Table B2: Stress-straindata for uniaxial compression test on SampleNormal stressUniaxial strain (%)Lateral strain (%)(MPa)0.00.00000.00005.00.0319-0.015010.00.0720-0.027515.00.1025-0.042520.00.1450-0.060025.00.1755-0.072530.00.2150-0.087535.00.2455-0.102541.00.2815-0.112546.00.3125-0.120952.00.3515-0.128558.00.4000-0.1325(f)Based on the plotted curve, calculate the average/tangent Young's modulusand Poisson's ratio for this sample, at 50 % UCS?

we have to evaluate the poisson's ratio & youngs modulus

Answered: Based on the plotted curve, calculate…

Based on the plotted curve, calculate the average/tangent Young's modulus and Poisson's ratio for this sample, at 50 % UCS?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
Draw the tensile curves of the following materials, taking into account the appropriate elongation at break, modulus of elasticity and tensile stress, on the side stress-strain graph. a)Low carbon steel (Ecelik=200Gpa),(Syield=300MPa),(Stensile=400MPa) b)High carbon steel (Esteel=200GPa),(Stensile=700MPa) c)Aluminum (Ealuminum=70GPa), (Syield=200MPa),(Stensile=300MPa) d)Cast iron (Ecast iron=120GPa),(Stensile=200MPa)
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
Civil engineers often use the straight-line equation, = b 0 + b 1x, to model the relationship between the shear strength y of masonry joints and precompression stress, x. To test this theory, a series of stress tests were performed on solid bricks arranged in triplets and joined with mortar. The precompression stress was varied for each triplet and the ultimate shear load just before failure (called the shear strength) was recorded. The stress results for n = 7 resulted in a Coefficient of Determination of 0.8436. Given that r 2= 0.8436, give a practical interpretation of r 2, the coefficient of determination for the least squares model. a. We expect to predict the shear strength of a triplet test to within about 0.8436 tons of its true value. b. About 84.36% of the total variation in the sample of y-values can be explained by (or attributed to) the linear relationship between shear strength and precompression stress. c. In repeated sampling, approximately 84.36% of…
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lb - in per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 142 kN. - Length of the specimen is 23 mm. - The yield strength is 82 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN, iv) Young's Modulus if the elongation is 1.6 mm at 15 kN and (v) Final diameter if the percentage of reduction in area is 20 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm)
Consider the tensile stress-strain diagram below. If samples 1 and 2 are identical except that they were tested at different temperatures, which sample was tested at a lower temperature? Note: This question will be marked negatively so consider your answer carefully. A. Sample 1 B. Both were tested at the same temperature/ Alby is by die dieselfde temperatuur getoets C. Sample 2
Bronze alloy, the following true stresses produce the corresponding plastic true strains, before to necking: On the basis of this information, compute the true stress necessary to produce a true strain of 0.25 and then find the engineering stress and strain at this point. True stresses (MPa) True strain 354 0121 70 018