Using the Tabulation of Diffusion Data, answer the following:(a) Calculate the diffusion coefficient for Cu in Al at 520'C.7.18e-14m2/s (Use scientific notation.)(b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for12hat 520 C?i 2.52

Answered: Image /qna-images/answer/826fadbd-7338-451c-b65e-e1c4d1eddda7.jpg

Using the Tabulation of Diffusion Data, answer the following: (a) Calculate the diffusion coefficient for Cu in Al at 520'C. 7.18e-14 m/s (Use scientific notation.) (b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for 12hat 520'C? i 2.52 hi

Using the Tabulation of Diffusion Data, answer the following: (a) Calculate the diffusion coefficient for Cu in Al at 520'C. 7.18e-14 m/s (Use scientific notation.) (b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for 12hat 520'C? i 2.52 hi

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Calculate the value of the diffusion coefficient D (in m2/s) at 750°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 × 10-5 m2/s and 177 kJ/mol, respectively.
The diffusion coefficients for metal A in metal B are given at two temperatures: T (K) D (m2/s) 1283 6.55 × 10–17 1543 6.43 × 10–16 Dtermine the activation energy (Qd), the value of Do and the magnitude of D at 1463 K?
A plate of iron is exposed to a carburizing atmosphere on one side and a decarburizing atmosphere on the other side. If a condition of steady state is achieved, calculate the diffusion flux of carbon through the plate if the concentrations of carbon at positions of 5 and 10 mm beneath the carburizing surface are 1.2 and 0.6 kg/m3, respectively. Assume a diffusion coefficient of 2.4 x 10-12 m2/s at this temperature.
The diffusion coefficients for iron in nickel are given at two temperatures: T(K) D(m2/s) 1273 9.4 x 10-16 1473 2.4 x 10-14 (a) Determine the values of D0 and the activation energy Qd. (b) What is the magnitude of D at 1100ºC (1373 K)?
Diffusion of carbon into the surface of BCC steel at 600oC for 10 hours results in a carbon concentration of 0.2wt% at a depth of 1.5 mm below the surface. At what depth will the same concentration be obtained if the diffusion time is increased to 20 hours, leaving the temperature at 600o
Diffusion of carbon into BCC iron for 12 hours at a temperature of 500 °C results in a carbon concentration of 0.2 wt% at a depth 2 mm from the surface. How long would it take to get a concentration of 0.2 wt% at a depth 3 mm from the surface at 500 °C?
Rank the magnitudes of the diffusion coefficients from greatest to least for the following systems: N in Fe at 700°C Cr in Fe at 700°C N in Fe at 900°C Cr in Fe at 900°C Now justify this ranking. (Note: Both Fe and Cr have the BCC crystal structure, and the atomic radii for Fe, Cr, and N are 0.124, 0.125, and 0.065 nm, respectively. You may also want to refer to Section 5.4.)
A sample containing 1.0 mole of oxygen gas initially at 45 degrees Celsius is heated to 110 degrees Celsius under isobaric conditions. Assuming that the accurate Cp value for oxygen gas can be obtained from the relationship given below, what would be the sample's new change in enthalpy (in KiloJoules)? Write the answer in THREE SIGNIFICANT FIGURES
Please kindly help. I will give a like. Thank you! a. Describe the S-curve model of diffusion on how does ‘rate of adoption’ change over time? At which-point is the rate of diffusion the fastest? b. S-curve model of diffusion: (true/false) and reasoning - k = 0, the rate of diffusion is instantaneous? - fixed k ≥ 0, the carrying capacity is determined only by the ratio of a and b? - fixed k ≥ 0, the rate of diffusion is determined only by the ratio of a and b? c. The diffusion of hybrid corn in the 1940s, who or which region seems to have adopted the hybrids more quickly and why?
An FCC iron-carbon alloy initially containing 0.20 wt% C is carburized at an elevated temperature and in an atmosphere that gives a surface carbon concentration constant at 1.0 wt%. If after 49.5 h, the concentration of carbon is 0.35 wt% at a position 4.0 mm below the surface, determine the temperature at which the treatment was carried out.
A mechanism for hardening steel is called carburization. To achieve this process, the piece of steel is exposed to an atmosphere rich in hydrocarbon such as methane (CH4). Consider a steel with a carbide concentration of 0.25wt%, which must be treated at 950˚C. If the carbon concentration at the surface is suddenly increased to 1.20wt%, how long does it take for a penetration of 0.5mm from the surface to reach a concentration of 0.80wt%? . The diffusion coefficient for carbon in iron at this temperature is 1.6 x 10-11 m2s-1. Assume that the piece of steel is semi-finite. Use the table below.
The running engine of an automobile produces carbon monoxide (CO), a toxic gas, at the rate of about 188 g CO per hour. A car is left idling in a poorly ventilated garage that is 6.0 m long,4.0 m wide, and 2.2 m high at 20°C. (a) Calculate the rate of CO production in mol/min. (b)How long would it take to build up a lethal concentration of CO of 1000 ppmv (parts per millionby volume)? Round off to 4 sig. figures for all calculations made prior to final answer and the final answer should be in 3 sig. figures