Considering typical characteristics and unit costs of sand casting, die casting and investment casting processes, which process would you prefer to use in order to produce the following parts and components? Write your answers into a similar Table as below, and briefly explain why you selected that process. A. 150 aluminum thin-wall section components. B. 100 nickel-alloy rocket components. C. 15,000 stainless steel machine parts with intricate shapes. D. 25,000 magnesium components with very precise dimensions. E. 50,000 cast iron components with good surface finish. F. 120,000 aluminum components with very complex shapes.

Considering typical characteristics and unit costs of sand casting, die casting and investment casting processes, which process would you prefer to use in order to produce the following parts and components? Write your answers into a similar Table as below, and briefly explain why you selected that process. A. 150 aluminum thin-wall section components. B. 100 nickel-alloy rocket components. C. 15,000 stainless steel machine parts with intricate shapes. D. 25,000 magnesium components with very precise dimensions. E. 50,000 cast iron components with good surface finish. F. 120,000 aluminum components with very complex shapes.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

1. Explain the three stages in casting process and its applications.
Write down the Experiment “Introduction to Casting Processes and study various stages of casting processes. Give examples of casting products.
Describe the stages involved in the contraction of metals during casting.(a) Contraction of the molten metals as it cools prior to its solidification.(b) Contraction of the metal during phase change from liquid to solid.(c) Contraction of the solidified metals as its temperature drops to ambient temperature.(d) All of above.(e) None of above.2. What kinds of defects in castings?(a) Hot tear.(b) Surface scar.(c) Plastic deformation.(d) Ductile flow.3. How does porosity have detrimental effects on the mechanical and physical properties ofcastings?(a) Pores in castings are resulted from internal discontinuities when that are prone topropagate under external stresses.(b) The toughness of a material will decrease as a result of porosity.(c) Physical properties, such as thermal and electrical conductivity, also be adverselyaffected by porosity.(d) Pores increase the strength and elastic modulus.(e) Porosity increases both the thermal and electrical conductivity4. Thermosetting plastics can…
1. Discuss briefly the things you have learned about;A. MetalsB. Casting ProcessC. Forming Process 2. Choose any product made of Metal and List down all the manufacturing processes itundergoes.
A aluminium alloy casting has a cylindrical geometry with 100mm in diameter and weighs 3200 gram. This casting takes 7.5 min to completely solidify. Another smaller and lighter cylindrical-shaped casting with the same diameterto-length ratio weighs 1800 gram. This casting is made of the same aluminium alloy and the same conditions of mold and pouring were used. Determinea) The mold constant in Chvorinov’s Rule,b) The dimensions of the lighter castingc) The total soldification time of the lighter casting. The density of aluminium alloy= 2.7 gram/cm3and n=2
For the casting of the part, whose perspective pictures are given below, take into account the surface of the section, the model design, if necessary, the core design, all the molding stages and finally the mold in the most suitable form for casting, and name all the mold elements by showing them on the figure (Note: The hole shown in the figure, full hole.)
2. What are the general defects found in casting processes? Name and briefly describe two.
Consider the red aluminum tool holder shown in Figure 4. Your job shop has been contracted to make 10,000 pieces this year, with possibility of making 20,000 more each year in the future. Consider the process options below, which option is the best? a) using die casting, cast the holder anodizing the holder to red color b) using injection molding, mold the holder without hole using a mill or drill press, cut the hole anodizing the holder to red color c) using sand mold, cast the holder without hole using a mill, cut all planar surfaces (smooth surfaces) using a mill or drill press, cut the hole anodizing the holder to red color d) using a hacksaw, cut a piece of 3"X3" bar stock to length using a mill, cut all planar surfaces using a mill or drill press, cut the hole anodizing the holder to red color
What is “back-of-the-envelope calculations”?
27) What are the casting defects arises due to faulty processes in casting, explain each type with neat sketch.
a) What is "Strip Casting" one of the casting methods? b) Which parameters affect strip thickness in strip casting? Write 4 parameters and list them. c) In the alumina based substrate shaped by strip casting, it is seen that the cast parts are quite fragile. What parameters do you intervene in order to increase the flexibility of the casting piece? (2 parameters) Explain the reasons. (2 Reasons)
These are the questions, would like working for each of them to be neat.