An arc welding is performed to join two metal pieces. After the welding process, the product is subjected to fatigue test. Discuss which part of the weld joint will have high potential to experience fatigue failure

An arc welding is performed to join two metal pieces. After the welding process, the product is subjected to fatigue test. Discuss which part of the weld joint will have high potential to experience fatigue failure

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter28: Filler Metal Selection

Section: Chapter Questions

Problem 4R: What chemicals alloys are a. considered to be contaminants to the weld metal? b. used to increase...

See similar textbooks

Related questions

Q: Hard soldering of metals can be done in the melting point temperature range of O 183°C-212°C…

A: Hard solders are used for brazing, and melt at a higher temperatures,alloy of copper with zinc or…

Q: What does liquid-solid phase bonding mean and in which cases is it preferred over welding? What does…

A: The liquid-solid phase bonding is a joining technique that has been used to join a variety of…

Q: Difference in solubility of gases in molten and solid state of metal during welding promotes Cracks…

Q: E70XX 1/4 V2 1/4 For the welding information shown, calculate the design capacity of the weld Rweld…

Q: You are spot welding two pieces of metal together with one weld. They are 6 mm thick each. The total…

A: Welding is a manufacturing technique that is done on the metal surfaces. In this operation, the…

Q: A resistance spot-welding operation is performed on two pieces of 1.5 mm thick sheet steel using…

Q: heat treatment is applied in welding processes and what its importance

A: Heat treatment in welding operation :

Q: 3) Total resistance in welding is composed of: (i) Resistance of electrode (ii) Contact resistance…

A: In welding

Q: What is a cold solder joint? Identify its causes, its appearance, and the means of correction.

Q: Explain the process of thermite welding with neat sketch. Write its applications.

Q: What is the principal benefit of a joint action with a mechanical advantage less than 1.0? What is…

A: Whenever we apply load at input end of a mechanism and get an increased load condition at the output…

Q: Dynamic forces F1 = 4000N and F2 = 6000N are applied to the welded part shown in the figure as shown…

Q: Two 3.5 mm thick metal (Um = 9.5 J/mm') sheets are being joined using resistance spot welding. To…

A: Given Data Thickness of plate = 3.5 mm Um=9.5 J/mm3 R = 140 microohms Time = 0.3 sec D = 5.5 mm t =…

Q: List the materials that can give off dangerous fumes during welding and require forced ventilation.

A: Welding fumes are very small particles of solid materials which can able to float in the air. Thes…

Q: Discuss the arc welding quality and type of defects involved? What are the inspection and testing…

A: Arc welding quality: The arc welding qualities are given as under: (1) There will be no cracks in…

Q: (Textbook: page 51, problem 12) How can machinery parts and pipeline welds be tested for flaws…

A: THESE TESTS LIKE X-RAYS AND HYDROSTATIC TESTS ARE NON DESTRUCTIVE TESTS. THE BASIC GOAL IS TO…

Q: The welding parameters to be used to butt weld a metal alloy are being evaluated. In order to set up…

A: Write the power delivered by the welding machine. P=4000 W Write the heat transfer function.…

Q: 1. Fusion welding means that the two surfaces to be joined and the filler metal are meling during…

A: in fusion welding a filler material is liquified and deposited into the gap between , which then…

Q: What are the 5 properties of metals? Why is it important to know for welding purposes?

A: 1. Hardness:- Properties of material which resist the penetration and wear by another metal or…

Q: Provide a general description of electric arc furnace used in Industrial Manufacturing of Steel

A: following is the answer to the above problem

Q: 1) The development of residual stresses in weld joint is due to? Heat treatment operations OUnevenly…

A: Residual stresses are the stresses that remains in the material even after the removal of the force…

Q: Are the Expansion joints, used to mitigate thermal stress in materials?

A: Expansion joint It is a configuration developed to join the sections together while efficiently…

Q: Define welding process.what are the limitations and drawbacks of welding in the field of Mechanical…

A: This question is based on the concept of welding

Q: What is metal inert gas welding and the effect of metal inert gas welding process parameters?…

A: what is metal inert gas welding?? answer-In this type of welding consumable type of electrode used.…

Q: Give some examples of Fastener Spacing?

A: Calculating fastener spacing; The formulas, The formulas shown here are derived directly from…

Q: why Filler metals are used in fusion welding process?

A: Filler metal Filler metal is a metal added in the making of a joint through welding, brazing, or…

Q: 6. Bolting bridges together is often preferred to welding, since bolting (think abou welds are often…

A: As per quidelines we need to solve only first three questions so please repost rest questions…

Q: Identify the conditions under which a brazed joint is likely to be “stronger” than the brazing…

A: Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: A steel cylindrical air receiver with 6.0 feet diameter and pressure load of 220 psi., design stress…

A: Answer: The bursting steam pressure of this air receiver is 1711.11 psi.

