Data taken from a tensile test is given below. The curve is linear between the origin and the first point. The gauge length is 34 mm and the cross sectional area is 12.56 mm2. Determine the modulus of elasticity. Force (N) Extension (mm) 7000 0.25 8000 0.32 8500 0.56 8500 0.7 Select one: O a. none of these options O b. 75.8 GPa O c. 109.5 GPa O d. 305 GPa O e. 201.6 MPa O f. 240 MPa O g. 86.3 GPa O h. 102 GPa

Data taken from a tensile test is given below. The curve is linear between the origin and the first point. The gauge length is 34 mm and the cross sectional area is 12.56 mm2. Determine the modulus of elasticity. Force (N) Extension (mm) 7000 0.25 8000 0.32 8500 0.56 8500 0.7 Select one: O a. none of these options O b. 75.8 GPa O c. 109.5 GPa O d. 305 GPa O e. 201.6 MPa O f. 240 MPa O g. 86.3 GPa O h. 102 GPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
I want answers to all four questions if possible. Thanks for help :) Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material.
Manufacturing engineering- A single strain gauge is mounted to measure the axial strain in a simple tensile member the recorded strain is 200 microstrain, what is the axial stress ? a) If the member is of steel? b) if the member is of aluminium ? The modulus of elasticity of steel is 200 GPa and that of aluminium is 70 GPa
The strains measured by a rosette strain gauge are
In a Torsion test done, the following data were collected: the radius of the specimen was 3mm and the gauge length 76.2mm. During the elastic zone: T1-0. 01N.m. 01-14.760, T2-17. 13N.m, and 02-36.910. The modulus of rigidity be equal to:
A tension test specimen had a gauge length of 2.5 in. After the test, the gauge length had increased to 6.5203 in. What is the uncertainty in the percentage elongation calculation of the specimen, if a caliper having an uncertainty of 0.001 in was used for measuring the length?
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
Question Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength.
A square bar subjected to a tensile load of 100KN having a gauge length of 200mm, extends to a length of 0.19mm. Given the tensile strength as 200 MPa, determine, (i) Side of the bar (express in mm) (ii) Final length (express in mm) (ii) Modulus of elasticity (express in GPa)
A square bar subjected to a tensile load of 100kN having a gauge length of 200mm extends to a length of 0.19mm . Given the tensile strength as 200 MPa , determine ( 1 ) Side of the bar ( express in mm ) Final length ( express in mm ) Modulus of elasticity ( express )
The following results were obtained in a tensile test on a mild steel specimen of original diameter 28 mm and gauge length 56 mm. Load at limit of proportionality : 96 kN Extension at 96 kN load : 0.068 mm Load at yield point : 105 kN Maximum load : 170 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 65.8 mm and the diameter at the neck was 18.8 mm. Calculate: (a). E, (b).σy, (c).σu, (d). PRIA and PE
6. State your answers to the following questions.Strain Gauge represents the deformation of a material through a change in resistance. If so, explain how temperature will affect the strain gauge in the experimental environment.①:In this experiment, the Strain Gauge measures the strain in micro units. Explain one possible error factor when applying a load by hanging a weight on the material with the strain gauge attached. (Hint: It is easy to shake by hanging the weight using a thread)①: