B/ The sprue leading into the runner of a certain mold has a length is 150 mm. The cross- sectional area at base of the sprue is 400 mm². The mold cavity has a volume is 0.002 m². Determine: (a) the velocity of the molten metal flowing through the base of the sprue, (b) the volume rate of flow, and (c) the time required to fill the mold cavity.

B/ The sprue leading into the runner of a certain mold has a length is 150 mm. The cross- sectional area at base of the sprue is 400 mm². The mold cavity has a volume is 0.002 m². Determine: (a) the velocity of the molten metal flowing through the base of the sprue, (b) the volume rate of flow, and (c) the time required to fill the mold cavity.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q1. A mold sprue is 20 cm long, and the cross-sectional area at its base is 2.5 cm2 .The sprue feeds a horizontal runner leading into a mold cavity whose volume is 1560 cm3. Determine:(A) velocity of the molten metal at the base of the sprue(B) volume rate of flow(C) time to fill the mold.
Determine the time required to fill the mold cavity along with the riser as shown in the following figure.
The passageways in the parting plane through which molten metal flow is regulated are known as: 1- Gate 2- Core 3- Runner 4- Chaplet
What is the advantage in casting turbine blades that have either highly aligned grain boundaries or no grain boundaries at all?
A sprue in a sand mould has a topdiameter of 20 mm and height of 200mm. The velocity of the molten metalat the entry of the sprue is 0.5 m/s.Assume acceleration due to gravity as9.8 m/s and neglect all losses. If themould is well ventilated, the velocity(upto 3 decimal points accuracy) of themolten metal at the bottom of the sprueis ______ m/s.
A sprue in a sand mould has a topdiameter of 20 mm and height of 200mm. The velocity of the molten metalat the entry of the sprue is 0.5 m/s.Assume acceleration due to gravity as9.8 m/s2 and neglect all losses. If themould is well ventilated, the velocity(upto 3 decimal points accuracy) of themolten metal at the bottom of the sprueis ______ m/s.
a riser in the shape of a sphere is to be designed for a sand casting mold. the casting is a rectangular plate, with length 200mm, width 100mm, and thickness 18mm. if the total solidification time of the casting itself is known to be 3.5 mm, determine the diameter of the riser so that it will take 25% longer for the riser to solidify. assume a value of 2 for ‘n’ m( the exponent in chvorinov’s rule). know the volume and surface area of a sphere.
Pure aluminium is poured into a sand mold. The metal level in the pouring basin is 203.2mm above the metal level in the mold, and the runner is circular with a 7.62 mm diameter.What is the velocity and the rate of flow of the metal into the mold? Is the flow turbulent orlaminar? Note that pure aluminum has a density of 2700 kg/m3and a viscosity of 0.004Ns/m
For the casting of the part, whose perspective pictures are given below, take into account the surface of the section, the model design, if necessary, the core design, all the molding stages and finally the mold in the most suitable form for casting, and name all the mold elements by showing them on the figure (Note: The hole shown in the figure, full hole.)
Down sprue is designed to deliver the molten metal cast iron having density of 8000 kg/m3 having a mass flow rate of 10 kg/s. height of sprue is 200 mm and height of pouring basin is 60 mm a. Find out flow rate of molten metal b. Area of ingate
A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.
Determine the time required to fill the mold cavity along with the riser as shown in the following figure. A slab of 1500 mm x 750 mm x 500 mm is required to be cast using a sand casting process. It was observed previously that the total solidification time (T) for this casting = 1.6 min. Find out the cylindrical riser dimensions (diameter to height ratio = 1) for a solidification time T = 5 min.