A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45 MPAVM (41 ksi Vin.). is exposed to a stress of 1000 MPa (145,000 psi). Will this specimen experi- ence fracture if it is known that the largest surface crack is 0.75 mm (0.03 in.) long? Why or why not? Assume that the parameter Y has a value of 1.0.

A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45 MPAVM (41 ksi Vin.). is exposed to a stress of 1000 MPa (145,000 psi). Will this specimen experi- ence fracture if it is known that the largest surface crack is 0.75 mm (0.03 in.) long? Why or why not? Assume that the parameter Y has a value of 1.0.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A specimen of a 4340 steel alloy having a plane strain fracture toughness of 25 MPa√m is exposed to a stress of 500 MPa. -Will this specimen experience fracture if it is known that the largest surface crack is 0.5 mm? Please explain why. Assume the parameter Y has a value of 1.0.
An 8-cm-square bar of steel is found to contain a1-mm corner crack, oriented perpendicular to the length ofthe bar. If an axial stress is applied from 0 to 420 MPa at afrequency of once every 10 minutes, how long will it take forthe rod to fracture? The properties of the bar are:KIC = 90 MPa √m , σys = 1500 MPa, and the crack growthrelation is da/dN = 2 x 10-37 ΔK4, with da/dN and ΔKbeing given in units of m/cycle and Pa √m , respectively
A component for an airerafl is made from an alyminum alloy that has a plane strain fracture toughness of 40 MPa mba. It has been determined thatfracture results at a stress of 365 MPa when the masimum internal crack length is 2.6 mm. For this component and alloy. compuie the stress leyel atwhich facture will occur for a crrical jnternal crack length of 4.0 mm
A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45MPa√m is exposed to a stress of 1000 MPa. The largest surface crack is 0.75mm and the parameter Y has a value of 1.0. Show that the specimen will fracture under this amount of applied stress.
Some aircraft component is fabricated from an aluminium alloy that has a plane strain fracture toughness of 35 MPa√m. It has been determined that fracture results at a stress of 250 MPa when the maximum (or critical) internal crack length is 2.0 mm. For this same component and alloy, show that whether fracture will or will not occur if the stress level is at 325 MPa and the maximum internal crack length is 1.0 mm.
Some aircraft component is fabricated from an aluminium alloy that has a plane strain fracture toughness of 40 MPa√m. It has been determined that fracture results at a stress of 300 MPa when the maximum (or critical) internal crack length is 4.0 mm. For this same component and alloy, will fracture occur at a stress level of 260 MPa when the maximum crack is 6.0 mm? Why or why not?
An 820 MPa (145,000 psi) stress is applied to a specimen of 4341 steel alloy, which has a plane strain fracture toughness of 45MPa squareroot (m). If the greatest surface crack is 0.95 mm (0.03 in) long, will this specimen fracture as a result? Assume that the parameter Y is 1.22.
Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface crack of length 0.20 mm and that has a tip radius of curvature of 0.001 mm when a stress of 1450 MPa is applied. The question is attached. The answer is not 29000. WileyPlus marks it as incorrect.
. Suppose that a wing component on an aircraft is fabricated from analuminum alloy that has a plane strain fracture toughness of 40 MPa√m. It has been determined that fracture results at a stress of 365MPa when the maximum internal crack length is 2.6 mm. For thissame component and alloy, compute the stress level at whichfracture will occur for a critical internal crack length of 4.0 mm.
NEED AN ANSWER ASAPAn aircraft component is to be fabricated from an aluminum alloy that has a plane strain fracture toughness of 45 MPa m and a yield strength of 500 MPa. It has been determined that fracture results at a stress of 250 MPa when the maximum internal crack length is 9 mm. For this same component and alloy, determine critical internal crack length that will result to fracture if the design stress is three-fourth of the yield strength. If the available flaw detection apparatus has a resolution limit of 3 mm, will the crack in (1) be detected? Why or why not? Show complete solution
You are given a 10-cm-diameter cylindrically shaped extruded bar (length = 50 cm) of an aluminum alloy. a. What specimen configurations would you use to characterize the degree of anisotropy of the material’s fracture toughness? b. If the lowest fracture toughness of the bar was found to be 20 MPa √m , what would be the load level needed to achieve this stress intensity level? c. Confirm the presence of plane-strain conditions, given that σys = 500 MPa. (Assume specimen thickness = 1 cm, a/W = 0.5, and bar diameter = 1.2 W.)
Why is the prediction of the tensile fracture of a brittle material is difficult to predict?