves (in mm) of a leaf spring using the following specifications: Total load = 140 kN; Number of springs supporting the load = 4; Maximum number of leaves = 10; Span of the spring = 1000 mm; Permissible deflection = 80 mm; Modulus of elasticity, E = 200 kN/mm2; and allowable stress in spring material is 600 MPa.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
A cylindrical specimen of a nickel alloy having an elastic modulus of 207 GPa and an original diameter of 10.2 mm experiences only elastic deformation when a tensile load of 8900 N is applied. Compute the maximum length of the specimen in mm before deformation if the maximum allowable elongation is 0.45 mm.