A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with a force of 40. 000 N. If the deformation is totally elastic and the original length is 120 mm, what is the final length of the specimen in mm? 120.01350 B 120.00116 120.00041 D 120.00029

A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with a force of 40. 000 N. If the deformation is totally elastic and the original length is 120 mm, what is the final length of the specimen in mm? 120.01350 B 120.00116 120.00041 D 120.00029

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An eight-inch-long steel has a cross section area of 0.25 in2. After a load of 5000 lbs has been applied, the length is found to be 8.0065 in. What is the unit deformation induced? Select one: a. 0.00081 b. 0.00041 c. 0.0081 d. 0.004
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation. use correct stratgy and correct E 0.55962
An engine part is being tested with a load of 65 000 lb. The allowable tensile stress is 10000 psi ,modulus of elasticity 40×106 psi . If the original length of specimen is 40 inches with elongation not exceeding 0.0155 inches, what diameter of the specimen is rejected.
Which of the following statements about the axial deformation formula is FALSE? a. The formula is applicable at points near the supports and points of application of loads b. The material may have a gradually varying cross-sectional area c. The material may have varying internal force across the length d. The material must exhibit elastic behavior.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
A cylindrical metal specimen having an original diameter of 12.8 mm (0.505 in.) and gauge length of m (2.000 in.) is pulled in tension until fracture occurs. The diameter at the point of fracture is 6.60 mm (0.260 in.), and the fractured gauge length is 72.14 mm (2.840 in.). Calculate the ductility in terms of percent reduction in area and percent elongation.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 65 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 36.1 mm - Final Diameter after fracture = 4.25 mm & - Ultimate stress = 401 MPa SOLUTION: Initial Length (in mm) = Final Area (in mm2) = Initial Area (in mm2) =
A tensile test was carried out on a tensile sample with a gauge length of 62.35 mm and a cross-sectional area of 5.17mm. Determine the final fracture length and final cross-sectional area of the specimen if the percentage elongation was 17.64% and the percentage reduction in the area was 3.78%
An engine parts is being tested with a load of 60000 lb. The allowable tensile stress is 10000 psi, modulus of elasticity of 40x106 psi. If the original length of specimen is 42 inches with elongation not exceeding 0.0015 in, what diameter of the specimen is rejected? a. 4.2 in b. 3.0 in c. 2.5 in d. 5.17 in
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 66 % - Percentage of Reduction in Area = 38 % - Final length after fracture = 34.6 mm - Final Diameter after fracture = 4.43 mm & - Ultimate stress = 364 i) Initial Length (in mm) = iv) Initial Diameter (in mm) =
A) An engineer works for a company that has many gray cast iron rods of different diameters and would like to design an equivalent rod that could handle a force of P= 10.0 kipkip without fracturing. What is the minimum diameter that this new rod must have to support P? B)A tensile test is being conducted on a steel-rod specimen with a gauge length of L0 = 4.0 in and an initial diameter of d0 = 0.75 in. If the final length of the rod at fracture is Lf= 5.53 in , find the percent elongation of the rod at fracture.
A tensile force of 10 kN is applied on a 0.02-m diameter and 2-m long rod. After applying theload, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. The lateral (transverse) strain is?