A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3! %3D

A riser in the shape of a sphere is to be designed for a sand casting mold. The casting is a rectangular plate, with length = 100 mm, width = 50 mm, and thickness = 10 mm. If the total solidification time of the casting itself is known to be 2.5 min, determine the diameter of the riser so that it will take 20% longer for the riser to solidify. %3D %3! %3D

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
1. A square section riser be designed for a sand-casting mold. The casting itself is a quarter-cylinder with a diameter of 12cm and a length 20cm. The total solidification time for this casting = 0.9 min. The square for the riser will have a height-to-width ratio of 2.0. Determine the dimensions of the riser so that it is total solidification time = 1.2 min.
A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.
what solidification time is required for a casting of 9.5 cm3 and a mold contact area of 10 cm2? The mold constant is 838 s/cm2.
With a solidification factor of 0.97 x 106 s/m², the solidification time (in seconds) for a spherical casting of 200 mm diameter is...
In sand casting of hollow part of lead, a cylindrical core of diameter 120 mm and height 180 mm is placed inside the mould cavity. The densities of core material and lead are 1600 kg/m³ and 11300 kg/m³ respectively. The net force (in N) that tends to lift he core during pouring of molten metal will be. . . . .
A aluminium alloy casting has a cylindrical geometry with 100mm in diameter and weighs 3200 gram. This casting takes 7.5 min to completely solidify. Another smaller and lighter cylindrical-shaped casting with the same diameterto-length ratio weighs 1800 gram. This casting is made of the same aluminium alloy and the same conditions of mold and pouring were used. Determinea) The mold constant in Chvorinov’s Rule,b) The dimensions of the lighter castingc) The total soldification time of the lighter casting. The density of aluminium alloy= 2.7 gram/cm3and n=2
A cylinder with a diameter of 40 mm and height of 80 mm solidifies in 3 minutes in a sand casting operation. What is the solidification time if the cylinder height is doubled? What is the time if the diameter is doubled?
When designing patterns for casting, patternmakers use special rulers that automatically incorporate solid shrinkage allowances into their designs. For example, a 12-in. patternmaker’s ruler is longer than 1 foot. How long should a patternmaker’s ruler be for making patterns for (a) aluminum castings and (b) high-manganese steel?
When casting a 4x10x20 in. Part, which has a top overflow with a H / D = 1.5 ratio, you want to determine the height and diameter of the overflow to prevent shrinkage in the part to be cast. Note: Remember that to achieve this, the overflow has to solidify some time after the piece has solidified, since in this case the overflow acts as a riser.
. A round casting is 0.2 m in diameter and 1 m in length. Another casting of the same metal iselliptical in cross section, with a major-to-minor axis ratio of 2, and has the same length andcross sectional area as the round casting. Both pieces are cast under the same conditions.What is the difference in the solidification times of the two castings?
A 5 cm cube solidifies in 4.6 min. Assume n=2. Calculate (a) the mold constant in Chvorinov’s rule and (b) the solidification time for a 1.25 cm X 12.5 cm X 15 cm bar cast under the same conditions