Q: Calculate the heat input during the arc welding process, if the voltage is 33 volts, current is 115…

Q: temperature

A: An I-beam made of 4140 steel is heat treated to form tempered martensite. It is then welded to a…

Q: (c) An arc welding is performed to join two metal pieces. After the welding process, the product is…

A: As given the two metals are welded using arc welding then a fatigue test is done on it. Fatigue…

Q: The current required for 5mm thick steel plates to be spot welded is 10,000amps. Then the current…

A: Calculated the current required for a 1.5mm thick aluminium plate to spot weld.

Q: An electron-beam welding operation will join two pieces of steel plate together. The plates are 2.5…

Q: 8) The correct ways to control liquation cracking tendency in fusion weld joint are I. Use of filler…

A: The way of arranging and control liquation cracking tendency in fusion is iii, iv and v

Q: Question 1.1 Identify the weld defect shown in Figure 1 below. Provide reasons for your selection.…

Q: What type(s) of bonding would be expected for each of the following materials: solid xenon, calcium…

A: Bonding of Materials: There are basically three types of material bonding. These include ionic,…

Q: why is arc shielding requried during arc welding ? how is the arc shielding accomplshed? provide the…

Q: What is the approximate value of the half value layer when Carbon-14 sample was used with an…

A: Aluminum shielding is used to provide strength and offers higher conductivity. Also, Aluminum does…

Q: (a) Describe brazing and soldering processes. (b) Two parts made of steel were joined by adhesive…

A: a) Brazing process it is process of metal-joining where two or more than two metals are joined…

Q: 3) During arc welding, the heat input per unit length reduces, with increase of (keeping other…

A: Arc Welding It is a process of joining two workpiece by heating them upto there melting point temp…

Q: (c) Two carbon steel workpieces were joined together by welding. The type of joint is butt joint.…

A: It is a production method that generally combines materials, metals, or thermoplastics to melt and…

Q: A welding operation on an aluminum alloy makes a groove weld. The cross-sectional area of the weld…

A: Given, The cross-sectional area of the weld, A=30 mm2 The welding velocity, v=4 mm/s The heat…

Question

100%

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Can a tee weld be strong if the welds on both sides do not have deep penetration? Why or why not?
What chemicals alloys are a. considered to be contaminants to the weld metal? b. used to increase tensile strength in the weld metal? c. used to increase corrosion resistance? d. used to reduce creep?
For a cross section of a typical fusion-welded joint: (a) list all types of different zones in the joint and (b) Explain the different types of grain structure that formed during welding of metal.
Provide a reasonable explanation for the following observation: a welded component made of Al 6061-T6 alloy is routinely found to deform plastically first in the region adjacent to the weld joint despite the fact that the stress is nominally the same everywhere in the component. What solution would you propose to fix this problem, assuming that the weld joint cannot be eliminated from the design?
What is metal inert gas welding and the effect of metal inert gas welding process parameters? Diagrams?
An RSW operation is used to join two pieces of sheet steel having a unit melting energy of 8369.85 J/cm3. The sheet steel has a thickness of 0.3125 cm. The weld duration will be set at 0.25 sec with a current of 11,000 amp. Based on the electrode diameter, the weld nugget will have a diameter of 0.75 cm. Experience has shown that 40% of the supplied heat melts the nugget and the rest is dissipated by the metal. If the electrical resistance between the surfaces is 130 micro-ohms, what is the thickness of the weld nugget assuming it has a uniform thickness?
why is arc shielding requried during arc welding ? how is the arc shielding accomplshed? provide the detailed explanation
It has been reported that gas–tungsten arc welds of aluminum made in the overhead position (assumed lap weld joint) tend to have a significantly higher porosity level than those made in the flat position: Explain why Sketch the general view of the overhead position Indicate where the (most probable) location of the porosity
Assume that two 1.5-mm thick steel sheets are being spot welded at a current of 4000 A and current-flow time is 0.3 s. Using electrodes 5 mm in diameter, estimate the amount of heat generated and the amount of heat required to melt the weld nugget. Use an effective resistance of 350 un. Take u= 9,7 Joule/mm Which one of the following are correct? O a. If the electrodes were 7 mm diameter, the amount of heat generated would decrease b. The amount of heat generated by the equipment is between 1600 to 1700 Joules c. The equipment has enough power to weld the steel sheets. d. The equipment does not have enough power to weld the steel sheets e. The amount of heat required is between 700 and 750 Joules
It has been reported that gas–tungsten arc welds of aluminum made in the overhead position (assumed lap weld joint) tend to have a significantly higher porosity level than those made in the flat position: a. Explain why b. Sketch the general view of the overhead position c. Indicate where the (most probable) location of the porosity
The unit melting energy for a certain sheet metal is 10J/mm^3 .The thickness of each of the two sheets to be spot-welded is = mm. To achive required strength, it is desired to form a weldnugget that is =7 mm in diameter and 3.5 mm thick. The weld duration will be set at 44 sec .If the electrical resistance between the two surfaces is 144 micro-ohms and only one half the electricity generated will be used to form the weld nugget Determine the minium current level required in this operation
What does liquid-solid phase bonding mean and in which cases is it preferred over welding? What does capillarity mean in this process?