A tensile stress is applied along the long axis of a cylindrical steel rod with adiameter of 10 mm. If the deformation is entirely elastic, determine the magnitude of the load required to produce a 5 X 10-3 mm change in diameter. Assume a modulus of elasticity of 200 GPa and a Poisson’s ratio of 0.27.

A tensile stress is applied along the long axis of a cylindrical steel rod with adiameter of 10 mm. If the deformation is entirely elastic, determine the magnitude of the load required to produce a 5 X 10-3 mm change in diameter. Assume a modulus of elasticity of 200 GPa and a Poisson’s ratio of 0.27.

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.