During freezing of a Cu-Zn alloy, we find that the composition is non-uniform. By heating thealloy to 600°C for 3 hours, diffusion of zinc helps to make the composition more uniform. Whattemperature would be required if we wished to perform this homogenization treatment in 30minutes?

Answered: During freezing of a Cu-Zn alloy, we…

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

To increase the hardness of a steel gear, it was carburized at 850oC by introducing 1.3%C at its steel surface. What will be the final carbon content 1.4 mm beneath the surface if this treatment was lasted for 26 hours. The initial carbon content of steel is 0.1%C. (gas constant is 8.31 j/mol.K)
For a steel alloy it has been determined that a carburizing heat treatment of 11.3 h duration will raise the carbon concentration to 0.34 wt% at a point 1.0 mm from the surface. Estimate the time necessary to achieve the same concentration at a 5.0 mm position for an identical steel and at the same carburizing temperature. t = ______ h
If the initial composition of the carbon steel is c0=0.3 wt%, calculate the carbon concentration (in wt%) at a distance 0.2mm from the surface of the component after 1 hour of decarburization.
1. You have ice at 263 K (-10.0 °C) and 1.0 atm. Whatvcould you do to make the ice sublime? 2. A sample of dry ice (solid CO2) is cooled to 173 K (-100.0 °C), and is set on a table at room temperature (298 K; 25 °C). At what temperature is the rate of sublimation and deposition the same (assume that pressure is held constant at 1 atm)?
Silicon having a melting point of 1412ºC forms an alloy with aluminum having a melting point of 660°C. The solidification temperature of the alloy is observed to be at 580°C at which the mass fraction of silicon is 0.125. Represent the liquid-solid diagram from the given data. Determine the phases present in the following conditions:
1. An FCC iron-carbon alloy initially containing 0.20 wt% C is carburized at an elevated temperature and in an atmosphere that gives a surface carbon concentration constant at 1.0 wt%. If after 49.5 h, the concentration of carbon is 0.35 wt% at a position 4.0 mm below the surface, determine the temperature at which the treatment was carried out. 2. Consider a metal single-crystal oriented such that the normal to the slip plane and the slip direction are at angles of 60° and 35°, respectively, with the tensile axis. If the critical resolved shear stress is 20.7 MPa, will an applied stress of 45 MPa cause the single crystal to yield? If not, what stress will be necessary?
Iron (Fe) undergoes an allotropic transformation at 912°C: upon heating from a BCC (α phase) to an FCC (γ phase). Accompanying this transformation is a change in the atomic radius of Fe—from RBCC = 0.12584 nm to RFCC = 0.12894 nm—and, in addition, a change in density (and volume). Compute the percentage volume change associated with this reaction. Indicate a decreasing volume by a negative number.
Given that a component is made of 0.1 wt.%C steel is carburized by introducing 1.0 wt.% carbon at its surface at 980ºC. Calculate the carbon content at 0.5 mm below the surface of this component after 1 hour.Do= 0.2 cm^2/s and Qd=40,000 cal/mol.
why diffusion coefficients of carbon in BCC and FCC in iron at temperature 912 c are difference? explain ?
For a Fe-2.5 %C alloy , what is the temperature at which the first liquid forms on heating and also give the composition of the liquid at that temperature
Calculate the diffusion coefficient for the interdiffusion of Zinc into Copper at 500 °C .
Calculate the concentration of monovacancies in gold at 1,000 K, knowingthat Hf = 1.4 × 10−19 J. If the gold is suddenly quenched to ambienttemperature, what will be the excess vacancy concentration?

SEE MORE QUESTIONS

Recommended textbooks for you

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Control Systems Engineering

Mechanical Engineering

ISBN:

9781118170519

Author:

Norman S. Nise

Publisher:

WILEY

Mechanics of Materials (MindTap Course List)

Mechanical Engineering

ISBN:

9781337093347

Author:

Barry J. Goodno, James M. Gere

Publisher:

Cengage Learning

Engineering Mechanics: Statics

Mechanical Engineering

ISBN:

9781118807330

Author:

James L. Meriam, L. G. Kraige, J. N. Bolton

Publisher:

WILEY

SEE MORE TEXTBOOKS

During freezing of a Cu-Zn alloy, we find that the composition is non-uniform. By heating the alloy to 600°C for 3 hours, diffusion of zinc helps to make the composition more uniform. What temperature would be required if we wished to perform this homogenization treatment in 30 minutes?